Nano-silver composite collagen surgical dressing and preparation method thereof

A technology of nano-silver and composite glue, which is applied in medical science, bandages, etc., can solve the problems of pure collagen sponge with poor mechanical properties and water resistance, and lack of antibacterial properties, and achieve broad-spectrum antibacterial properties, simple operation, The effect of high mechanical properties

Inactive Publication Date: 2017-07-25
SICHUAN UNIV
View PDF9 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, collagen does not have antibacterial ability, and some toxic and harmful microorganisms tend to grow crazily in the collagen matrix; in addition, the mechanical properties and water resistance of pure collagen sponge are poor, and its use alone cannot meet the requirements of market applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] After blending the dialdehyde xanthan gum solution with a mass concentration of 1% and the silver nitrate solution with a mass concentration of 2%, it was stirred at room temperature in the dark for 20 minutes, then the mixed solution was boiled, condensed and refluxed for 30 minutes, and after cooling to room temperature, the It was dialyzed for 5 days, then centrifuged at a speed of 6000r / min for 10min, and the supernatant was taken to obtain a nano-silver solution; the collagen was dissolved in deionized water to obtain a collagen solution with a mass concentration of 0.4%, and then injected into the mold. A collagen sponge with a thickness of 4 nm was prepared by freeze-drying, then soaked in the above-prepared nano-silver solution for 30 minutes, and freeze-dried to obtain a nano-silver composite collagen medical dressing.

Embodiment 2

[0019] Blend the dialdehyde carboxymethyl cellulose and dialdehyde inulin solution with a mass concentration of 5% and the silver nitrate solution with a mass concentration of 5%, and then stir at room temperature in the dark for 30 minutes, then boil the mixed solution, condense and reflux for 40 minutes After being cooled to room temperature, it was dialyzed for 5 days, then centrifuged at a speed of 7000r / min for 10min, and the supernatant was taken to obtain a nano-silver solution; the collagen was dissolved in deionized water to obtain a collagen solution with a mass concentration of 0.7%. Then pour it into a mold, prepare a collagen sponge with a thickness of 5 nm by freeze-drying, then soak it in the nano-silver solution prepared above for 25 minutes, and obtain a nano-silver composite collagen medical dressing after freeze-drying.

Embodiment 3

[0021] Blend the dialdehyde starch solution with a mass concentration of 0.5% and the silver nitrate solution with a mass concentration of 7%, and stir at room temperature in the dark for 30 minutes, then boil the mixed solution, condense and reflux for 20 minutes, and dialyze it after cooling to room temperature After 5 days, centrifuge at a speed of 5000r / min for 15min, take the supernatant to obtain the nano-silver solution; dissolve the collagen in deionized water to obtain a collagen solution with a mass concentration of 0.5%, then pour it into the mold, and freeze A collagen sponge with a thickness of 3 nm was prepared by drying, then soaked in the above-prepared nano-silver solution for 28 minutes, and freeze-dried to obtain a nano-silver composite collagen medical dressing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to nano-silver composite collagen surgical dressing and a preparation method of the nano-silver composite collagen surgical dressing. The preparation method comprises the following steps: uniformly mixing a dialdehyde polysaccharide solution and silver nitrate solution, completely boiling the mixed solution, carrying out reflux condensation, after the mixed solution is cooled to the room temperature, carrying out dialysis and centrifugalizing, taking the supernate, thus obtaining nano-silver solution, soaking collagen sponge in the nano-silver solution, and carrying out freeze drying, thus obtaining the nano-silver composite collagen surgical dressing. The stable nano-silver solution with narrow particle size distribution range is prepared by adopting a pollution-free reduction method, in addition, dialdehyde polysaccharide in the solution can have Schiff base chemical crosslinking reaction with collagen, and thus the physical properties of the collagen sponge are enhanced. The prepared nano-silver composite collagen surgical dressing has the advantages of broad-spectrum antibacterial activity, rapid bleeding-stopping property, high mechanical property, good moisture retention and biocompatibility, and has the potential market application prospect in the field of treating burns and scalds.

Description

technical field [0001] The invention relates to the technical field of biomedical materials, in particular to a composite collagen medical dressing which has the characteristics of broad-spectrum bacteriostasis, rapid hemostasis, good moisture retention and biocompatibility and can promote the rapid healing of burns and scald wounds and its preparation method. Background technique [0002] Burns and scalds are common in everyday life. Burn and scald wounds are easily infected by pathogenic microorganisms. Therefore, chemical drugs such as antibiotics, disinfectants, and bactericides are widely used clinically to kill microorganisms and promote rapid wound healing. The extensive use of its chemical drugs will cause the resistance of microorganisms, such as the resistance of Escherichia coli to kanamycin and streptomycin, and the resistance of Salmonella typhi to chloramphenicol. Global microbial disasters caused by microbial resistance frequently occur, so research and deve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L26/00
CPCA61L26/0066A61L26/0085A61L26/0095A61L2300/104A61L2300/404C08L89/00
Inventor 李德富葛黎明穆畅道史鲁浙杨森
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More