Method of manufacturing artificial fish reef with residence frame to be disassembled

A technology for artificial fish reefs and residences, which is applied in the fields of application, fish farming, and climate change adaptation. It can solve the problems of environmental pollution, short lifespan, and lack of utilization, and achieves easy adhesion to marine plants, which is conducive to concealment and density. , ideal effect of waterproof performance

Active Publication Date: 2017-09-05
NINGBO INST OF TECH ZHEJIANG UNIV ZHEJIANG
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But above-mentioned artificial fish reefs of these prior art all have certain deficiency more or less: the shortcoming of such as common reinforced concrete: steel bar is easy to corrode, causes concrete to crack, collapses at last, therefore, general common reinforced concrete fish reef only has two The lifespan is about ten years, and the lifespan is short; in addition, the old tire reefs have certain pollution to the water body, while the steel reefs affect the seabed environment
[0004] At present, with the continuous development of the real estate industry, a large number of residential buildings are dismantled and turned into construction waste, which will lead to the generation of a large amount of construction waste, causing environmental pollution and not being effectively utilized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of manufacturing artificial fish reef with residence frame to be disassembled

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Reinforced concrete cutting: After processing the residential frame to be dismantled with tools such as jacks, pneumatic hammers, and hydraulic hammers, use a steel bar cutter to cut off the steel bars, and use water to cool them to obtain a residential frame structure;

[0023] (2) Cutting treatment: use silicone emulsion as the waterproof coating on the end face of reinforced concrete for surface coating, the coating penetrates into the concrete surface 2-3mm to form a waterproof layer, thereby preventing seawater from entering; then use cured fluorocarbon resin The paint is applied with a top coat and dried;

[0024] (3) Reinforced concrete surface treatment: Spray mortar on the surface of the concrete to make the surface uneven; mix the components including water into a wet material in advance according to the proportion, and send the dehumidified material to the The spray gun, and the compressed air input near the muzzle sprays the wet material, forming an unev...

Embodiment 2

[0034] The raw materials of the mortar include: 20 parts of cement, 50 parts of slag, 12 parts of steel slag, 8 parts of alkali slag, 12 parts of propylene milk, 1 part of manganese-containing waste slag, 25 parts of machine-made sand or concrete waste slag, polycarboxylic acid air-entrained reducing 0.01 part of water agent, appropriate amount of water. Others are with embodiment 1.

Embodiment 3

[0036] The raw materials of the mortar include: 12 parts of cement, 25 parts of slag, 10 parts of steel slag, 6 parts of alkali slag, 10 parts of propylene milk, 1 part of manganese-containing waste slag, 16 parts of machine-made sand or concrete waste slag, polycarboxylic acid air-entrained reducing 0.008 part of water agent, appropriate amount of water. Others are with embodiment 1.

[0037] The technical indicators of the sprayed mortar of the present invention: the compressive strength is greater than 23MPa, and the bonding tensile strength is greater than 1.5MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method of manufacturing an artificial fish reef with a residence frame to be disassembled. The method includes the preparing steps of cutting reinforced concrete of the residence frame to be disassembled, processing notches and processing the surface of the reinforced concrete. In the notch processing step, organosilicon emulsion is used as a waterproof coating for the fracture face of the reinforced concrete, surface coating is conducted, the coating permeates into the surface layer of the concrete by 2-3 mm to form a waterproof layer, and consequently sea water is prevented from entering; cured type fluorocarbon resin paint is used for forming a finishing coating, and then the finishing coating is dried. The method has the advantages of being low in manufacturing cost, capable of effectively using the residence frame to be disassembled and reducing environment pollution, low in heavy metal content and beneficial for fish shoal elusion or survival and achieving resource recycling.

Description

technical field [0001] The invention relates to the technical field of artificial fish reefs, in particular to a method for making artificial fish reefs by using a residential frame to be demolished. Background technique [0002] Artificial reefs refer to artificial facilities that are composed of one or more natural or artificial objects and are purposefully placed in the sea to improve the ecological environment, increase fishery resources, and promote social and economic development. The artificial reef construction project is one of the marine fishery ecological projects emerging in the 20th century, and is an important part of the marine ranching system engineering. The construction of artificial reefs is beneficial to the improvement of marine land, the construction of marine ranch, the adjustment of marine industry structure, the promotion and optimization of marine industry, the development of marine tourism and related industries, the restoration and improvement of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A01K61/77
CPCA01K61/77Y02A40/81
Inventor 陈伟王忠瑾沈建生耿健
Owner NINGBO INST OF TECH ZHEJIANG UNIV ZHEJIANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com