Anion functional glaze material for ceramic tile and method for preparing anion functional glaze material

A negative ion and functional technology, which is applied in the field of negative ion functional tile glaze and its preparation, can solve the problems of excessive toxic and harmful substances, unhealthy radioactivity, and low negative ion release, so as to improve sleep, improve human immunity, and have a variety of varieties Effect

Inactive Publication Date: 2017-09-05
高慧芹
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Or the release of negative ions is low, which basically has no effect, or the radioactivity exceeds the standard, which is not suitable for health; or the decay is too fast; or the toxic and harmful substances such as heavy metals exceed the standard, which cannot meet the market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Negative ion functional tile glaze of the present invention is made up of base material A component and function B component, wherein

[0023] Base A component formula:

[0024] Potassium feldspar 50%, kaolin 8%, calcite 12%, zircon 23%, zinc oxide 1.6%, talc 5.4%.

[0025] Functional Component B Formula:

[0026] Hexacyclic powder 35%, germanite 30%, titanium dioxide 25%, praseodymium dioxide 7%, diindium oxide 2.5%, emulsified silicone oil 0.5%.

[0027] Take base material A component 98%, function B component 2%.

[0028] Add appropriate amount of water according to the above formula, mix on the disperser, grind on the grinder, and then enter the production line, the coating amount is 90g / piece (600*600), 160g / piece (800*800), the variety that can be produced is antique Brick, imitation wood strip brick.

[0029] Product performance indicators are as follows:

[0030] 1. Negative ion release ≥ 3000 / cm 3 *s

[0031] 2. Radiation value: internal illumination ind...

Embodiment 2

[0035] Negative ion functional tile glaze of the present invention is made up of base material A component and function B component, wherein

[0036] Base A component formula:

[0037] Potassium feldspar 50%, kaolin 8%, calcite 12%, zircon 23%, zinc oxide 1.6%, talc 5.4%.

[0038] Functional Component B Formula:

[0039] Hexacyclic powder 35%, germanite 30%, titanium dioxide 25%, praseodymium dioxide 7%, diindium oxide 2.5%, emulsified silicone oil 0.5%.

[0040] Take base material A component 95%, function B component 5%.

[0041] Add appropriate amount of water according to the above formula, mix on the disperser, grind on the grinder, and then enter the production line, the coating amount is 90g / piece (600*600), 160g / piece (800*800), the variety that can be produced is antique Brick, imitation wood strip brick.

[0042] The performance indicators of the products are as follows:

[0043] 1. Negative ion release ≥ 8000 / cm 3 *s

[0044] 2. Radiation value: internal illu...

Embodiment 3

[0048] Negative ion functional tile glaze of the present invention is made up of base material A component and function B component, wherein

[0049] Base A component formula:

[0050] Potassium feldspar 50%, kaolin 8%, calcite 12%, zircon 23%, zinc oxide 1.6%, talc 5.4%.

[0051] Functional Component B Formula:

[0052] Hexacyclic powder 35%, germanite 30%, titanium dioxide 25%, praseodymium dioxide 7%, diindium oxide 2.5%, emulsified silicone oil 0.5%.

[0053] Take base material A component 93%, function B component 7%.

[0054] Add appropriate amount of water according to the above formula, mix on the disperser, grind on the grinder, and then enter the production line, the coating amount is 90g / piece (600*600), 160g / piece (800*800), the variety that can be produced is antique Brick, imitation wood strip brick.

[0055] The performance indicators of the products are as follows:

[0056] 1. Negative ion release ≥ 1200 / cm 3 *s

[0057] 2. Radiation value: internal illu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an anion functional glaze material for ceramic tiles and a method for preparing the anion functional glaze material. The anion functional glaze material comprises 93-99% of basic material components A and 7-1% of functional components B. The basic material components A comprise feldspar, kaolin, zinc oxide, barium carbonate, corundum powder and quartz or comprise feldspar, kaolin, zinc oxide, calcite, zircon and talc powder, and the functional components B comprise hexacyclic stone powder, germanite powder, titanium dioxide, rare earth components and emulsified silicone oil. The anion functional glaze material for the ceramic tiles and the method have the advantages that anions can be released by the anion functional glaze material in a long-acting manner, accordingly, air can be purified, harmful gas can be removed, and the immunity of human bodies can be enhanced; diversified varieties can be produced by the aid of the method and are low in manufacturing cost, the method is simple, convenient and feasible, the anion functional glaze material produced by the aid of the method is stable in production quality, the release amounts of the anions can be controlled according to requirements, good indoor purification effects can be realized, and the anion functional glaze material and the method are safe and environmentally friendly.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a negative ion functional tile glaze and a preparation method thereof. Background technique [0002] With the improvement of living standards, people's requirements for decorative materials are also developing from a single decorative function to a multi-functional direction, such as air purification function, anti-smog, formaldehyde removal, ammonia benzene, TVOC, elimination of electromagnetic radiation and release of harmful substances that are beneficial to human health Negative air ions, far infrared rays, etc. Although there are many decorative materials that can satisfy the above functions, such as diatom mud, activated carbon, photocatalyst, etc., there are serious limitations. Although diatom mud and activated carbon adsorption materials have a certain degree of adsorption to harmful substances, but the application time is short, their functions will be l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00
CPCC03C8/00
Inventor 高慧芹
Owner 高慧芹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com