Environment-friendly material waterproof fire-retardant panel and preparation method thereof

An environmentally friendly material and board technology, applied in flat products, other household appliances, applications, etc., can solve the problems of stimulating human skin, polluting the air environment, affecting construction quality, etc., and achieves simple preparation process, good moisture resistance, and high practical value Effect

Inactive Publication Date: 2017-09-22
HEFEI DAHU ELECTRIC WIRE & CABLE TECH CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyurethane foam, polystyrene foam and their composite boards, which were widely used in the past, are not only flammable but also emit a lot of smoke (containing toxic carcinogens such as hydrogen cyanide and dioxin) if exposed to high temperature or open flames. In recent years, rapid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of environmental protection material waterproof flame-retardant sheet material of this embodiment, comprises the raw material of following parts by weight:

[0034] 10 parts of white latex, 5 parts of silica sol, 4 parts of waterproofing agent, 10 parts of flame retardant, 8 parts of reinforcing modifier, 70 parts of straw, 10 parts of binder, 3 parts of tripolyphosphoric acid, 7 parts of kaolin, 6 parts of gypsum 5 parts of activated carbon, 6 parts of shell powder, 2 parts of nano-zinc oxide, 1 part of nano-titanium dioxide, 8 parts of bentonite, and 25 parts of water.

[0035] The waterproofing agent in this embodiment is a mixture of paraffin wax and rosin in a weight ratio of 2:3.

[0036] The flame retardant in this embodiment is a mixture of aluminum hydroxide, zinc phosphate and magnesium hydroxide in a weight ratio of 2:3:1.

[0037] The strengthening modifier in this embodiment is a mixture of boric acid aqueous solution, salicylic acid aqueous solutio...

Embodiment 2

[0046] A kind of environmental protection material waterproof flame-retardant sheet material of this embodiment, comprises the raw material of following parts by weight:

[0047] 20 parts of white latex, 7 parts of silica sol, 6 parts of waterproofing agent, 12 parts of flame retardant, 12 parts of reinforcing modifier, 90 parts of straw, 15 parts of binder, 5 parts of tripolyphosphoric acid, 9 parts of kaolin, 8 parts of gypsum 7 parts of activated carbon, 12 parts of shell powder, 4 parts of nano-zinc oxide, 3 parts of nano-titanium dioxide, 14 parts of bentonite, and 35 parts of water.

[0048] The waterproofing agent in this embodiment is a mixture of paraffin wax and rosin in a weight ratio of 2:3.

[0049] The flame retardant in this embodiment is a mixture of aluminum hydroxide, zinc phosphate and magnesium hydroxide in a weight ratio of 2:3:1.

[0050] The strengthening modifier in this embodiment is a mixture of boric acid aqueous solution, salicylic acid aqueous sol...

Embodiment 3

[0059] A kind of environmental protection material waterproof flame-retardant sheet material of this embodiment, comprises the raw material of following parts by weight:

[0060] 15 parts of white latex, 6 parts of silica sol, 5 parts of waterproofing agent, 11 parts of flame retardant, 10 parts of reinforcing modifier, 80 parts of straw, 13 parts of binder, 4 parts of tripolyphosphoric acid, 8 parts of kaolin, 7 parts of gypsum 6 parts of activated carbon, 9 parts of shell powder, 3 parts of nano-zinc oxide, 2 parts of nano-titanium dioxide, 11 parts of bentonite, and 30 parts of water.

[0061] The waterproofing agent in this embodiment is a mixture of paraffin wax and rosin in a weight ratio of 2:3.

[0062] The flame retardant in this embodiment is a mixture of aluminum hydroxide, zinc phosphate and magnesium hydroxide in a weight ratio of 2:3:1.

[0063] The strengthening modifier in this embodiment is a mixture of boric acid aqueous solution, salicylic acid aqueous solu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly material waterproof fire-retardant panel. The environment-friendly material waterproof fire-retardant panel is prepared from the following raw materials in parts by weight: 10 to 20 parts of white latex, 5 to 7 parts of silica sol, 4 to 6 parts of waterproof agent, 10 to 12 parts of fire retardant, 8 to 12 parts of reinforced modifier, 70 to 90 parts of straw, 10 to 15 parts of adhesion agent, 3 to 5 parts of tripolyphosphate, 7 to 9 parts of kaoline, 6 to 8 parts of gypsum, 5 to 7 parts of activated carbon, 6 to 12 parts of shell powder, 2 to 4 parts of nano-zinc oxide, 1 to 3 parts of nano-titanium dioxide, 8 to 14 parts of bentonite and 25 to 35 parts of water. As a large number of agricultural wastes are adopted in the environment-friendly material waterproof fire-retardant panel disclosed by the invention, resources are saved, cost is reduced, materials are poisonless and harmless, environment-friendly and healthy, furthermore, the panel is good in flame retardant property, high in strength, good in moisture resistance, good in size stability and corrosion-resistant, a preparation process is simple, and the environment-friendly material waterproof fire-retardant panel has a relatively high practical value and a good application prospect.

Description

technical field [0001] The invention relates to the technical field of environmental protection materials, in particular to an environmental protection material waterproof and flame-retardant plate and a preparation method thereof. Background technique [0002] The development trend of wood-based panels is rapidly changing from wood to various wood substitutes as raw materials. Using crop straw as the main raw material to produce composite wheat straw panels has various excellent physical and mechanical properties, surface decoration properties and secondary processing properties, and has become a high-strength environmental protection panel. This type of board is a load-bearing structural material that is completely different from traditional boards. It can be used in construction engineering, packaging and furniture decoration, and has become a revolutionary board that replaces traditional boards. This kind of board has good heat insulation, sound absorption and noise pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L97/02C08L91/06C08L31/04C08L93/04C08L29/04C08L63/00C08K13/02C08K3/22C08K3/26C08K3/34C08K3/32B29C43/58B29B7/00B29L7/00
CPCC08L97/02B29B7/002B29C43/58B29C2043/5808B29L2007/002C08K2003/2224C08K2003/2227C08K2003/2241C08K2003/2296C08K2003/265C08K2003/321C08K2201/011C08K2201/014C08L2201/02C08L2205/035C08L2205/16C08L91/06C08L93/04C08L31/04C08L29/04C08L63/00C08K13/02C08K3/22C08K3/26C08K3/346C08K3/34C08K3/32
Inventor 王月斌
Owner HEFEI DAHU ELECTRIC WIRE & CABLE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap