A preparing process of an antifouling soft-light marble tile

A preparation process, marble technology, applied in clay products, applications, household appliances, etc., can solve the problem of large differences in visual and tactile effects, and achieve the effect of reducing product reflectivity, solving light pollution problems, and wear-resistant scratches

Inactive Publication Date: 2017-09-26
淄博新博陶瓷有限公司 +1
View PDF11 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The pattern on the surface of the tile can be applied by inkjet grid printing technology to form a pattern whose pattern can achieve a highly simulated effect with marble, but the surface roughness and reflective effect of this kind of tile are quite different from polished marble, resulting in The actual visual and tactile effects are still quite different from polished marble

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The composition of crystal color frit used in the present embodiment is silicon oxide 51%, aluminum oxide 20%, potassium oxide 2%, sodium oxide 1%, calcium oxide 13%, magnesium oxide 4%, fluorine oxide 3%, phosphorus oxide 1%, boron oxide 5%;

[0025] 32 parts by weight of feldspar, 4 parts of crystal color frit, 12.5 parts of pyrophyllite, 30 parts of white clay, and 18 parts of high alumina. , the fineness reaches 250 mesh; then the powder is formed through the spray milling process, and then pressed and formed by a press with a pressure of 300bar;

[0026] Put it on the large-scale production conveying line after forming, and pour the bottom glaze first; the surface glaze is inkjet printed into a marble pattern, and the weight of the glaze is as follows: 27 parts of feldspar, 17 parts of crystal color frit, 4 parts of corundum, and 8 parts of kaolin 9 parts of zinc oxide, 10 parts of wollastonite, 2 parts of barium oxide, 13 parts of quartz;

[0027] After that, fi...

Embodiment 2

[0031] The composition of crystal color frit used in the present embodiment is silicon oxide 51%, aluminum oxide 20%, potassium oxide 2%, sodium oxide 1%, calcium oxide 13%, magnesium oxide 3.5%, fluorine oxide 3.3%, phosphorus oxide 1.2%, boron oxide 5%;

[0032] 32 parts by weight of feldspar, 4 parts of crystal color frit, 13 parts of pyrophyllite, 28 parts of white clay, and 19 parts of high alumina stone. , the fineness reaches 250 mesh; then the powder is formed through the spray milling process, and then pressed and formed by a press with a pressure of 300bar;

[0033] Put it on the large-scale production conveying line after forming, and pour the bottom glaze first; the surface glaze is inkjet printed into a marble pattern, and the weight of the glaze is composed of 27 parts of feldspar, 18 parts of crystal color frit, 4 parts of corundum, and 8 parts of kaolin 9 parts of zinc oxide, 10 parts of wollastonite, 2 parts of barium oxide, 12 parts of quartz;

[0034] Afte...

Embodiment 3

[0038] The composition of crystal color frit used in this embodiment is silicon oxide 51%, aluminum oxide 20%, potassium oxide 2%, sodium oxide 1%, calcium oxide 13%, magnesium oxide 4.5%, fluorine oxide 2.7%, phosphorus oxide 0.8, boron oxide 5%;

[0039] 33 parts by weight of feldspar, 4 parts of crystal frit, 12 parts of pyrophyllite, 32 parts of white clay, and 17 parts of high alumina stone. , the fineness reaches 250 mesh; then the powder is formed through the spray milling process, and then pressed and formed by a press with a pressure of 300bar;

[0040] Put it on the large-scale production conveying line after forming, and pour the bottom glaze first; the surface glaze is inkjet printed into a marble pattern, and the weight of the glaze is as follows: 28 parts of feldspar, 17 parts of crystal color frit, 4 parts of corundum, and 8 parts of kaolin 9 parts of zinc oxide, 9 parts of wollastonite, 2 parts of barium oxide, 14 parts of quartz;

[0041] After that, firing is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to view more

Abstract

A preparing process of an antifouling soft-light marble tile is disclosed and belongs to the technical field of tile preparation. The process is characterized in that the process includes steps of 1) preparing a green body, 2) applying ground coat, 3) performing ink-jet printing of marble pattern overglaze, 4) firing and 5) soft polishing; a green body material used in the green body preparing step includes, by weight, 30-35 parts of feldspar, 3-5 parts of crystal frit, 10-15 parts of pyrophyllite, 25-35 parts of white clay and 15-20 parts of high-aluminum rock; and a glaze material used in the overglaze includes, by weight, 25-30 parts of feldspar, 15-20 parts of crystal frit, 3-5 parts of corundum, 7-10 parts of kaolin, 8-10 parts of zinc oxide, 8-11 parts of wollastonite, 1-3 parts of barium oxide and 10-15 parts of quartz. The simulation degree between the tile and natural marble in the aspects of visual inspection and touch senses is high. The fouling resistance, wear resistance, coloring effects, crack resistance, and the like of the tile are superior to those of the natural marble.

Description

technical field [0001] The invention discloses a preparation process of antifouling soft marble tiles, which belongs to the technical field of tile preparation. Background technique [0002] Soft light tiles, also known as soft light elegant surface tiles, the existing manufacturing processes mainly include the following: one is to evenly spread transparent crystal particles on the surface of ceramic tiles in a wet way through a glaze spray cabinet or a glaze throwing cabinet, and the other The advantage is that it has good combination with the green body, and the disadvantage is that the dry particles have poor fluidity, easy to block the spray gun holes, poor production control, poor flatness, and low hardness; the second is to wet the transparent crystal particles through the glaze cabinet. Evenly spread on the surface of ceramic tiles, the advantage is that the fired tiles have better flatness, but the disadvantage is that the hardness is low, the dry particles have poor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/04C03C8/00C04B33/34
CPCC03C8/00C04B33/04C04B33/13C04B33/34C04B2235/3217C04B2235/3427C04B2235/3463
Inventor 王铎
Owner 淄博新博陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap