Flame retardant antifogging wet tissue and processing method thereof

A flame-retardant and anti-fog technology, which is applied in the direction of flame-retardant fiber, anti-coloring pollution/anti-fouling fiber, biochemical fiber treatment, etc., can solve the problems of inability to achieve flame-retardant effect, and achieve improved flame-retardant performance, Maintain long-term release effect

Inactive Publication Date: 2017-11-03
东莞市荣腾纳米科技有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a flame-retardant anti-fog wet wipe and its processing method, which solves the problem that the existing wet wipes generally only have one of the functions of antibacterial, deodorant, environmental protection, radiation protection, and releasing infrared rays and negative ions. Or many kinds, but it can't achieve the flame retardant effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A flame-retardant anti-fog wet wipe, comprising 1 part of non-woven fabric and 3 parts of flame-retardant self-cleaning anti-fog liquid by weight, and the flame-retardant self-cleaning anti-fog liquid comprises 21.89g of organic silicon by weight Resin emulsion (mass concentration 40%), 2.02g of nano-magnesia powder, 1.10g of nano-antimony oxychloride, 0.03g of nano-Ag powder, 0.29g of nonylphenol polyoxyethylene ether, 9.10g of ethylene glycol alcohol, 7.82g of glycerin, 0.06g of polyoxypropylene polyoxyethylene glyceryl ether, 0.04g of polydimethylsiloxane, 0.74g of sodium citrate, 1.77g of jasmine fragrance microcapsule emulsion (solid Content 30%) and 8.68g of deionized water.

[0030] The preparation method is:

[0031] Weigh 2.02g nano-magnesia powder, 1.10g nano-antimony oxychloride, 0.03g nano-Ag powder, 0.29g nonylphenol polyoxyethylene ether and 8.68g deionized water according to the proportion, and put them into the high-speed planetary ball mill. In the ta...

Embodiment 2

[0038]A flame-retardant anti-fog wet wipe, comprising 1 part of non-woven fabric and 3 parts of flame-retardant self-cleaning anti-fog liquid by weight, said flame-retardant self-cleaning anti-fog liquid comprising 15.75g of organic fluororesin by weight Emulsion (mass concentration 50%), 3.60g nano aluminum hydroxide powder, 0.04g nano Au powder, 0.45g polyvinylpyrrolidone, 16.95g ethylene glycol, 0.09g polyoxyethylene polyoxypropanol Amino ether, 0.74g of sodium citrate, 1.65g of lavender fragrance microcapsule emulsion (solid content 30%) and 10.14g of deionized water.

[0039] The preparation method is:

[0040] Weigh 3.60g of nano-aluminum hydroxide powder, 0.04g of nano-Au powder, 0.45g of polyvinylpyrrolidone and 10.14g of deionized water according to the proportion, put them into the material tank of the high-speed planetary ball mill, disperse for 5 hours after ball milling and filter to obtain Nano slurry.

[0041] 16.95g ethylene glycol, 0.74g sodium citrate, 0.09...

Embodiment 3

[0047] A flame-retardant anti-fog wet wipe, comprising 1 part of non-woven fabric and 2 parts of flame-retardant self-cleaning anti-fog liquid by weight, said flame-retardant self-cleaning anti-fog liquid comprising 10.78g of silicone emulsion by weight (mass concentration 30%), 14.59 fluorine-modified silicone emulsion (mass concentration 30%), 2.75g nano-magnesia powder, 1.23g nano-antimony oxychloride, 0.03g nano-Ag powder, 0.32g polycarboxylic acid, 21.54 g glycerin, 0.10 g polyoxypropylene polyoxyethylene glyceryl ether, 0.59 g sodium gluconate, 0.27 g sodium citrate, 1.69 g cologne fragrance microcapsule emulsion (solid content 30%) and 10.58 g deionized water.

[0048] The preparation method is:

[0049] Weigh 2.75g nano-magnesia powder, 1.23g nano-antimony oxychloride, 0.03g nano-Ag powder, 0.32g polycarboxylic acid and 10.58g deionized water according to the proportion, put them into the material tank of the high-speed planetary ball mill, and ball mill After dispers...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a flame-retardant antifogging wet tissue and a processing method thereof. The wet tissue is prepared from 1 part of non-woven fabric and 3 to 4 parts of flame-retardant self-cleaning antifogging liquid according to weight ratio, wherein the flame-retardant self-cleaning antifogging liquid is prepared from the following components in percentage by weight: 20 to 30% of hydrophobic resin emulsion, 0.5 to 5% of nano-meter flame retardant, 0.1 to 5% of nano-antibacterial agent, 0.1 to 3% of dispersant, 5 to 15% of antifreezing agent, 0.05 to 1.5% of defoaming agent, 0.5 to 1.5% of chelating agent, 0.5 to 3% of aromatic microcapsule emulsion and 55 to 75% of deionized water. Compared with the prior art, the flame-retardant antifogging wet tissue provided by the invention has the advantages that the nano-meter flame retardant in the formula can form a flame-retardant layer on the surface of organic glass or polymer films of acrylic, polycarbonate, polyester, polystyrene and the like, so that the flame resistance of a material is remarkably improved; an aromatic deodorization function is given to the wet tissue by the added aromatic microcapsule emulsion, and the maintenance of long-term release of the aromatic odor is facilitated.

Description

technical field [0001] The invention relates to a flame-retardant anti-fog appliance, in particular to a flame-retardant anti-fog wet wipe and a processing method thereof. Background technique [0002] In the prior art, general wet wipes are disposable cleaning and sanitary products made of wet-strength, soft-fiber and high-permeability substrates, which are folded, humidified, and packaged. This type of wet wipes generally consists of two parts: a base material and a liquid medicine. The base material of wet wipes is mainly made of non-woven fabrics, and the non-woven fabrics are mainly spunlace non-woven fabrics; the liquid medicine needs to be specially designed according to different users, which is the most technology-intensive production process of wet wipes. core process. Different types of wet wipes have different functions and uses. For example, ordinary wet wipes are mainly used to clean the skin, disinfectant wipes are used to clean small wounds and surroundin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/44D06M11/45D06M11/47D06M11/83D06M13/00D06M13/148D06M13/192D06M13/207D06M15/256D06M15/356D06M15/53D06M15/643
CPCD06M11/44D06M11/45D06M11/47D06M11/83D06M13/005D06M13/148D06M13/192D06M13/207D06M15/256D06M15/3562D06M15/53D06M15/643D06M16/00D06M2200/01D06M2200/12D06M2200/25D06M2200/30
Inventor 宋龙虎
Owner 东莞市荣腾纳米科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com