A waterborne coating composition used for exterior walls of buildings and a preparing method thereof

A water-based technology for building exterior walls, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problem that water-based coatings do not have waterproof performance, high tensile strength and good flexibility, serious environmental pollution, and lack of mechanical performance and other issues, to achieve the effects of excellent mechanical properties, excellent waterproof performance and low cost

Inactive Publication Date: 2017-11-17
天津市金三鑫水性涂料科技有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing water-based coatings do not have excellent waterproof performance, high tensile strength and good flexibility, limited range of application, do not have excellent mechanical properties, high cost, low yield, and serious environmental pollution, so , we propose a water-based coating composition for building exterior walls and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] This embodiment proposes a water-based coating composition for building exterior walls, including the following raw materials in parts by weight: 30 parts of water-based polyurethane emulsion, 25 parts of polyacrylate, 26 parts of isocyanate, 25 parts of polyether, 16 parts of sodium methyl silicate 11 parts of sodium carbonate, 10 parts of talcum powder, 11 parts of mica powder, 12 parts of titanium dioxide, 8 parts of sodium tripolyphosphate, 9 parts of polyoxyethylene fatty acid ester, 7 parts of sodium polyacrylate, 6 parts of tricresyl phosphate , 5 parts of ethylene glycol butyl ether, 4 parts of tetrachloroisophthalonitrile, 3 parts of ethylene glycol, 5 parts of terpineol, and 30 parts of deionized water.

[0020] Present embodiment also proposes a kind of preparation method of water-based coating composition for building exterior wall, comprises the following steps:

[0021] S1: Put water-based polyurethane emulsion, polyacrylate, isocyanate, polyether, sodium ...

Embodiment 2

[0026] This embodiment proposes a water-based coating composition for building exterior walls, including the following raw materials in parts by weight: 33 parts of water-based polyurethane emulsion, 27 parts of polyacrylate, 28 parts of isocyanate, 27 parts of polyether, 18 parts of sodium methyl silicate 13 parts of sodium carbonate, 13 parts of talc powder, 14 parts of mica powder, 15 parts of titanium dioxide, 10 parts of sodium tripolyphosphate, 11 parts of polyoxyethylene fatty acid ester, 9 parts of sodium polyacrylate, and 8 parts of tricresyl phosphate , 7 parts of ethylene glycol butyl ether, 6 parts of tetrachloroisophthalonitrile, 5 parts of ethylene glycol, 7 parts of terpineol, and 32 parts of deionized water.

[0027] Present embodiment also proposes a kind of preparation method of water-based coating composition for building exterior wall, comprises the following steps:

[0028] S1: Put water-based polyurethane emulsion, polyacrylate, isocyanate, polyether, sod...

Embodiment 3

[0033] This embodiment proposes a water-based paint composition for building exterior walls, including the following raw materials in parts by weight: 35 parts of water-based polyurethane emulsion, 29 parts of polyacrylate, 31 parts of isocyanate, 30 parts of polyether, 20 parts of sodium methyl silicate 14 parts of sodium carbonate, 15 parts of talc powder, 16 parts of mica powder, 17 parts of titanium dioxide, 12 parts of sodium tripolyphosphate, 13 parts of polyoxyethylene fatty acid ester, 11 parts of sodium polyacrylate, 10 parts of tricresyl phosphate , 9 parts of ethylene glycol butyl ether, 8 parts of tetrachloroisophthalonitrile, 7 parts of ethylene glycol, 8 parts of terpineol, and 34 parts of deionized water.

[0034] Present embodiment also proposes a kind of preparation method of water-based coating composition for building exterior wall, comprises the following steps:

[0035] S1: Put water-based polyurethane emulsion, polyacrylate, isocyanate, polyether, sodium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based paint composition for building exterior walls and a preparation method thereof, comprising the following raw materials in parts by weight: 30-35 parts of water-based polyurethane emulsion, 25-29 parts of polyacrylate, 26-31 parts of isocyanate, polyether 25‑30 parts, 16‑20 parts of sodium methyl silicate, 11‑14 parts of sodium carbonate, 10‑15 parts of talc powder, 11‑16 parts of mica powder, 12‑17 parts of titanium dioxide, 8‑12 parts of sodium tripolyphosphate 9-13 parts of polyoxyethylene fatty acid ester, 7-11 parts of sodium polyacrylate, 6-10 parts of tricresyl phosphate, 5-9 parts of ethylene glycol butyl ether, 4-8 parts of tetrachloroisophthalonitrile , 3-7 parts of ethylene glycol, 5-8 parts of terpineol, 30-34 parts of deionized water; including the following steps: S1: water-based polyurethane emulsion, polyacrylate, isocyanate, polyether, sodium methyl silicate and deionized water in a blender. The invention has excellent waterproof performance, high tensile strength and good flexibility, and also has excellent mechanical properties, low cost, high yield and no pollution to the environment.

Description

technical field [0001] The invention relates to the technical field of water-based coatings, in particular to a water-based coating composition for building exterior walls and a preparation method thereof. Background technique [0002] The definition of paint refers to a fine chemical product that is coated on the surface of an object by a specific construction method and cured to form a beautiful and continuous protective film with a certain strength on the surface of the object, or to form a coating film with a certain special function. It can cover various defects on the coated surface to make it beautiful, that is, decorative; it can control moisture, isolate corrosive gases such as carbon dioxide, sulfur dioxide, and hydrogen chloride in the air, and prevent the climate from affecting the coated object and the metal substrate. Rust, that is, has a protective function; it can give the surface of the coated object various colors and has a marking effect; in addition, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/08C09D175/04C09D133/04C09D7/12C08G18/48
CPCC09D175/08C08G18/48C08K2201/014C08L2205/02C08L2205/035
Inventor 宋复东李志勇
Owner 天津市金三鑫水性涂料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products