Interior wall coating and preparation method thereof

A technology for interior wall coatings and raw materials, applied in the direction of coatings, etc., can solve the problems of inconspicuous improvement of the indoor environment, and achieve the effects of excellent thermal insulation and sound insulation, low cost, and wide sources

Inactive Publication Date: 2017-12-01
HEFEI SHANGHAN DECORATION ENG CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the prior art, there have been reports about the application of modified nano-bamboo charcoal powder in architectural coatings, but in practical applications, the improvement of indoor environment is not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Interior wall coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An interior wall coating, the following raw materials are weighed: 30kg of acrylic resin, 20kg of silicone acrylic resin, 15kg of modified nano-bamboo charcoal powder, 3kg of barium ice feldspar powder, 5kg of talcum powder, 8kg of styrene-acrylic emulsion, 4kg of diatomaceous earth, and lime calcium powder 1kg, defoamer 1kg, wetting and dispersing agent 2kg, film-forming aid 2kg, leveling agent 1kg and organic solvent 15kg;

[0028] The preparation method of the above-mentioned modified nano-bamboo charcoal powder is: take 15kg of bamboo charcoal powder and put it into glacial acetic acid solution and soak it for 3 hours, take it out, filter it, wash it with deionized water, then calcinate it at 360°C for 1 hour, and then grind it into a nano-powder. .

[0029] Among them, the above-mentioned defoaming agent adopts polydimethylsiloxane; the wetting and dispersing agent adopts calcium lignosulfonate; Two mixtures of isobutyrate, and the mass ratio between the two is 1:...

Embodiment 2

[0035] An interior wall coating, the following raw materials are taken by weighing: 40kg of acrylic resin, 30kg of silicone acrylic resin, 20kg of modified nano-bamboo charcoal powder, 6kg of barium ice feldspar powder, 10kg of talcum powder, 15kg of styrene-acrylic emulsion, 8kg of diatomaceous earth, lime calcium powder 5kg, defoamer 2kg, wetting and dispersing agent 3kg, film-forming aid 3kg, leveling agent 2kg and organic solvent 25kg;

[0036] The preparation method of the above-mentioned modified nano-bamboo charcoal powder is: take 20 kg of bamboo charcoal powder and put it into glacial acetic acid solution to soak for 4 hours, take it out, filter, wash with deionized water, then calcinate at 390 ° C for 1.5 hours, and then grind it into a nano-powder. have to.

[0037] Among them, the above-mentioned defoaming agent adopts phenylethyl alcohol oleate; the wetting and dispersing agent adopts alkyl aryl polyether; Two mixtures of butyrate, and the mass ratio between the ...

Embodiment 3

[0043] An interior wall coating, the following raw materials are taken by weighing: 50kg of acrylic resin, 40kg of silicone acrylic resin, 25kg of modified nano-bamboo charcoal powder, 10kg of barium ice feldspar powder, 16kg of talcum powder, 22kg of styrene-acrylic emulsion, 12kg of diatomaceous earth, lime calcium powder 10kg, defoamer 5kg, wetting and dispersing agent 6kg, film-forming aid 6kg, leveling agent 5kg and organic solvent 35kg;

[0044] The preparation method of the above-mentioned modified nano-bamboo charcoal powder is: take 25kg of bamboo charcoal powder and put it into glacial acetic acid solution and soak it for 5h, take it out, filter it, wash it with deionized water, calcinate it at 420°C for 2h, and then grind it into a nano-powder. .

[0045] Among them, the above-mentioned defoaming agent adopts polyoxypropylene; the wetting and dispersing agent adopts diisooctyl hyaluronate; Two mixtures of diisobutyrate, and the mass ratio between the two is 1:3; ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an interior wall coating and a preparation method thereof. The interior wall coating is prepared from the following raw materials in parts by weight: acrylic resin, silicone acrylic resin, modified bamboo charcoal powder, hyalophane powder, talcum powder, a styrene-acrylic emulsion, kieselguhr, ash calcium powder, a defoaming agent, a wetting dispersant, a coalescing agent, a flatting agent and an organic solvent. The preparation method comprises the steps of firstly adding the defoaming agent, the wetting dispersant, the coalescing agent, the flatting agent and other raw materials to a mixing bowl for mixing evenly to obtain a mixture; grinding the mixture through a sand mill, wherein the fineness of the ground material is smaller than or equal to 10microns; and finally pouring the ground material and remaining raw materials to the mixing bowl for stirring homogenization treatment. The interior wall coating is capable of effectively adsorbing harmful gases in indoor air, regulating the indoor humidity in real time and improving the indoor environment, and is simple in preparation, low in cost, good in paint film property and high in covering power.

Description

technical field [0001] The invention relates to the field of architectural coatings, in particular to an interior wall coating and a preparation method thereof. Background technique [0002] Interior wall paint is an important part of building decoration materials, mostly made of emulsion, deionized water, pigments and other additives. The relatively authoritative book "Painting Technology" in the Chinese coatings industry defines it like this: "Painting is a material that can be coated on the surface of an object by different construction techniques to form a solid adhesion, certain strength, and continuity. Thin film, the film formed in this way is commonly called coating film, also known as paint film or coating." It belongs to organic chemical polymer materials, and the formed coating film belongs to the type of polymer compound. According to the classification of modern chemical products, coatings belong to fine chemical industry Products, modern coatings are gradually...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D133/04C09D125/14C09D7/12
CPCC09D133/00C08K2201/011C08K2201/014C08L2205/035C08L43/04C08L25/14C08K13/06C08K3/04C08K3/34C08K5/103
Inventor 俞克波
Owner HEFEI SHANGHAN DECORATION ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap