Composite PVC sheet produced by using waste PVC
A PVC resin and sheet technology, which is applied in the field of automobile brake system materials, can solve the problems of short service life, insufficient quality, and unattractive appearance of PVC sheets, and achieve good anti-resonance effect, high temperature resistance, and water resistance. Good results
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0018] Raw material ratio of composite PVC sheet: 90 parts of old PVC recycled material, 50 parts of PVC resin, 5 parts of plasticizer, 3 parts of light calcium carbonate, 10 parts of paraffin, 0.5 parts of antifungal agent, 3 parts of stabilizer, UV absorption 5 parts of agent, 20 parts of plant fiber, 15 parts of butyl rubber, 2 parts of dispersant, 0.1 part of coloring agent, 1 part of reinforcing modified filler and 15 parts of vinyl chloride graft copolymer based on ethylene-vinyl acetate resin share.
[0019] Wherein, the ultraviolet absorber in the material in the composite PVC sheet includes nano-γ-FeO(OH), nano-Fe 3 o 4 and nano TiO 3 .
[0020] Wherein, the preparation method of the composite PVC sheet is as follows:
[0021] 1). Preparation of waste PVC material: Firstly, the old recycled PVC material is shredded and washed with hot water at 60°C. After cleaning, it is filtered, dried for 60 minutes, and heated to 80°C for softening. The softened material Carry...
Embodiment 2
[0026] Raw material ratio of composite PVC sheet: 100 parts of old PVC recycled material, 60 parts of PVC resin, 10 parts of plasticizer, 8 parts of light calcium carbonate, 15 parts of paraffin, 1 part of antifungal agent, 5 parts of stabilizer, UV absorption 9 parts of agent, 30 parts of plant fiber, 20 parts of butyl rubber, 3 parts of dispersant, 1 part of coloring agent, 2 parts of reinforced modified filler and 25 parts of vinyl chloride graft copolymer based on ethylene-vinyl acetate resin share.
[0027] Wherein, the ultraviolet absorber in the material in the composite PVC sheet includes nano-TiO 3 , Nano Cu 2 O and nano ZnO.
[0028] Wherein, the preparation method of the composite PVC sheet is as follows:
[0029] 1). Preparation of waste PVC material: Firstly, the old recycled PVC material is shredded and washed with hot water at 75°C. After cleaning, it is filtered, dried for 30 minutes, and heated to 100°C for softening. The softened material Carry out steam ...
Embodiment 3
[0034] Raw material ratio of composite PVC sheet: 95 parts of old PVC recycled material, 55 parts of PVC resin, 8 parts of plasticizer, 5 parts of light calcium carbonate, 12 parts of paraffin, 1 part of antifungal agent, 3 parts of stabilizer, UV absorption 6 parts of agent, 25 parts of plant fiber, 16 parts of butyl rubber, 2 parts of dispersant, 0.5 part of coloring agent, 1 part of reinforcing modified filler and 20 parts of vinyl chloride graft copolymer based on ethylene-vinyl acetate resin share.
[0035] Wherein, the ultraviolet absorber in the material in the composite PVC sheet includes nano-γ-FeO(OH), nano-TiO 3 , Nano Cu 2 O and nano ZnO.
[0036] Wherein, the preparation method of the composite PVC sheet is as follows:
[0037] 1). Preparation of waste PVC material: Firstly, the old recycled PVC material is shredded and washed with hot water at 70°C. After cleaning, it is filtered, dried for 45 minutes, and heated to 90°C for softening. The softened material C...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology