Method for preparing noble metal platinum nano catalyst

A precious metal and platinum nanotechnology, applied in the direction of catalyst activation/preparation, chemical instruments and methods, physical/chemical process catalysts, etc., to achieve the effects of convenient filtration and recovery, good storage stability, and low precious metal content

Inactive Publication Date: 2018-03-30
SHAOXING UNIVERSITY
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the serious lifetime problem in the use of nano-noble metal catalysts, it is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation method of noble metal platinum nano-catalyst, characterized in that: the preparation method according to the following steps:

[0030] Step 1, adding tetraammine platinum acetate to dissolve in water, then adding an acidifying agent, and ultrasonically stirring to obtain a platinum ion solution;

[0031] Step 2, subjecting the platinum ion solution to a sealed reaction for 2 hours, and then distilling under reduced pressure with slight heat to obtain a concentrated solution;

[0032] Step 3, dissolving sodium sulfite into the concentrated solution, and adding an electrolyte for electrolysis for 2 hours to obtain a suspension, which is filtered to obtain a noble metal nano-catalyst.

[0033] The platinum ion concentration of the platinum ion solution in the step 1 is 0.06mol / L, and the acidifying agent adopts acetic acid.

[0034] The frequency of the ultrasonic stirring in the step 1 is 1.5 kHz, and the ultrasonic time is 30 min.

[0035] The sealing rea...

Embodiment 2

[0043] A preparation method of noble metal platinum nano-catalyst, characterized in that: the preparation method according to the following steps:

[0044] Step 1, adding tetraammine platinum acetate to dissolve in water, then adding an acidifying agent, and ultrasonically stirring to obtain a platinum ion solution;

[0045] Step 2, subjecting the platinum ion solution to a sealed reaction for 4 hours, and then distilling under reduced pressure with slight heat to obtain a concentrated solution;

[0046] Step 3, dissolving sodium sulfite into the concentrated solution, and adding an electrolyte for electrolysis for 4 hours to obtain a suspension, which is filtered to obtain a noble metal nano-catalyst.

[0047] The platinum ion concentration of the platinum ion solution in the step 1 is 0.60mol / L, and the acidifying agent is hydrochloric acid.

[0048] The frequency of the ultrasonic stirring in the step 1 is 2.5 kHz, and the ultrasonic time is 60 min.

[0049] The sealing r...

Embodiment 3

[0057] A preparation method of noble metal platinum nano-catalyst, characterized in that: the preparation method according to the following steps:

[0058] Step 1, adding tetraammine platinum acetate to dissolve in water, then adding an acidifying agent, and ultrasonically stirring to obtain a platinum ion solution;

[0059] Step 2, subjecting the platinum ion solution to a sealed reaction for 3 hours, and then distilling under reduced pressure with slight heat to obtain a concentrated solution;

[0060]Step 3, dissolving sodium sulfite into the concentrated solution, and adding an electrolyte for electrolysis for 3 hours to obtain a suspension, which is filtered to obtain a noble metal nano-catalyst.

[0061] The platinum ion concentration of the platinum ion solution in the step 1 is 0.25mol / L, and the acidifying agent adopts acetic acid.

[0062] The frequency of the ultrasonic stirring in the step 1 is 2.0 kHz, and the ultrasonic time is 40 min.

[0063] The sealing reac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of noble metal catalysts, and particularly relates to a method for preparing a noble metal platinum nano catalyst. The method for preparing the noble metal platinumnano catalyst comprises the following steps of: step 1, adding platinum tetra-amino acetate into water for dissolution, then adding an acidifying agent, and performing ultrasonic stirring to obtain aplatinum ion solution; step 2, performing a sealed reaction on the platinum ion solution for 2-4 hours, and then performing gentle heating reduced pressure concentration to obtain a concentrated solution; and step 3, dissolving sodium sulfite in the concentrated solution, and adding an electrolyte into the concentrated solution, conducting an electrolysis reaction for 2-4 hours so as to obtain suspension, and performing filtration to obtain the noble metal platinum nano catalyst. The method for preparing the noble metal platinum nano catalyst has the advantages of a simple preparation process,easy operation, low content of noble metal and a high industrial value.

Description

technical field [0001] The invention belongs to the field of noble metal catalysts, and in particular relates to a preparation method of a noble metal platinum nanometer catalyst. Background technique [0002] Industrial catalysts are generally used in the chemical industry for polymerization, alkylation, hydrogenation, dehydrogenation, oxidation, synthesis, etc. Among them, the use of noble metal series in hydrogenation catalysts is increasing year by year. Carbon-supported noble metal hydrogenation catalysts are widely used in organic synthesis industries such as liquid-phase hydrogenation and dehydrogenation. 2,2-Dichlorohydroazobenzene dye intermediate is the raw material of azo dyes and organic pigments. It has a very large market demand in the fine chemical industry. bits get. The zinc powder reduction method was used in the early industrial production. Although the cost was low, the product yield was low (about 70%), which actually increased the cost. In recent ye...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/42B01J37/10B01J37/34C07F7/18
CPCB01J23/42B01J35/0013B01J37/10B01J37/342C07F7/1804C07F7/1876
Inventor 李志彬徐海涛
Owner SHAOXING UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap