A highly weather-resistant, water-based technology, used in biocide-containing paints, antifouling/underwater coatings, coatings, etc., can solve the problems of poor weather resistance, poor mildew resistance, and easy delamination of paint films, and achieve dense paint films. The effect of flexibility, strong mildew resistance, and not easy to yellow

Inactive Publication Date: 2018-03-30
上海君子兰新材料股份有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to provide high weather-resistant water-based mildew-resistant varnish for woodware, solve the problems ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly weather-resistant waterborne mildewproof varnish for wooden ware
  • Highly weather-resistant waterborne mildewproof varnish for wooden ware
  • Highly weather-resistant waterborne mildewproof varnish for wooden ware

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0025] Embodiment 2: raw material proportioning adopts the following table:

[0026]

[0027]

[0028] Adjust the viscosity to 70KU.

[0029] project

mass percentage

Water-Based Acrylic Emulsion

80%

BYK 024

0.2%

BYK 028

0.3%

BYK 346

0.3%

AMP 95

0.1%

leveling agent

0.3%

DPnB

3.5%

Deionized water

12.45%

In-tank fungicide

0.05%

UV absorber

0.7%

light stabilizer

0.7%

Dry film antifungal agent

1.2%

PUR 40

0.2%

[0030] Adjust the viscosity to 70KU.

[0031] In the embodiment of the present invention, the water-based acrylic emulsion can form a cross-linked network structure when forming a film, has high toughness and water resistance, and can be used in some places with high waterproof requirements outdoors, semi-outdoors or some indoors. The defoamer is one or a combination of water-based non-silicone fatty acid po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a highly weather-resistant waterborne mildewproof varnish for wooden ware. The highly weather-resistant waterborne mildewproof varnish is prepared from the following raw materials in percentage by weight according to a proportional ratio: 65 to 80% of waterborne acrylic emulsion, 0.2 to 0.5% of defoamer, 0.2 to 0.5% of wetting agent, 0.1 to 0.2% of ammonia neutralizing agent, 0.2 to 0.5% of flatting agent, 2 to 5% of film-forming additive, 2 to 15% of deionized water, 0.05 to 0.1% of tank internal sterilizant, 0.1 to 0.5% of ultraviolet light absorbent, 0.1 to 0.5% oflight stabilizer, 0.5 to 1.5% of dry film mildewproof agent, and 0.1 to 2% of thickener. The highly weather-resistant waterborne mildewproof varnish has the advantages that the deionized water is usedfor blending the film-forming additive, the internal sterilizant and the dry film mildew-proof agent, the filming property is good, a paint film is dense, flexible and tough, the high temperature-resistant property and water-resistant property are good, the easiness in whitening is avoided, the chemical stability is excellent, and the easiness in cracking due to temperature differences between daytime and night and weather change is avoided; the environment-friendly effect is realized, the content of VOC (volatile organic compound) is low, the heavy metal is not contained, the sunlight radiation-resistant property is realized, the easiness in yellowing, delaminating and aging is avoided, the mildew-proof property is strong, and the outdoor common mildews and bacteria with function on woodcan be resisted.

Description

technical field [0001] The present invention relates to the application technology of IPC classification C09D paint composition raw material for this purpose, especially the highly weather-resistant water-based mildew-proof varnish for woodware. Background technique [0002] Water-based paint is a paint that uses water as a diluent. Water-based paints include water-soluble paints, water-diluted paints, water-dispersible paints or latex paints. Water-soluble paints use water-soluble resins as film-forming materials, represented by polyvinyl alcohol and its various modified products, in addition to water-soluble alkyd resins, water-soluble epoxy resins, and inorganic polymer water-based resins. [0003] At present, water-based wood paints have achieved good results in indoor furniture, but for some outdoor wood products such as outdoor floors, park seats, gazebos, plant landscape fences, etc., there are still many shortcomings in water-based paints. The two main aspects are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D5/14
CPCC09D133/04C09D5/14
Inventor 杨艳丹马强华邓文根
Owner 上海君子兰新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products