A method for regenerating an amination catalyst used for the hydroamination of polyether polyols to prepare polyetheramines

A technology of alcohol hydrogen amine and polyether multi-component, which is applied in the field of regeneration of amination catalysts for the preparation of polyether amines by hydrogen amination of polyether polyols, and can solve the problems of catalyst activity reduction, active component sintering, and Dispersion reduction and other problems to achieve the effect of improving activity

Active Publication Date: 2021-01-15
WANHUA CHEM GRP CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The common problem of the above-mentioned amination catalyst: the activity of the catalyst decreases with the increase of the use time during use, that is, the catalyst is deactivated
In the washing process of this patent, a large amount of organic solvent is used to wash the catalyst, which has the problems of solvent waste and solvent recovery cost; while the impregnation process uses a concentrated nitric acid solution with an acid concentration of 15-30% to impregnate the catalyst, which destroys the structure of the alumina carrier and dissolves the activity. The problem of components; during the roasting process, air or nitrogen or a mixture of air and nitrogen in any proportion is used for high-temperature roasting, which solves the problem of carrier alumina rehydration and will lead to a decrease in the dispersion of active components and sintering of active components

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] (1) Washing step: add the deactivated catalyst into the acetic acid solution with a concentration of 5wt% according to the solid-to-liquid volume ratio of 1:1, heat to reflux for 8 hours, filter, wash until neutral, and dry.

[0050] (2) Roasting step: under normal pressure, place the amination catalyst obtained by washing and drying in a fixed-bed reactor and raise the temperature to 400°C at a heating rate of 3°C / min. A hydrogen peroxide solution with a concentration of 16wt% was used for charcoal regeneration, and the roasting time was 5 hours until no CO2 was detected in the tail gas, and the temperature was lowered to obtain a roasted and regenerated amination catalyst.

[0051] (3) Reduction step: under normal pressure, the fixed bed reactor is heated to 200°C, the heating rate is 0.5°C / min, and the hydrogen / nitrogen gas mixture with a volume ratio of 1:40 is fully reduced for 5 hours, and the temperature is lowered to obtain the reduction Regenerated amination ca...

Embodiment 2

[0055] (1) Washing step: Add the deactivated catalyst into the acetic acid solution with a concentration of 30wt% according to the solid-to-liquid volume ratio of 1:5, heat to reflux for 10 hours, filter, wash until neutral, and dry.

[0056] (2) Roasting step: under normal pressure, place the amination catalyst obtained by washing and drying in a fixed-bed reactor and raise the temperature to 300°C at a heating rate of 1°C / min. A hydrogen peroxide solution with a concentration of 20 wt% is used for charcoal regeneration, and the roasting time is 10 hours, until no CO2 is detected in the tail gas, and the temperature is lowered to obtain a roasted and regenerated amination catalyst.

[0057] (3) Reduction step: under normal pressure, the fixed bed reactor is heated to 100°C, the heating rate is 0.8°C / min, and the hydrogen / nitrogen gas mixture with a volume ratio of 1:10 is fully reduced for 15 hours, and the temperature is lowered to obtain the reduction Regenerated amination ...

Embodiment 3

[0061] (1) Washing step: add the deactivated catalyst into the acetic acid solution with a concentration of 20wt% according to the solid-to-liquid volume ratio of 1:8, heat to reflux for 5 hours, filter, wash until neutral, and dry.

[0062] (2) Roasting step: under normal pressure, place the amination catalyst obtained by washing and drying in a fixed-bed reactor and raise the temperature to 450°C at a heating rate of 5°C / min. A hydrogen peroxide solution with a concentration of 15 wt% is used for charcoal regeneration, and the roasting time is 8 hours, until no CO2 is detected in the tail gas, and the temperature is lowered to obtain a roasted and regenerated amination catalyst.

[0063] (3) Reduction step: under normal pressure, the fixed bed reactor is heated to 250°C, the heating rate is 1°C / min, and the hydrogen / nitrogen gas mixture with a volume ratio of 1:20 is fully reduced for 8 hours, and the temperature is lowered to obtain the reduction Regenerated amination catal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for regenerating an amination catalyst used for preparing polyether amine by hydroamination of polyether polyols. The method comprises: (A) adding an inactivated amination catalyst to an organic acid solution, and heating to reflux , filtered, washed, and then dried; (B) the amination catalyst obtained by washing and drying treatment is regenerated by burning charcoal in the presence of hydrogen peroxide to obtain a regenerated amination catalyst after roasting; (C) roasting the catalyst with hydrogen The regenerated amination catalyst is reduced to obtain a regenerated amination catalyst. The regeneration treatment method of the present invention has solved because coking even carbon deposition, catalyst active component copper sintering and Ni 0 Regeneration method of deactivated amination catalyst caused by crystal phase aggregation. The regeneration treatment method of the present invention is mainly applied to the regeneration treatment process of the amination catalyst for preparing polyetheramine by hydroamination of polyether polyol.

Description

technical field [0001] The present invention relates to a method for regeneration of an amination catalyst used for the hydroamination of polyether polyols to prepare polyetheramines, more precisely, it relates to alumina as a carrier, selected from Ni, Co, Cu and Pd Two or more metals are active components selected from Zr, Cr, Mo, Fe, Zn, Sn, Ce, Mg, Mn, La, Hf, Sr, V, Mn, W, Pb, Pt, Ag, Rh, Ru, Bi, Nd, Sb and Be additives in the catalyst composed of more than one metal or its oxides are used in the hydrogenation of polyether polyols to prepare polyether amine amination reaction deactivation after regeneration, The invention belongs to the technical field of catalysts. Background technique [0002] Polyether amine, also known as amino-terminated polyether (ATPE for short), is a kind of polyoxyalkylene compound whose molecular main chain is polyether skeleton and the end is blocked by amino group. Most of these amino-terminated polyethers use polyether (polyethylene glyco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/89B01J23/96B01J38/02B01J38/10B01J38/16B01J38/62C07C213/02C07C217/08C08G65/328C08G65/48
CPCB01J23/8993B01J23/96B01J38/02B01J38/10B01J38/16B01J38/62C07C213/02C08G65/328C08G65/48C07C217/08Y02P20/584
Inventor 任树杰张聪颖李鑫刘振国唐磊吴健姜庆梅曹善健黎源
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com