A magnetic polymer adsorption material, preparation method and application

An adsorption material and polymer technology, applied in chemical instruments and methods, magnetic/electric field water/sewage treatment, other chemical processes, etc., can solve problems that cannot adapt to the broad-spectrum adsorption of organic matter

Active Publication Date: 2020-07-31
NANJING UNIV +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Aiming at the limitations of the adsorption of the magnetic materials prepared in the prior art and the inability to adapt to the defects of broad-spectrum adsorption of organic matter in water bodies, the present invention aims to provide a high magnetic material with good particle size uniformity, strong magnetism and strong adsorption. molecular adsorption material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A magnetic polymer adsorption material, preparation method and application
  • A magnetic polymer adsorption material, preparation method and application
  • A magnetic polymer adsorption material, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] In this embodiment, the steps for preparing the magnetic polymer adsorption material are as follows:

[0040] (1), preparation of magnetic Fe 3 o 4 @oleic acid nanoparticles: Add 1g of ferrous chloride and 2g of ferric chloride, 100mL of water into a 250mL flask, stir and mix evenly, protect with nitrogen, then add 4mol / L sodium hydroxide solution at 60°C 20mL, oleic acid 0.75g, at this moment, the quality of described oleic acid is magnetic Fe 3 o 4 0.5 times that of nanoparticles. After reacting for 10 hours, adjust the pH value of the solution to 3, wash the product with water and ethanol for 5 times, and obtain the magnetic Fe after drying. 3 o 4 @oleic acid nanoparticles.

[0041] (2), preparation of oil phase solution: 2g magnetic Fe 3 o 4 @Oleic acid nanoparticles were dissolved in 30mL of toluene solution, respectively added 3g N-vinylpyrrolidone, 3g divinylbenzene, 0.05g AIBN, and mixed in an ice bath to obtain an oil phase solution. The mass of N-vinyl...

Embodiment 2

[0057] In this embodiment, the steps for preparing the magnetic polymer adsorption material are as follows:

[0058] (1), preparation of magnetic Fe 3 o 4 @oleic acid nanoparticles: Add 2.6g ferrous chloride and 6.4 ferric chloride, 200mL water into a 500mL flask, stir and mix evenly, protect with nitrogen, then add 2mol / L potassium hydroxide at 100°C Solution 40mL, oleic acid 4g, the quality of described oleic acid is magnetic Fe 3 o 4 2 times that of nanoparticles; after 6 hours of reaction, the pH value of the solution was adjusted to 3. The product was washed 5 times with water and methanol and dried to obtain the magnetic Fe 3 o 4 @oleic acid nanoparticles.

[0059] (2), preparation of oil phase solution: 1g magnetic Fe 3 o 4 @Oleic acid nanoparticles were dissolved in 10mL of cyclohexanol solution, 2g of N-vinylpyrrolidone, 1.5g of divinylbenzene, and 0.07g of AIBN were added respectively, and mixed evenly in an ice bath to obtain an oil phase solution. The mass...

Embodiment 3

[0063] In this embodiment, the steps for preparing the magnetic polymer adsorption material are as follows:

[0064] (1), preparation of magnetic Fe 3 o 4 @oleic acid nanoparticles: Add 1g of ferrous chloride and 7g of ferric chloride, 100mL of water into a 250mL flask, stir and mix evenly, protect with nitrogen, then add 20mL of saturated ammonia solution and 3g of oleic acid at a temperature of 70°C , the quality of the oleic acid is magnetic Fe 3 o 4 1.7 times that of nanoparticles; after 0.5 hours of reaction, the pH value of the solution was adjusted to 3. The product was washed 5 times with water and methanol and dried to obtain the magnetic Fe 3 o 4 @oleic acid nanoparticles.

[0065] (2), preparation of oil phase solution: 2g magnetic Fe 3 o 4@Oleic acid nanoparticles were dissolved in 30mL of DMF solution, 3g of N-vinylpyrrolidone, 2g of divinylbenzene, and 0.1g of BPO were added respectively, and mixed in an ice bath to obtain an oil phase solution. The mass...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a magnetic polymer adsorption material, a preparation method and an application, and belongs to the field of magnetic polymer materials. The preparation method comprises the following steps: (1) preparing magnetic nanoparticles; (2) dissolving the magnetic nanoparticles in a porogen, adding N-vinylpyrrolidone, divinylbenzene and an initiator respectively, and mixing them uniformly; (3) ) adding an emulsifier and a dispersant to the aqueous solution; adding a part of the oil phase solution prepared in step (2) when the temperature is lower than 60 °C, adding the rest of the oil phase solution when the temperature rises above 60 °C, stirring the reaction, and then carrying out Precipitate, filter, wash, and dry to finally obtain the magnetic polymer adsorption material. The particle size of the material is between 2 and 100 μm, the magnetization is 5 to 19.5 emu / g, and the specific surface area is 210 to 950 m 2 / g, the material can be applied to the adsorption of inorganic and organic substances in the solution, the controlled release of inorganic and organic substances, and the separation of different substances.

Description

technical field [0001] The invention belongs to the field of polymer material preparation method and application thereof, and in particular relates to a magnetic polymer adsorption material, its preparation method and application. Background technique [0002] In recent years, magnetic polymer materials have shown great application potential in the pretreatment and adsorption removal of environmental pollutants due to their high adsorption capacity and good separation performance. At present, the magnetic polymer adsorption materials used in the environmental field are mainly divided into two categories, one is ion exchange type, and the other is ultra-high cross-linked materials with high specific surface area. [0003] After searching, the related application has been published in the prior art; Chinese Patent No. CN201010017687.1, the application whose publication date is 2012.07.04 discloses a preparation method of magnetic acrylic acid series strong base anion exchange ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/26B01J20/28B01J20/30
CPCB01J20/26B01J20/28009B01J20/3085B01J20/28064B01J20/28021B01J20/06B01J20/28061B01J20/261B01J20/3064B01J20/3071B01J20/22B01J20/28004C02F2305/08C02F1/488C02F2101/305C02F2303/16C02F1/288C02F1/285C02F1/281C02F1/48C02F2101/10C02F2101/30
Inventor 周庆姚志建李爱民焦伟双陈冬李启蒙孙杰
Owner NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com