Antibacterial polyvinyl chloride resin and preparation method thereof

A technology of polyvinyl chloride resin and fluorine epoxy resin, which is applied in the field of antibacterial polyvinyl chloride resin and its preparation, and can solve the problems of insufficient antibacterial performance of polyvinyl chloride resin, etc.

Inactive Publication Date: 2018-05-08
HWASU
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the technical problems existing in the background technology, the present invention proposes a kind of antibacterial polyvinyl chloride resin and its preparation method, to solve the Chinese patent application literature "a kind of polyvinyl chloride resin and its preparation method and application (application publication number: CN101143954A) " the problem that the polyvinyl chloride resin antibacterial performance that discloses is insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] The preparation method of described antibacterial polyvinyl chloride resin, comprises the following steps:

[0021] S1. Mix polyvinyl chloride resin, polylactic acid, organic fluorine epoxy resin, polyphenylene sulfide, polycarbonate, polyhydroxybutyrate and vinyl acetate in parts by weight, heat up to 70-80°C, and keep warm for 20 -30min, then add calcium molybdate, chitosan, zinc borate, diatomaceous earth, wood fiber powder and chlorinated paraffin, mix well, continue to heat up to 90-100°C, keep warm for 15-25min, then heat at 850-1050r / min Stir at a rotating speed for 30-50min, cool to room temperature to obtain the base material;

[0022] S2. Mix zinc phosphate, fluorine micropowder, nano-titanium dioxide, silane coupling agent KH-560 and antibacterial modification additive evenly, heat up to 60-80°C, keep warm for 10-20min, and then stir at 680-980r / min for 15 -25min, cooled to room temperature to obtain modified material;

[0023] S3. Raise the temperature of ...

Embodiment 1

[0026] An antibacterial polyvinyl chloride resin, in parts by weight, comprising the following raw materials: 70 parts of polyvinyl chloride resin, 35 parts of polylactic acid, 20 parts of organic fluorine epoxy resin, 6 parts of polyphenylene sulfide, and 3.5 parts of polycarbonate , 3 parts of polyhydroxybutyrate, 4.5 parts of vinyl acetate, 3 parts of calcium molybdate, 3.5 parts of chitosan, 4.5 parts of zinc borate, 4 parts of diatomaceous earth, 3 parts of wood fiber powder, 4.5 parts of chlorinated paraffin, 4 parts of polyethylene glycol, 3 parts of trioctyl trimellitate, 4.5 parts of polycaprolactone, 4 parts of trimethyl phosphate, 2.5 parts of tributyl citrate, 4 parts of adipic hydrazide, 3.5 parts of tartaric acid, 2.5 parts of potassium persulfate, 4.5 parts of zinc phosphate, 6 parts of fluorine micropowder, 7.5 parts of nano titanium dioxide, 4 parts of silane coupling agent KH-560, 25 parts of antibacterial modification additive.

[0027] The modifier is prepa...

Embodiment 2

[0033] An antibacterial polyvinyl chloride resin, in parts by weight, comprising the following raw materials: 60 parts of polyvinyl chloride resin, 50 parts of polylactic acid, 15 parts of organic fluorine epoxy resin, 9 parts of polyphenylene sulfide, and 2 parts of polycarbonate , 5 parts of polyhydroxybutyrate, 3 parts of vinyl acetate, 5 parts of calcium molybdate, 2 parts of chitosan, 6 parts of zinc borate, 2 parts of diatomaceous earth, 5 parts of wood fiber powder, 3 parts of chlorinated paraffin, 6 parts of polyethylene glycol, 1 part of trioctyl trimellitate, 6 parts of polycaprolactone, 2 parts of trimethyl phosphate, 4 parts of tributyl citrate, 3 parts of adipic hydrazide, 5 parts of tartaric acid, 1 part of potassium persulfate, 6 parts of zinc phosphate, 4 parts of fluorine micropowder, 9 parts of nano titanium dioxide, 3 parts of silane coupling agent KH-5603, 30 parts of antibacterial modification additive.

[0034] The modifier is prepared according to the fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses antibacterial polyvinyl chloride resin, and belongs to the technical field of resin preparation. The antibacterial polyvinyl chloride resin is prepared from polyvinyl chlorideresin, polylactic acid, organic fluorine epoxy resin, polyphenylene sulfide, polycarbonate, polyhydroxybutyrate, vinyl acetate, calcium molybdate, chitosan, zinc borate, kieselguhr, wood fiber powder,chlorinated paraffin, polyethylene glycol, trioctyl trimellitate, polycaprolactone, trimethyl phosphate, tributyl citrate, adipic dihydrazide, tartaric acid, potassium peroxodisulfate, zinc phosphate, fluorine micro powder, nanometer titania, a silane coupling agent KH-560 and antibacterial performance additives. The antibacterial polyvinyl chloride resin is prepared through the steps of preparing a base material, preparing a modified material, mixing the base material, the modified material and other materials and the like. The prepared polyvinyl chloride resin has the excellent antibacterial performance.

Description

technical field [0001] The invention relates to the technical field of resin preparation technology, in particular to an antibacterial polyvinyl chloride resin and a preparation method thereof. Background technique [0002] The main component of polyvinyl chloride resin is polyvinyl chloride, and other components are added to enhance its heat resistance, toughness, ductility, etc. It is a well-loved, popular and widely used synthetic material in the world today. It is the second most used synthetic material worldwide. According to statistics, in 1995 alone, the production of PVC in Europe was about 5 million tons, while its consumption was 5.3 million tons. In Germany, PVC production and consumption average 1.4 million tons. PVC is being produced and applied all over the world at a growth rate of 4%. The growth rate of PVC in Southeast Asia is particularly significant, thanks to the urgent needs of infrastructure construction in Southeast Asian countries. Among the mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L67/04C08L63/00C08L81/02C08L5/08C08L97/02C08L91/06C08L71/02C08L27/12C08K13/06C08K3/22C08K3/32C08K9/12C08K3/28
CPCC08L27/06C08K2003/2241C08K2003/328C08K2201/011C08L2205/025C08L2205/035C08L2205/16C08L67/04C08L63/00C08L81/02C08L5/08C08L97/02C08L91/06C08L71/02C08L27/12C08K13/06C08K3/22C08K3/32C08K9/12C08K3/28
Inventor 丘永桂魏昭辉
Owner HWASU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap