A structural engineering, high-performance technology, applied in the field of building materials, can solve the problems of few types, low strength, high water absorption, and achieve the effect of improving various properties
Active Publication Date: 2021-08-06
SOUTHWEAT UNIV OF SCI & TECH
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
There are few types of high-strength lightweight aggregate products in my country, high water absorption (>5%), and generally low strength (cy
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
example 1
[0025] The main process of producing high-performance light bones on the binocular rotary kiln ceramics production line is:
[0026] 1) The mixture is mixed with a mandatory stirring mixer, and the raw powder passes through the belt conveyor into the ball disk, and the light bone material ball, agonized, and after drying after 8 ~ 12mm;
[0027] 2) Light bone material balls from the kiln tail feeding into the rotary kiln system, preheating the kiln (rear section of the double barrel rotary kiln) Rotary 1.2R / min, calcined kiln (front section of the double barrel rotary kiln) turn 1.8R / min, life The residence time in the kiln in the kiln is about 30 to 60 min, and the temperature of the kiln head is controlled at 1250 to 1380 ° C;
[0028] 3) After the roasting clinker is removed by the kiln head, the discharge temperature is 950 to 1100 ° C, forced air cooling to 100 ° C, and is sent to the yard by the conveyor;
[0029] Among them, the raw material and ingredients of the raw p...
example 2
[0031] The specific implementation process of the process process is in Example 1, in which the raw material and ingredients of the raw powder and the ingredients are 45 copies, 1 kaolin, 5 partsilish ash, 29 parts of the dolomite; every 100 Base) Add: 1 part of calcium carbonate, 5 copies of pulverized coal, 2 parts TiO2.
example 3
[0033] The specific implementation process of the process process is in Example 1, in which the raw material and ingredients of the raw powder and the ingredients are: 1,4 of aluminum soil, 54 high-carbon chrome-free metal; Base) Add: 1 coal, 5 pieces of iron powder, 5 parts of TiO2, 2 parts ZrO2, 0.5 parts boron oxide.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-performance lightweight aggregate design idea and method with the main goal of regulating the mineral composition. To achieve the purpose of greatly improving the relative performance of lightweight aggregate. The content of the present invention is: use silicon-aluminum raw materials and magnesium raw materials, and add suitable crystal nucleating agents, swelling agents and fluxing agents, mix the materials, obtain raw meal balls after balling, and obtain cordierite-based pellets after firing. High performance lightweight aggregate with main crystal phase. The implementation of the invention can provide a simple, easy and operable solution for the preparation of high-performance lightweight aggregate.
Description
Technical field [0001] The present invention relates to a high-performance light bone material belonging to the field of building materials. Background technique [0002] At present, high-strength light aggregate concrete (LC40) formulation technology has become mature, highly high, high durability and overall cost reduction, so that it has a very significant comparative advantage in the field of structural engineering, especially in high-level and super High-rise buildings, as well as the superiority of large span bridges. Therefore, the application of light bone material concrete in structural engineering has gradually matured, and it will have a very broad prospect in the future. [0003] Structural engineering light bones are generally high-strength poster, sintered ceramics and vaporized ceramics. But unfortunately, the design theory of the above three high-strength and light aggregates still uses ordinary ceramsite ideas, that is, the main raw materials are mainly based on ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more