A kind of hydrophilic polyvinylidene fluoride resin

A polyvinylidene fluoride resin, hydrophilic technology, applied in water/sewage treatment, water/sludge/sewage treatment, osmosis/dialysis water/sewage treatment, etc. question

Active Publication Date: 2021-04-09
ZHEJIANG QUZHOU JUSU CHEM IND CO LTD +2
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the nanoparticles on the surface are easy to fall off, and have almost no removal effect on heavy metal ions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrophilic polyvinylidene fluoride resin
  • A kind of hydrophilic polyvinylidene fluoride resin
  • A kind of hydrophilic polyvinylidene fluoride resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of hydrophilic polyvinylidene fluoride resin, its raw material formula is as follows:

[0024]

[0025]

[0026] The preparation method is as follows:

[0027] (1) Suspension polymerization

[0028] After adding 240kg of deionized water to the polymerization kettle, replace it with high-purity nitrogen gas. After the replacement is qualified, add 70kg of VDF monomer, 30kg of acrylic acid, 0.09kg of hydroxymethyl cellulose, 0.3kg of mercaptan, 0.4kg of diisopropyl peroxycarbonate and 10kg of deionized water was reacted at a stirring speed of 55rpm, the reaction temperature was 35°C, the reaction time was 12h, and the reaction pressure was 2.7Mpa to obtain a suspension polymerization product;

[0029] (2) Post-processing of suspension polymerization products

[0030] Wash the suspension polymerization product obtained in step (1) three times with deionized water (washing speed: 30rpm), then wash three times with deionized water at 60°C, then centrifuge and ...

Embodiment 2

[0032] A kind of hydrophilic polyvinylidene fluoride resin, its raw material formula is as follows:

[0033]

[0034] The preparation method is the same as in Example 1, and the analytical data of the product are shown in Table 1.

Embodiment 3

[0036] A kind of hydrophilic polyvinylidene fluoride resin, its raw material formula is as follows:

[0037]

[0038] The preparation method is the same as in Example 1, and the analytical data of the product are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrophilic polyvinylidene fluoride resin, which is prepared from the following components in parts by weight: 60-90 parts of VDF monomer, 10-50 parts of comonomer, and 0.05-1.5 parts of dispersant , 0.1-0.5 parts of chain transfer agent, 0.1-1.0 parts of initiator. The ultrafiltration membrane made of the hydrophilic polyvinylidene fluoride resin of the invention has good hydrophilicity, high membrane flux, long service life and good removal effect on metal ions.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a preparation method of hydrophilic polyvinylidene fluoride resin. Background technique [0002] Polyvinylidene fluoride (PVDF) has been widely used in the preparation of microstructures due to its good mechanical properties, heat resistance, chemical corrosion resistance and easy film formation, so that the corresponding film has excellent chemical oxidation resistance and corrosion resistance. Water treatment membrane fields such as filtration, ultrafiltration and reverse osmosis membranes. However, due to the strong hydrophobicity of PVDF, PVDF membranes have defects such as low water flux, easy to be polluted by organic matter, and short service life, and conventional PVDF water treatment membranes have almost no removal effect on heavy metal ions, which severely limit PVDF membranes. The scope of application of water treatment membranes. [0003] Conv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F214/22C08F222/02C08F220/06C08F2/38C08F2/18C08F2/20B01D71/34B01D61/14C02F1/44
CPCB01D61/145B01D71/34C02F1/444C08F2/18C08F2/20C08F2/38C08F214/22C08F220/06C08F222/02