Preparation method of plastic slipping agent

A slip agent and plastic technology, applied in the field of plastic slip agent preparation, can solve the problems of long-term antistatic, single performance, film haze, transparency, etc., to improve appearance quality and enhance moisturizing effect. , the effect of small wet angle

Inactive Publication Date: 2018-09-04
袁杰
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a plastic slippery agent for the problems that the current existing plastic slippery products have single performance, cannot be used for long-term antistatic effects on plastic films and plastic products, and have a great influence on film haze and transparency. The preparation method of the agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] A preparation method of a plastic slippery agent, the preparation method comprising the steps of:

[0018] (1) Take aluminum-nickel alloy powder and add it to sodium hydroxide solution at a mass ratio of 3:20, stir and mix at 25~30°C, let it stand still, take the precipitate and wash it with distilled water to obtain washings, take oleic acid amide at a mass ratio of 30 : 1 Add washings, stir and mix at 70~75°C, pass through hydrogen protection, keep warm at 0.4MPa, 150~160°C for 3~4h, cool to room temperature, and obtain the cooled product;

[0019] (2) Take toluene and add anhydrous calcium chloride and metal sodium powder according to the mass ratio of 10:5:1, stir and mix, distill at atmospheric pressure, collect fractions at 110~112°C to obtain distillates, and take cooling substances according to the mass ratio Add the distillate at a ratio of 1:6, heat up to 40~55°C, stir and mix to obtain a mixture, take 3-chloropropyltrimethoxysilane and add the distillate at a...

Embodiment 1

[0023] Oleic acid amide: purchased from Jiangxi Weike Oleochemical Co., Ltd.

[0024] A preparation method for a plastic slippery agent, comprising the steps of:

[0025] (1) Take aluminum-nickel alloy powder and add it into sodium hydroxide solution with a mass fraction of 25% according to the mass ratio of 3:20, stir and mix at 25°C for 3 hours, let it stand, take the precipitate and wash it with distilled water to obtain the washing, and take oleic acid Amide was added to the washings at a mass ratio of 30:1, stirred and mixed at 70°C for 20 minutes, introduced with hydrogen, kept at 0.4MPa and 150°C for 3 hours, and cooled to room temperature to obtain the cooled substance;

[0026] (2) Take toluene and add anhydrous calcium chloride and metal sodium powder at a mass ratio of 10:5:1, stir and mix for 5 hours, distill at atmospheric pressure, collect fractions at 110°C to obtain distillates, and take cooling substances at a mass ratio of 1 : 6 Add the distillate, heat up t...

Embodiment 2

[0030] Oleic acid amide: purchased from Jiangxi Weike Oleochemical Co., Ltd.

[0031] A preparation method for a plastic slippery agent, comprising the steps of:

[0032](1) Take the aluminum-nickel alloy powder and add it to the sodium hydroxide solution with a mass fraction of 25% according to the mass ratio of 3:20, stir and mix at 30°C for 5 hours, let it stand, take the precipitate and wash it with distilled water to obtain the washing, and take oleic acid Amide was added to the washings at a mass ratio of 30:1, stirred and mixed at 75°C for 30 minutes, introduced with hydrogen, kept at 0.4MPa and 160°C for 4 hours, and cooled to room temperature to obtain the cooled substance;

[0033] (2) Take toluene and add anhydrous calcium chloride and metal sodium powder at a mass ratio of 10:5:1, stir and mix for 6 hours, distill at atmospheric pressure, collect fractions at 112°C to obtain distillates, and take cooling substances at a mass ratio of 1 : 6 Add the distillate, heat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a plastic slipping agent, which belongs to the technical field of fine chemical industry. Unsaturated components of oleamide such as linoleic acid amideand linolenic acid amide are removed by adopting a skeleton nickel selective hydrogenation method, so that a substance with higher purity which can reduce the viscosity of plastic resin melt and improve the mobility can be obtained, then the obtained oleamide substance is used for modifying 3-gamma-chloropropyl trimethoxysilane, and when the oleamide substance is added in the preparation processof a plastic product, the surface tension of a plastic film is reduced, the wetting angle is reduced, and the wetting effect of the plastics can be improved. As the content of polyether chains is increased, the surface water absorption performance of the plastics is improved, the surface resistivity is reduced, and the antistatic capability is improved. The problems that the existing plastic slipping agent is single in product performance, the plastic film and the plastic product cannot resist the static electricity for a long time and the haze and transparency of the film are severely influenced can be solved.

Description

technical field [0001] The invention belongs to the technical field of fine chemicals, and in particular relates to a preparation method of a plastic smoothing agent. Background technique [0002] The slip agent belongs to one of the products in the slip agent technical field. Slip agent is a white or light yellow powder, which is used to enhance the resistance to mechanical stirring and shearing force. The main ingredients are edible colloid, enzyme preparation and emulsifier. Plastic slip agent is a white neutral powdery solid, which has good dispersibility to various substances such as dyes and pigments. In plastic processing, it can play the role of smoothing, lubricating, glazing, demoulding, anti-adhesive, anti-caking, anti-humidity, anti-static, dispersing and increasing the surface brightness of the product, without affecting the transparency and physical properties of the final product. nature. It is an ideal new, high-efficiency, non-toxic plastic processing lu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L77/12C08K13/06C08K9/06C08K9/04C08K3/16C08K3/08C08K5/20C08K5/134
CPCC08K2003/0812C08K2003/0862C08K2003/162C08L23/12C08L2201/10C08L77/12C08K13/06C08K9/06C08K9/04C08K3/16C08K3/08C08K5/20C08K5/1345
Inventor 袁杰庄文琴丁正颖
Owner 袁杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com