Building waterproof paint and preparation method thereof

A technology for building waterproofing and coatings, applied in the field of building waterproofing coatings, can solve the problems of poor film formation, difficult to meet the requirements of waterproof performance, affecting the wide application of environmental protection coatings, etc. strong effect

Inactive Publication Date: 2018-09-14
德泰建设有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating also has problems such as slightly poor film-forming property and difficult to meet the requirements of waterproof performance when used, which affects the wide application of environmentally friendly coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Building waterproof paint and preparation method thereof
  • Building waterproof paint and preparation method thereof
  • Building waterproof paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The raw materials for the preparation of the architectural waterproof coating described in this example include: 30kg of glutinous rice flour, 20kg of crop starch, 8kg of quartz powder, 20kg of diatom mud, 1kg of calcite powder, 8kg of polyglutamic acid, 8kg of polylactic acid fiber, [choline] L-glutamine 10kg, and plant hydrolyzate.

[0025] Wherein, the polylactic acid fiber is a fiber with a length of 0.1-0.5 mm and a diameter of less than 0.5 mm.

[0026] The plant enzymatic hydrolyzate described in this example is prepared according to the following steps: take 15kg of water chestnuts and 25kg of burdock and mix them, add equal weight of water to mix and make slurry at room temperature, and add 10wt of the total amount of the water chestnuts and burdock to the obtained slurry % pectinase and cellulase (mass ratio 1:1), carry out enzymolysis treatment at normal temperature; enzymatic hydrolyzate, and the obtained enzymolyzate is concentrated under reduced pressure ...

Embodiment 2

[0034] The raw materials for the preparation of the architectural waterproof coating described in this example include: 40kg of glutinous rice flour, 15kg of crop starch, 15kg of quartz powder, 10kg of diatom mud, 3kg of calcite powder, 3kg of polyglutamic acid, 15kg of polylactic acid fiber, [choline] L-glutamine 5kg, and plant hydrolyzate.

[0035] Wherein, the polylactic acid fiber is a fiber with a length of 0.1-0.5 mm and a diameter of less than 0.5 mm.

[0036] The plant enzymolyzate described in this example is prepared according to the following steps: take 25kg of water chestnuts and 15kg of burdock and mix them, add equal weight of water to mix and make slurry at room temperature, and add 15wt of the total amount of water chestnuts and burdock to the resulting slurry. % pectinase and cellulase (mass ratio 1:1), carry out enzymolysis treatment at normal temperature; enzymatic hydrolyzate, and the obtained enzymolyzate is concentrated under reduced pressure to 1 / 10 of...

Embodiment 3

[0039] The raw materials for the preparation of the architectural waterproof coating described in this example include: 35kg of glutinous rice flour, 18kg of crop starch, 12kg of quartz powder, 15kg of diatom mud, 2kg of calcite powder, 5kg of polyglutamic acid, 12kg of polylactic acid fiber, [choline] L-glutamine 8kg, and plant hydrolyzate.

[0040] Wherein, the polylactic acid fiber is a fiber with a length of 0.1-0.5 mm and a diameter of less than 0.5 mm.

[0041] The plant enzymatic hydrolyzate described in this example is prepared according to the following steps: Take 20kg of water chestnuts and 20kg of burdock and mix them, add equal weight of water to mix and make slurry at room temperature, and add 12wt of the total amount of water chestnuts and burdock to the obtained slurry % pectinase and cellulase (mass ratio 1:1), carry out enzymolysis treatment at normal temperature; enzymatic hydrolyzate, and the obtained enzymolyzate is concentrated under reduced pressure to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of building paint production, and particularly relates to building waterproof paint, and further discloses a preparation method of the building waterproofpaint. The building waterproof paint is prepared by using sticky rice powder and farm products as substrates, using quartz powder, calcite powder and diatom ooze as filling materials, and adding polyglutamic acid and polylactic acid fiber subjected to modification treatment. The bonding performance and the waterproof performance are further enhanced, so that the paint has the characteristics of good bonding performance, waterproof and dampproof effects, no peeling, no falling, non-toxicity, harmlessness and no pollution. Compared with the existing technical scheme, the paint has better waterproof performance.

Description

technical field [0001] The invention belongs to the technical field of architectural paint production, in particular relates to an architectural waterproof paint, and further discloses a preparation method thereof. Background technique [0002] With the improvement of people's living standards, the requirements for the living environment are also increasing, which has led to the rapid development of the construction and decoration industries. Traditional building interior wall coatings contain formaldehyde, which poses serious harm to people's health, and are gradually eliminated by the market. Non-toxic and environmentally friendly coatings have become people's first choice. After years of development, some interior wall paints have reached national standards and meet the requirements of non-toxic and harmless paints. However, these environmentally-friendly paints cannot be directly applied to the wall. Putty is used as the bottom layer. During the construction of the putt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D103/02C09D7/61C09D7/63C09D7/65D06M13/402C12P1/00D06M101/32
CPCC08K2003/265C08L2205/025C08L2205/035C08L2205/16C09D103/02C12P1/00C09D7/61C09D7/63C09D7/65C09D7/70D06M13/402D06M2101/32C08L3/02C08L77/04C08L67/04C08K3/36C08K7/26C08K3/26
Inventor 张可江刘美丽
Owner 德泰建设有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap