Environment-friendly low-cost bamboo mat manufacturing method

A low-cost, bamboo mat technology, applied in the field of bamboo mats, can solve the problems of a large number of chemical waste water, cumbersome bamboo silk substrate process, unfavorable environmental protection and other problems, and achieves the effects of good sterilization effect, enhanced toughness and long storage time.

Inactive Publication Date: 2018-10-12
施文杰
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing bamboo mat production method generally includes polishing the bamboo silk base material for making the bamboo mat, then soaking in hydrogen peroxide, cooking and bleaching, drying, then dyeing, and then weaving the bamboo mat. It is necessary to spray paint on the surface of the bamboo mat. Using this production method, the bamboo silk base material of the bamboo mat is made of cumbersome technology and high production cost. In addition, a large amount of chemical preparations need to be used in the production process, and a large amount of chemicals will be produced in the bleaching and dyeing process. waste water, which is not conducive to environmental protection, causing enterprises to spend more to treat waste water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of environmental protection low-cost bamboo mat preparation method that the present invention proposes comprises the following steps:

[0021] S1. Add cocoic acid monoethanolamide and water to the pretreated bamboo bundles, stir, add dropwise silver nitrate solution, stir after the addition is complete, use sodium hydroxide to adjust the pH of the system to 8.5-9.2, add citric acid solution, microcrystalline Paraffin wax and hydrogenated castor oil are sealed and heated, and in the state of passing through the air, potassium permanganate is added to stir, the temperature is cooled to room temperature, filtered, and washed to obtain the bamboo bundle compound;

[0022] S2. Add water and nano-montmorillonite to the bamboo bundle composite, stir, ultrasonically disperse, filter, and wash;

[0023] S3. Send the bamboo bundles into the drying and disinfection carbon dryer. The heating temperature of the drying and disinfection carbon dryer is 160°C, and the heating ti...

Embodiment 2

[0025] A kind of environmental protection low-cost bamboo mat preparation method that the present invention proposes comprises the following steps:

[0026] S1, 20 parts of pretreated bamboo bundles are added 2 parts of coconut oil monoethanolamide and 100 parts of water by weight and stirred for 4 hours, and 8 parts of silver nitrate solution with a concentration of 2wt% are added dropwise, and stirred for 30 minutes after the addition is complete. Sodium oxide adjusts the pH value of the system to 8.5-9.2, adding 4 parts of citric acid solution with a concentration of 10wt%, 2 parts of microcrystalline paraffin, and 4 parts of hydrogenated castor oil for airtight heating, and adding 2 parts of high manganese Potassium acid was stirred for 160min, cooled to room temperature, filtered, and washed to obtain the bamboo bundle compound;

[0027] S2. Add 100 parts of water and 8 parts of nano-montmorillonite to 40 parts of bamboo bundle composite by weight, stir for 20 minutes, ul...

Embodiment 3

[0030] A kind of environmental protection low-cost bamboo mat preparation method that the present invention proposes comprises the following steps:

[0031] S1, add 30 parts of pretreated bamboo bundles by weight to 1 part of coconut oil monoethanolamide, 100 parts of water and stir for 8 hours, add 4 parts of silver nitrate solution with a concentration of 4wt%, and stir for 20 minutes after the addition is complete. Sodium oxide adjusts the pH value of the system to 8.5-9.2, adding 6 parts of citric acid solution with a concentration of 5wt%, 4 parts of microcrystalline paraffin, and 2 parts of hydrogenated castor oil for airtight heating, and adding 4 parts of high manganese Potassium acid was stirred for 100min, cooled to room temperature, filtered, and washed to obtain the bamboo bundle compound;

[0032] The pretreated bamboo bundles are prepared by the following process: remove the branches and leaves from the original bamboo, decompose them into bamboo bundles, dry the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly low-cost bamboo mat manufacturing method. The manufacturing method comprises the following steps that S1, coconut oleic acid monoethanolamide and waterare added into a preprocessed bamboo bundle for stirring, a silver nitrate solution is dropwise added, stirring is carried out after dropwise adding, the pH value of a system is adjusted to be 8.5-9.2by using a sodium hydroxide, a citric acid solution, microcrystalline wax and hydrogenated castor oil are added so as to carry out closed heating, under the condition that air is introduced, potassium permanganate is added for stirring, the mixture is cooled to the room temperature, and filtering and washing are carried out to obtain a bamboo bundle compound; S2, water and nano montmorillonite are added into the bamboo bundle compound for stirring, and ultrasonic dispersion, filtering and washing are carried out; and S3, the bamboo bundle is fed into a drying and disinfecting carbon drying machine, the heating temperature of the drying and disinfecting carbon drying machine is 160-190 DEG C, the heating time is 2-4 hours, carbonatization is carried out on bamboo powder, the carbonizationdegree is 5%-30%, and then the environment-friendly low-cost bamboo mat is obtained through weaving.

Description

technical field [0001] The invention relates to the technical field of bamboo mats, in particular to an environment-friendly and low-cost bamboo mat preparation method. Background technique [0002] Bamboo mat has the advantages of low cost and good for human health, and is widely used in the outer packaging of cables. The existing bamboo mat production method generally includes polishing the bamboo silk base material for making the bamboo mat, then soaking in hydrogen peroxide, cooking and bleaching, drying, then dyeing, and then weaving the bamboo mat. It is necessary to spray paint on the surface of the bamboo mat. Using this production method, the bamboo silk base material of the bamboo mat is made of cumbersome technology and high production cost. In addition, a large amount of chemical preparations need to be used in the production process, and a large amount of chemicals will be produced in the bleaching and dyeing process. waste water, which is not conducive to envi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/08B27K3/52B27K9/00B27M1/06
CPCB27K3/08B27K3/52B27K9/002B27M1/06
Inventor 施文杰
Owner 施文杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap