Steel-iron surface detergent and preparation method thereof

A technology for steel surface and cleaning agent, applied in the field of cleaning agent processing, can solve the problems of low oil cleaning efficiency, affecting processing, corrosion of metals such as aluminum, etc. The effect of reducing cleaning costs

Inactive Publication Date: 2018-11-02
怀宁县恒源再生科技有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the various metal degreasing agents that are often used at present contain various toxic and harmful substances such as sodium nitrite, etc., which pollute the environment and cause harm to the operator's body. Process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A steel surface cleaning agent, said cleaning agent is made of the following raw materials in parts by weight: 20 parts of sodium fatty acid methyl ester sulfonate, 10 parts of alkylphenol polyoxyethylene ether, 12 parts of sulfobetaine, triethanolamine oleate 2 parts, 4 parts of sodium carbonate, 2 parts of silicone, 2 parts of defoamer, 4 parts of rust inhibitor, 1 part of dispersant, 0.5 part of corrosion inhibitor, 80 parts of deionized water.

[0024] The defoamer is a mixture of polyoxyethylene polyoxypropanolamine ether, emulsified silicone oil and polydimethylsiloxane in a mass ratio of 1:1:2; the rust inhibitor is triethanolamine, sodium tetraborate and glucose The mass ratio of sodium acid sodium is a mixture of 3:1:1; the dispersant is any one or a combination of sodium lauryl sulfate, methyl amyl alcohol, cellulose derivatives and polyacrylamide; the The corrosion inhibitor is a mixture of tolutriazole and mercaptobenzothiazole in a mass ratio of 2:1.

[00...

Embodiment 2

[0030] A steel surface cleaning agent, said cleaning agent is made of the following raw materials in parts by weight: 30 parts of sodium fatty acid methyl ester sulfonate, 14 parts of alkylphenol polyoxyethylene ether, 16 parts of sulfobetaine, triethanolamine oleate 6 parts, 6 parts of sodium carbonate, 3 parts of silicone, 4 parts of defoamer, 6 parts of rust inhibitor, 3 parts of dispersant, 0.8 part of corrosion inhibitor, 100 parts of deionized water.

[0031] The defoamer is a mixture of polyoxyethylene polyoxypropanolamine ether, emulsified silicone oil and polydimethylsiloxane in a mass ratio of 1:1:2; the rust inhibitor is triethanolamine, sodium tetraborate and glucose The mass ratio of sodium acid sodium is a mixture of 3:1:1; the dispersant is any one or a combination of sodium lauryl sulfate, methyl amyl alcohol, cellulose derivatives and polyacrylamide; the The corrosion inhibitor is a mixture of tolutriazole and mercaptobenzothiazole in a mass ratio of 2:1.

[...

Embodiment 3

[0037] A steel surface cleaning agent, said cleaning agent is made of the following raw materials in parts by weight: 25 parts of sodium fatty acid methyl ester sulfonate, 12 parts of alkylphenol polyoxyethylene ether, 14 parts of sulfobetaine, triethanolamine oleate 4 parts, 5 parts of sodium carbonate, 2.5 parts of organic silicon, 3 parts of defoamer, 5 parts of rust inhibitor, 2 parts of dispersant, 0.7 parts of corrosion inhibitor, 90 parts of deionized water.

[0038] The defoamer is a mixture of polyoxyethylene polyoxypropanolamine ether, emulsified silicone oil and polydimethylsiloxane in a mass ratio of 1:1:2; the rust inhibitor is triethanolamine, sodium tetraborate and glucose The mass ratio of sodium acid sodium is a mixture of 3:1:1; the dispersant is any one or a combination of sodium lauryl sulfate, methyl amyl alcohol, cellulose derivatives and polyacrylamide; the The corrosion inhibitor is a mixture of tolutriazole and mercaptobenzothiazole in a mass ratio of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a steel-iron surface detergent and a preparation method thereof, which relates to the technical field of processing of detergents. The detergent is prepared from the followingraw materials in parts by weight: 20 to 30 parts of methyl ester sulfonate, 10 to 14 parts of alkylphenol polyoxyethylene, 12 to 16 parts of sulphobetaine, 2 to 6 parts of triethanolamine oleate, 4 to 6 parts of sodium carbonate, 2 to 3 parts of organic silicon, 2 to 4 parts of defoaming agent, 4 to 6 parts of antirust agent, 1 to 3 parts of dispersing agent, 0.5 to 0.8 part of corrosion inhibiter, and 80 to 100 parts of deionized water. By adopting the steel-iron surface detergent and the preparation method thereof, the weaknesses of the prior art can be overcome, the cleaning effect of thetraditional metal detergent for a steel-iron material can be improved, while the surface oil contaminant of the steel and iron is effectively removed, a long-acting antifouling effect can be achieved,and the steel-iron surface detergent also has the advantages of low cost, convenience in production, safety in use, no environmental pollution and the like.

Description

technical field [0001] The invention relates to the technical field of cleaning agent processing, in particular to a steel surface cleaning agent and a preparation method thereof. Background technique [0002] Steel products are often used in the process of processing, storage and transportation, which are based on mineral or animal and vegetable oils, plus various organic additives or inorganic substances. This is the main source of oil pollution on the steel surface. The existence of oil pollution will affect pickling. The quality of rust removal and phosphating affects the drying performance of the coating and reduces the adhesion of the coating. Therefore, the equipment must be cleaned on the surface of steel parts before use. Steel equipment used in the fields of organic chemical and food production will also generate oil stains on the surface. If it is not cleaned, it will affect product quality. [0003] Steel cleaning agents belong to metal cleaning agents. Metal c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/18C23G1/19
CPCC23G1/18C23G1/19
Inventor 樊双七
Owner 怀宁县恒源再生科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap