Technology for preparing baking-free bricks with iron tailings, secondary aluminum ash and acid leaching magnesium residues
A technology of aluminum ash slag and unburned bricks, which is applied in the manufacture of rayon, single-component polyolefin rayon, and fiber chemical characteristics, can solve the problems of unfavorable fiber concrete collective interface, poor concrete dispersion, and difficult mixing. Achieve good mechanical properties and hydrophilic properties, reduce the amount of cement, and good alkali resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1
[0023] A process for preparing non-burning bricks by utilizing iron tailings-secondary aluminum ash slag-acid-leaching manganese slag, characterized in that, comprising the following steps:
[0024] (1) Melt blending modification of polypropylene fibers:
[0025] Add 0.006 part of stearic acid to 0.3 part of ground calcium carbonate, and after wet activation at 85-95 ° C for 45min, dry and grind it; blend it with 1 part of polypropylene fiber and 0.1 part of polyethylene glycol , using a 180-200 ℃ twin-screw extruder for blending and granulation, drying the blended pellets at 104-106 ℃, and using a melt spinning machine to grow filaments to obtain modified polypropylene fibers;
[0026] (2) Pretreatment of secondary aluminum ash slag of raw materials:
[0027] Put 155 parts of secondary aluminum slag into a 120-125 ℃ electric heating blast drying oven to dry for 3 hours, cool naturally, take it out, and grind it with a ball mill to obtain secondary aluminu...
Example Embodiment
[0034] Example 2
[0035] A process for preparing non-burning bricks by utilizing iron tailings-secondary aluminum ash slag-acid-leaching manganese slag, characterized in that, comprising the following steps:
[0036] (1) Melt blending modification of polypropylene fibers:
[0037] Add 0.012 parts of stearic acid to 0.6 parts of heavy calcium carbonate, and after wet activation at 85-95 ° C for 55 minutes, dry and grind it; blend it with 2 parts of polypropylene fibers and 0.2 parts of polyethylene glycol , using a 180-200 ℃ twin-screw extruder for blending and granulation, drying the blended pellets at 104-106 ℃, and using a melt spinning machine to grow filaments to obtain modified polypropylene fibers;
[0038] (2) Pretreatment of secondary aluminum ash slag of raw materials:
[0039] Put 165 parts of secondary aluminum ash slag into a 120-125 ℃ electric heating blast drying oven to dry for 4 hours, cool naturally, take it out, and grind it with a ball mill to obtain seco...
PUM
Property | Measurement | Unit |
---|---|---|
Compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap