A kind of colored polymer conductive beads and preparation method thereof

A polymer bead and polymer technology, applied in the field of colored polymer conductive beads and their preparation, can solve the problems of poor light fastness, complicated process, poor compatibility with polymers, etc., and achieve good conductive effect and color , Simple process, good compatibility effect

Active Publication Date: 2021-05-28
WUHAN POLYTECHNIC UNIVERSITY
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the above-mentioned existing reports, the first type is to introduce organic dyes by suspension polymerization, but organic dyes are easily soluble in organic solvents, flammable and will decompose when exposed to sunlight. Therefore, organic dyes have poor weather resistance, poor solvent resistance, and poor light fastness And flammable, seriously affect the performance of colored expandable polystyrene beads
The second category is inorganic pigments, which need to be hydrophobically modified and then introduced into the suspension polymerization system. The introduction of inorganic pigments will reduce the mechanical properties to a certain extent
The third category is the use of melt blending technology, which needs to add a variety of additives and additives. The process is complicated. The added conductive additive is inorganic and has poor compatibility with polymers. It can only be achieved when the amount of conductive additive added is large. Inhibit the effect of static electricity, and at the same time greatly reduce the mechanical properties of polymers
[0006] To sum up, the existing reported patents and literature do not solve the problem of dual functions of color and static electricity suppression at the same time, and the existing reports all use inorganic pigments and organic pigments, and do not use the intrinsic color of conductive polymers to solve the problem of polymerization at the same time. Reports on the color of the beads and the suppression of static electricity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of colored polymer conductive beads and preparation method thereof
  • A kind of colored polymer conductive beads and preparation method thereof
  • A kind of colored polymer conductive beads and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] 1) Preparation of conductive polymer seed solution

[0048] Dissolve polyaniline in dimethyl sulfoxide to prepare 0.5 mg / mL polyaniline seed solution.

[0049] 2) Confinement and controllable swelling pretreatment of polymer beads

[0050] Weigh 15 g of polystyrene beads and disperse them in 25 mL of polystyrene beads in a mixed solvent of chloroform / ethanol (the volume ratio of chloroform and ethanol is 1:4), mechanically stir for 1 min, and the rotating speed is 40 rpm. Liquid separation to obtain pretreated polystyrene beads.

[0051] 3) Synthesis of colored polymer conductive beads

[0052] Add 20 mL of 0.5 mol / L aqueous hydrochloric acid solution, 3 mmol of aniline monomer and 0.5 mL of 0.5 mg / mL polyaniline seed solution into the reaction flask, then add 15 g of the pretreated polystyrene beads obtained in step 2) to the above system , keep the stirring speed at 60rpm, absorb for 6min, add dropwise an initiator solution consisting of 3mmol ammonium persulfate a...

Embodiment 2

[0054] 1) Preparation of conductive polymer seed solution

[0055] Dissolve polypyrrole in dimethyl sulfoxide to prepare 1 mg / mL polypyrrole seed solution.

[0056] 2) Confinement and controllable swelling pretreatment of polymer beads

[0057] Weigh 20 g of polymethyl methacrylate beads and disperse them in the mixed solvent of dichloromethane / methanol (the volume ratio of dichloromethane and methanol is 1:6) of 30 mL of polymethyl methacrylate beads, mechanically stir for 2 min , with a rotating speed of 50 rpm, and solid-liquid separation to obtain pretreated polymethyl methacrylate beads.

[0058] 3) Synthesis of colored polymer conductive beads

[0059] Add 25 mL of 0.8 mol / L phosphoric acid aqueous solution, 5 mmol of pyrrole monomer and 1 mL of 1 mg / mL polypyrrole seed solution to the reaction flask, then add 20 g of the pretreated polymethyl methacrylate beads obtained in step 2) to the above system In the process, keep the stirring speed at 80rpm, absorb for 12min,...

Embodiment 3

[0061] 1) Preparation of conductive polymer seed solution

[0062] Dissolve polyaniline in dimethyl sulfoxide to prepare 1.2 mg / mL polyaniline seed solution.

[0063] 2) Confinement and controllable swelling pretreatment of polymer beads

[0064] Weigh 25g of expandable polystyrene beads and disperse them in the mixed solvent of toluene / propanol of 40mL of polymer beads (the volume ratio of toluene to propanol is 1:8), mechanically stir for 4min, the rotating speed is 60rpm, solid Liquid separation to obtain pretreated expandable polystyrene beads.

[0065] 3) Synthesis of colored polymer conductive beads

[0066] Add 30mL of 1mol / L perchloric acid aqueous solution, 8mmol aniline monomer and 1mL of 1.2mg / mL polyaniline seed solution to the reaction bottle, then, add 25g of pretreated expandable polystyrene beads obtained in step 2) In the above system, keep the stirring speed at 90rpm, absorb for 15min, add dropwise the initiator solution composed of 8mmol ammonium persulfa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a colored polymer conductive bead and a preparation method thereof. The preparation method comprises: 1) preparation of conductive polymer seed liquid; 2) confinement and controllable swelling pretreatment of polymer beads; 3) synthesis of colored polymer conductive beads. The present invention can realize the limited and controllable swelling of the surface layer of the polymer beads through the pretreatment process of the limited and controllable swelling of the polymer beads, and then control the synthesis process factors of the colored polymer conductive beads to obtain a series of different Conductive properties and colored conductive polymer beads in different colors. The conductive polymer has good compatibility with the polymer beads, and the lower content of the conductive polymer can endow the polymer beads with better conductive effect and color without destroying the internal structure of the polymer beads. The polymer beads still maintain the foaming properties of the polymer beads.

Description

technical field [0001] The invention belongs to the field of colored polymer conductive beads, and more specifically relates to a colored polymer conductive bead and a preparation method thereof. Background technique [0002] Polymer beads such as polystyrene, polymethyl methacrylate, expandable polystyrene and expandable polymethyl methacrylate are widely used in the fields of building materials, packaging, decoration and handicrafts. Common polymer beads are white, but some applications require colored polymer beads. Therefore, a large number of research reports on colored polymer beads have been derived. The Chinese invention patent application with publication number CN 102875713A discloses a color expandable polystyrene resin and a method for preparing color expandable polystyrene resin in one step. The patent application adds organic dyes to styrene monomers , the color expandable polystyrene resin is prepared by one-step suspension polymerization method. In addition...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/06C08L79/02C08L33/12C08L79/04C08L25/14C08G73/02C08G73/06
CPCC08G73/0266C08G73/0611C08L25/06C08L25/14C08L33/12C08L79/02C08L79/04
Inventor 闫俊涛冯港英夏佳慧吉茂林王春蕾李建芬柴波范国枝
Owner WUHAN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com