Method for preparing stretchable bending-resistant PVC hose
A bending-resistant and flexible hose technology, applied in the field of PVC material preparation, can solve the problems of poor stretchability of PVC hose, easy whitening of break points, poor dispersion of PVC, etc., to improve low-temperature flexibility and phase Capacitance, the effect of improving stretch elasticity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1
[0025] Take the basalt and put it into a grinder and pulverize it for 3 hours to obtain basalt abrasive. Place the basalt abrasive in a corundum crucible with a leaking nozzle, the diameter of which is 8 mm, and move the corundum crucible into a resistance furnace. Power on and heat up to 1350°C, heat and melt for 20 minutes to obtain molten basalt material, open the leaking nozzle, and use a traction rod to draw the molten basalt material to obtain basalt fibers with a diameter of 6 mm; take 200 mL of ethyl orthosilicate and 300 mL of anhydrous ethanol and mix them. Put it into a beaker, add 60 mL of hydrochloric acid with a mass fraction of 10% to the beaker, and stir it with a magnetic stirrer at a speed of 400 r / min for 1 h to obtain a silica sol, and add 20 mL of a mass fraction of 5% to the silica sol. The polyvinyl alcohol was aged at room temperature for 20 hours to obtain a silica sol precursor. The basalt fiber was immersed in the silica precursor ...
Example Embodiment
[0026] Example 2
[0027] Take the basalt and put it into a grinder for 3.5 hours to get basalt abrasive, put the basalt abrasive in a corundum crucible with a leaking nozzle, the diameter of the leaking nozzle is 9mm, move the corundum crucible into a resistance furnace, and heat up the basalt at a heating rate of 22°C / min. , energize and heat up to 1370 ° C, heat and melt for 22 minutes to obtain basalt molten material, open the leak nozzle, and use a traction rod to pull the drawing basalt molten material to obtain basalt fibers with a diameter of 7 mm; take 210 mL of ethyl orthosilicate and 320 mL of anhydrous ethanol mixed Put it into a beaker, add 70 mL of hydrochloric acid with a mass fraction of 10% to the beaker, and stir it with a magnetic stirrer at a speed of 420 r / min for 1.5 h to obtain a silica sol. Add 25 mL of the mass fraction to the silica sol. 5% polyvinyl alcohol, aged for 22h at room temperature to obtain a silica sol precursor, immersed the basalt fiber ...
Example Embodiment
[0028] Example 3
[0029] Take the basalt and put it in a grinder and pulverize it for 4 hours to obtain basalt abrasive. Place the basalt abrasive in a corundum crucible with a leaking nozzle, the diameter of which is 10 mm, and move the corundum crucible into a resistance furnace. Power on and heat up to 1400°C, heat and melt for 25 minutes to obtain molten basalt material, open the leaking nozzle, and draw the molten basalt material with a traction rod to obtain a basalt fiber with a diameter of 8 mm; take 220 mL of ethyl orthosilicate and 350 mL of anhydrous ethanol and mix it with Put it into a beaker, add 80 mL of hydrochloric acid with a mass fraction of 10% to the beaker, and stir it with a magnetic stirrer at a speed of 450 r / min for 2 hours to obtain a silica sol, and add 30 mL of a mass fraction of 5% to the silica sol. The polyvinyl alcohol was aged at room temperature for 24h to obtain a silica sol precursor. The basalt fiber was immersed in the silica precursor t...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap