A waterborne carbon fiber sizing agent and a preparing method thereof

A carbon fiber, hydrophilic emulsifier technology, applied in the direction of carbon fiber, fiber treatment, improved hand fiber, etc., can solve the problems of epoxy resin emulsion performance limitation, long synthesis cycle, high production equipment requirements, etc.

Active Publication Date: 2019-02-26
ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The carbon fiber sizing agent prepared by the chemical synthesis method has the advantages of high storage stability and excellent performance; the disadvantages are: the synthesis cycle is long, the requirements for production equipment are high, and the reaction process requires the u

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A waterborne carbon fiber sizing agent and a preparing method thereof
  • A waterborne carbon fiber sizing agent and a preparing method thereof
  • A waterborne carbon fiber sizing agent and a preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0078] According to a typical embodiment of the present invention, a water-based carbon fiber sizing agent is provided. This water-based carbon fiber sizing agent is made of the following components by weight:

[0079]

[0080] The water-based carbon fiber sizing agent of the present invention is a water-based carbon fiber sizing agent combined by heat curing and light curing. The carbon fiber after the sizing can be dried by high-temperature heat drying, and then cured by light curing, so that the carbon fiber The performance of the sizing agent is further improved; the combination of thermal curing and light curing provided by the present invention improves the production efficiency of the carbon fiber sizing agent, enhances the clustering of the fiber bundles, and is not easy to shed crumbs during the weaving process, and can be combined with the ring Perfect combination with epoxy resin prepreg.

[0081] Preferably, the epoxy resin is added in an amount of 22 to 30 par...

Embodiment 1

[0121] The carbon fiber sizing agent of this embodiment is made by the following components (table 4) by weight after curing and photocuring:

[0122] Table 4

[0123]

[0124]

[0125] The preparation method is as follows:

[0126]Add 24 parts of 0161 (E-54) (Bluestar Nantong Xingchen Synthetic Materials), 6 parts of 1703 (Double Bond Chemical Co., Ltd.), and 1 part of propylene glycol methyl ether solvent into a mixing bucket with a condenser. Raise the temperature to 80°C, stir and disperse for 1 hour, and the stirring speed is 800r / min, so that the epoxy resin is mixed evenly. Then, under the condition of uniform stirring, slowly add 8 parts of BOM-25 into the above epoxy resin system to make it uniformly dispersed in the epoxy resin, stirring time is 1 hour, stirring speed is 1000r / min. Then, lower the temperature to 70°C, add 0.35 parts of wetting and dispersing agent ANTI-TERRA-250 to make it evenly dispersed in the system. Then, lower the temperature to 65° C....

Embodiment 2

[0128] The carbon fiber sizing agent of this embodiment is made by the following components (Table 5) by weight after curing and photocuring:

[0129] table 5

[0130]

[0131]

[0132] The preparation method is as follows:

[0133] Add 24 parts of WSR618 (E-51) (Bluestar Nantong Xingchen Synthetic Materials) and 0.7 parts of oleic acid amide into a mixing tank with a condenser, raise the temperature to 150°C, stir for 1 hour, and the stirring speed is 600r / min . Reduce the temperature of the system to 80°C, add 4 parts of 1636 (Double Bond Chemical Co., Ltd.) and 1 part of propylene glycol methyl ether solvent, stir and disperse for 1 hour, and the stirring speed is 800r / min, so that the epoxy resin is mixed evenly. Then, lower the temperature to 70°C, and slowly add 8.65 parts of BOM-25 to the above epoxy resin system under uniform stirring to make it evenly dispersed in the epoxy resin. The stirring time is 1 hour and the stirring speed is 1000r / min. . Then, lower...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A waterborne carbon fiber sizing agent and a preparing method thereof are disclosed. The sizing agent is prepared from, by weight, 16-32 parts of epoxy resin, 4-8 parts of epoxy acrylate, 2-15 parts of a hydrophilic emulsifier, 0-20 parts of aqueous polyurethane emulsion, 0-10 parts of aqueous urethane acrylate, 0-5 parts of higher fatty acid amide, 0.01-3 parts of a photoinitiator, 0.05-5 parts of an aqueous wetting and dispersing agent, 0.1-5 parts of a thickening agent, 0.2-5 parts of a solvent and 30-70 parts of deionized water. The sizing agent is a waterborne carbon fiber sizing agent combining heat-curing and photo-curing. Carbon fibers sized by the sizing agent can be dried through a high-temperature drying manner and then cured through a photo-curing manner so that the performanceof the sizing agent is further improved.

Description

technical field [0001] The invention relates to the technical field of carbon fiber sizing agents, in particular to a water-based carbon fiber sizing agent and a preparation method thereof. Background technique [0002] At present, sizing agents play an extremely important role in the application of high-performance carbon fiber and fiber-reinforced resin composites. After sizing treatment on the surface of carbon fiber, it can improve the properties of carbon fiber such as clustering, smoothness, wear resistance and processability, and meet the requirements of carbon fiber in subsequent manufacturing processes such as weaving and processing. [0003] The sizing agents used in the existing market are mainly divided into two categories: oily sizing agents and water-based sizing agents. As the country's requirements for environmental protection are getting higher and higher, the proportion of water-based sizing agents in the market is getting higher and higher. The water-bas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/55D06M13/224D06M15/564D06M13/402D06M101/40
CPCD06M13/2246D06M13/402D06M15/55D06M15/564D06M2101/40D06M2200/50
Inventor 王友东王海龙丁清华
Owner ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap