Double-component diatom ooze water-based paint with zero VOC (Volatile Organic Compound) emission

A muddy water-based, two-component technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problems of reducing the performance of diatom mud and unreasonable material matching

Active Publication Date: 2019-03-08
刘鹏
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is used to replace wallpaper and latex paint, and is suitable for interior wall decoration of villas, apartments, hotels, homes, hospitals, etc. However, the materials used in diatom mud produced by many manufacturers are extremely unreasonable, and the surface area of ​​diatom earth is sealed. The performance of diatom mud is greatly reduced, and a more reasonable formula system is needed to develop diatom mud coatings, so as to provide people with better decorative materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-component diatom ooze water-based paint with zero VOC (Volatile Organic Compound) emission
  • Double-component diatom ooze water-based paint with zero VOC (Volatile Organic Compound) emission

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of far-infrared ceramic powder X is prepared by the following method:

[0028] (1) Preparation of mixture granules: in parts by weight, 9 parts of scandium oxide (800 orders), 6 parts of silicon dioxide (800 orders), 9 parts of aluminum oxide (800 orders), 14 parts of cerium oxide ( 800 mesh), 70 parts of water are added to the ball milling equipment for ball milling for 6 hours, then the discharge is added, sprayed and granulated, and the particle diameter is 20 mesh, and the granules with a water content of 8% are obtained;

[0029] (2) Sintering: under the pressure of 30MPa, the pellets in step (1) are pressed into plates by dry pressing, and then in a tubular kiln, a weak reducing atmosphere (90% volume fraction of N 2 with a volume fraction of 10% H 2 Uniform gas mixture), calcined at 1500°C for 5h, and then cooled to room temperature to obtain a dense plate;

[0030] (3) Crushing: The dense version was crushed, milled with zirconium beads for 48 hours, an...

Embodiment 2

[0032] A kind of far-infrared ceramic powder Y is prepared by the following method:

[0033] (1) Preparation of mixture granules: In parts by weight, 6 parts of transition metal oxide, 8 parts of silicon dioxide (800 mesh), 9 parts of alumina (800 mesh), 11 parts of cerium oxide (800 mesh) ), 60 parts of water were added to the ball milling equipment for ball milling for 5h, then the discharge was added, sprayed and granulated to obtain granules with a particle diameter of 20 mesh and a water content of 12%;

[0034] (2) Sintering: under the pressure of 30MPa, the pellets in step (1) are pressed into plates by dry pressing, and then in a tubular kiln, a weak reducing atmosphere (90% volume fraction of N 2 with a volume fraction of 10% H 2 Uniform gas mixture), calcined at 1400°C for 8 hours, and then cooled to room temperature to obtain a dense plate;

[0035] (3) Crushing: The dense plate was crushed, milled with zirconium beads for 48 hours, and passed through a 1200-mesh ...

Embodiment 3

[0037] A kind of far-infrared ceramic powder Z is prepared by the following method:

[0038] (1) Preparation of mixture granules: in parts by weight, 5 parts of scandium oxide (800 mesh), 5 parts of silicon dioxide (800 mesh), 5 parts of aluminum oxide (800 mesh), 10 parts of cerium oxide ( 800 mesh), 50 parts of water are added to the ball milling equipment for ball milling for 4h, then the discharge is added, sprayed and granulated, and the particle diameter is 20 mesh, and the granules with a water content of 8% are obtained;

[0039] (2) Sintering: under the pressure of 30MPa, the pellets in step (1) are pressed into plates by dry pressing, and then in a tubular kiln, a weak reducing atmosphere (90% volume fraction of N 2 with a volume fraction of 10% H 2 Uniform gas mixture), calcined at 1400°C for 5h, and then cooled to room temperature to obtain a dense plate;

[0040] (3) Crushing: the dense version was crushed, milled with zirconium beads for 48 hours, and passed th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to a double-component diatom ooze water-based paint with zero VOC (Volatile Organic Compound) emission, which is characterized by being formed by components A and B in parts by weight, wherein the component A comprises 0.5 to 1 part of potassium persulfate, 30 to 40 parts of diatom ooze powder, 10 to 15 parts of rutile type titanium dioxide, 6 to 12 parts of far-infrared ceramic powder; 45 to 75 parts of water, 1 to 2 parts of a leveling agent and 0.3 to 0.6 part of a defoaming agent; and the component B comprises 6 to 12 parts of crosslinkable monomer, 2 to 4 parts of antibacterial monomer, 0.1 to 0.3 part of a catalyst, 3 to 5 parts of water-based stearate and 15 to 25 parts of water. The double-component diatom ooze water-based paint has excellent antibacterial andair purification effects and wide application prospect.

Description

technical field [0001] The invention belongs to the technical field of architectural coatings, and relates to a two-component diatom mud water-based coating with zero VOC emission. Background technique [0002] With the rapid development of the national economy and the gradual improvement of people's material living standards, interior decoration has become increasingly popular. People spend two-thirds of their life indoors, and modern people spend 80%-90% of their time indoors living and working in an indoor environment. Therefore, the quality of the indoor environment directly affects people's health. [0003] Diatom mud is a kind of dry powder interior wall decoration coating material prepared with inorganic gelling substance as the main bonding material and diatom material as the main functional filler. It has the functions of eliminating formaldehyde, purifying air, adjusting humidity, releasing negative oxygen ions, fire retardant, wall self-cleaning, sterilization an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/14C09D7/61C09D7/63C09D7/65
CPCC09D7/63C09D7/65C09D7/70C09D1/00C09D5/14C09D7/61
Inventor 不公告发明人
Owner 刘鹏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap