Environment-friendly porcelain film coating used for outer wall

A ceramic film coating and environmental protection technology, applied in fire-resistant coatings, antifouling/underwater coatings, coatings, etc., can solve the problems of water resistance, weather resistance, antifouling resistance, antibacterial and mildew resistance, etc., and achieve low cost and preparation technology. Simple and effective results

Inactive Publication Date: 2019-03-08
常州天瑞新材料科技有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the shortcomings of poor water resistance, weather resistance, stain resistance and antibacterial and mildew resistance in the prior art, and propose an environmentally friendly porcelain film coating for exterior walls

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The invention discloses an environmentally friendly porcelain film coating for exterior walls, which is prepared from the following components according to the mass percentage: 44% of silica sol dispersion liquid, 3% of filler, 35% of silane coupling agent, 10% of pigment, leveling 0.5% agent, 2% weather resistance agent, 2% antibacterial agent, 1% ultraviolet absorber, 1.5% polydimethyl hydroxy silicone oil, 1% organic acid catalyst.

[0031] The silica sol dispersion is prepared by mixing silica sol with large particle size and silica sol with small particle size at a mass ratio of 3:1.

[0032] The filler is basalt short fiber.

[0033] The pigment is iron manganese black, and the leveling agent is a hydrophilic polyether modified silicone leveling agent.

[0034] The weather resistance agent adopts polybenzimidazole.

[0035] Described antibacterial agent adopts silver chloride.

[0036] The ultraviolet absorber is formed by mixing benzotriazole-4-sulfonic acid a...

Embodiment 2

[0045] The invention discloses an environmentally friendly porcelain film coating for exterior walls, which is prepared from the following components according to the mass percentage: 45% of silica sol dispersion liquid, 4% of filler, 30% of silane coupling agent, 15% of pigment, leveling 1% antibacterial agent, 1% weather resistance agent, 1% antibacterial agent, 1.5% ultraviolet absorber, 1% polydimethyl hydroxy silicone oil, and 0.5% organic acid catalyst.

[0046] The silica sol dispersion is prepared by mixing silica sol with large particle size and silica sol with small particle size at a mass ratio of 2:1.

[0047] The filler is precipitated barium sulfate.

[0048] The pigment is iron manganese black, and the leveling agent is a hydrophilic polyether modified silicone leveling agent.

[0049] The weather resistance agent adopts polybenzimidazole.

[0050] The antibacterial agent adopts silver tungstate.

[0051] The ultraviolet absorber is formed by mixing benzotria...

Embodiment 3

[0060]The invention discloses an environmentally friendly porcelain film coating for exterior walls, which is prepared from the following components according to the mass percentage: 50% of silica sol dispersion liquid, 1% of filler, 35% of silane coupling agent, 5% of pigment, leveling 0.1% antibacterial agent, 1.9% weather resistance agent, 2% antibacterial agent, 1.5% ultraviolet absorber, 1.5% polydimethyl hydroxy silicone oil, and 2% organic acid catalyst.

[0061] The silica sol dispersion is prepared by mixing silica sol with large particle size and silica sol with small particle size at a mass ratio of 4:1.

[0062] The filler is mica powder.

[0063] The pigment is iron manganese black, and the leveling agent is a hydrophilic polyether modified silicone leveling agent.

[0064] The weather resistance agent adopts polybenzimidazole.

[0065] Described antibacterial agent adopts zinc carbonate.

[0066] The ultraviolet absorber is formed by mixing benzotriazole-4-sul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly porcelain film coating used for an outer wall. The environment-friendly porcelain film coating is prepared from the following ingredients by weight percentage: 40-50% of silica sol dispersion, 1-4% of filters, 30-40% of a silane coupling agent, 5-15% of pigment, 0.1-1% of a leveling agent, 1-3% of a weather proofing agent, 1-3% of an antibacterial agent, 0.5-1.5% of an ultraviolet light absorber, 1-3% of poly-dimethyl hydroxyl silicone oil and 0.5-2% of an organic acid catalyst. A preparation method of the coating comprises the following steps: weighing raw materials for standby use; adding the fillers and the pigment into the silica sol dispersion and dispersing the fillers and the pigment; adding the weather proofing agent, the antibacterial agent, the ultraviolet light absorber and the organic acid catalyst and dispersing the weather proofing agent, the antibacterial agent, the ultraviolet light absorber and the organic acid catalyst; adding the silane coupling agent, the leveling agent and the poly-dimethyl hydroxyl silicone oil and uniformly dispersing the silane coupling agent, the leveling agent and the poly-dimethyl hydroxyl silicone oil, so as to obtain a product. The environment-friendly porcelain film coating product used for the outer wall, which is prepared from the matched materials has the advantages of being excellentin water resistance, weather resistance, soiling resistance, antibacterial property and better in effect; in addition, the preparation process is simpler in and is lower in cost.

Description

technical field [0001] The invention relates to the technical field of porcelain film coatings, in particular to an environment-friendly porcelain film coating for exterior walls. Background technique [0002] Paint is a material that can be coated on the surface of an object by different construction techniques to form a solid film with firm adhesion, certain strength, and continuity. . [0003] Membrane coating is a kind of coating, because of its excellent performance, it has been widely used in recent years. However, the existing porcelain coatings generally have the defects of poor water resistance, weather resistance, stain resistance and antibacterial and mildew resistance. effective improvement. [0004] Chinese Patent Announcement No. CN201510332612.5 relates to a ceramic film paint that can be sprayed at room temperature, which belongs to the technical field of porcelain film paint. Its raw material composition is: composed of A component, B component, C componen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/16C09D5/18C09D5/14C09D7/61C09D7/63C09D7/65
CPCC09D1/00C09D5/14C09D5/1687C09D5/18
Inventor 邓科洹孙大东
Owner 常州天瑞新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com