Composite cement using carbide slag and fly ash as admixture

A technology for composite cement and fly ash, applied in the field of composite cement, can solve the problems of high fuel consumption and heat consumption, complex production process, increase production cost, etc., and achieve the effects of reducing heat consumption, simple production process and speeding up

Inactive Publication Date: 2019-04-02
FUZHOU UNIV
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, some people have carried out research on the use of calcium carbide slag as raw material and high-temperature calcination to prepare cement, but the production process is complicated, the fuel consumption and heat consumption are high, and the exhaust gas emission is large, which increases the production cost.
[0005] Fly ash refers to the material that is discharged from the flue and collected by the dust collector after the pulverized coal is burned in the boiler in the coal-fired power plant. It is one of the by-products of coal combustion with the largest emission in my country at present. 7000cm 2 / g, the main component is SiO 2 , Al 2 o 3 and Fe 2 o 3 , it is a typical pozzolanic material with potential activity. Fly ash is used as cement and concrete admixture in the production of cement, sintered bricks and other new building materials, as well as in the fields of civil engineering, water conservancy and marine engineering. The main way to utilize external fly ash, so far there is no report on the use of calcium carbide slag and fly ash as admixture materials to prepare composite cement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Using calcium carbide slag and fly ash as a mixture to prepare composite cement, the raw material formula is: 5% dry carbide slag, 20% fly ash, 10% slag, 60% Portland cement clinker, and 5% gypsum. .

[0024] Preparation steps:

[0025] 1) The calcium carbide slag is dried by drying equipment and crushed. After drying, the moisture content is less than 1wt%, and the particle size after crushing is less than 25mm.

[0026] 2) Weigh dry calcium carbide slag, fly ash, Portland cement clinker, slag, and gypsum according to the above formula, and add them to the mill to grind together until the cement fineness is 80 μm and the sieve residue < 10%. Composite cement is prepared.

[0027] 3) Determine the compressive strength and flexural strength of composite cement product samples at different hydration ages according to the national standard GB / T17671-1999, and determine the setting time and stability of composite cement product samples according to the national standard G...

Embodiment 2

[0029] Using calcium carbide slag and fly ash as a mixture to prepare composite cement, the raw material formula is: 10% dry carbide slag, 20% fly ash, 10% slag, 55% Portland cement clinker, and 5% gypsum. .

[0030] Preparation steps:

[0031] 1) The calcium carbide slag is dried by drying equipment and crushed. After drying, the moisture content is less than 1wt%, and the particle size after crushing is less than 25mm.

[0032] 2) Weigh dry calcium carbide slag, fly ash, Portland cement clinker, slag, and gypsum according to the above formula, and add them to the mill to grind together until the cement fineness is 80 μm and the sieve residue < 10%. Composite cement is prepared.

[0033] 3) Determine the compressive strength and flexural strength of composite cement product samples at different hydration ages according to the national standard GB / T17671-1999, and determine the setting time and stability of composite cement product samples according to the national standard ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a composite cement using carbide slag and fly ash as admixture, wherein the composite cement comprises the following raw materials in percentage by weight: 5-10% of dry carbideslag, 20% of fly ash, 10% of mineral slag, 55-60% of portland cement clinker and 5% of gypsum, and the sum of the weight percentage of each component is 100 percent. At first, that carbide slag is dried and crushed, then the dry carbide slag, the fly ash, the portland cement clinker, the mineral slag and the gypsum are weighed according to the formula, and the composite cement can be prepared by sequentially adding the raw materials into a mill and grinding together. As that carbide slag and the fly ash are used as admixtures to prepare the composite cement, the waste is changed into treasure,not only environmental pollution is reduced, but also the preparation process of the product is simple, the production cost is low, the early strength of the prepared composite cement is high, and the composite cement has good social and economic benefit.

Description

technical field [0001] The invention relates to the comprehensive utilization of solid waste in the field of ecological environment materials, and more specifically relates to a composite cement using calcium carbide slag and fly ash as mixed materials. Background technique [0002] Cement is a powdery hydraulic cementitious material that can be mixed with water to form a plastic slurry, which can cement sand, stone and other materials, and can be hardened in the air and hardened in water. There are many types of cement, which are divided into three categories: general cement, special cement and special cement. Among them, composite cement is one of the varieties of general cement. Cement has better plasticity after mixing with water, and higher strength can be obtained after cement hardening, and the durability of cement is better. Therefore, cement is not only widely used in industrial and civil buildings, but also widely used in transportation, urban construction, agricu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/26C04B7/24C04B7/19C04B7/36
CPCC04B7/19C04B7/24C04B7/26C04B7/36Y02P40/10
Inventor 叶东忠
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products