Hydrocarbon oil desulfurization catalyst containing IMF-structure molecular sieve, preparation method of hydrocarbon oil desulfurization catalyst and process for hydrocarbon oil desulfurization

A technology of desulfurization catalyst and molecular sieve, which is applied in the direction of molecular sieve catalysts, chemical instruments and methods, physical/chemical process catalysts, etc., can solve the problems of increased operating costs and easy wear of catalysts, and achieves reduced operating and application costs and good wear resistance , the effect of high breakthrough sulfur capacity

Active Publication Date: 2019-05-07
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, this type of catalyst is prone to wear and tear during use, and the catalyst needs to be continuously replenished, which increases operating costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrocarbon oil desulfurization catalyst containing IMF-structure molecular sieve, preparation method of hydrocarbon oil desulfurization catalyst and process for hydrocarbon oil desulfurization
  • Hydrocarbon oil desulfurization catalyst containing IMF-structure molecular sieve, preparation method of hydrocarbon oil desulfurization catalyst and process for hydrocarbon oil desulfurization
  • Hydrocarbon oil desulfurization catalyst containing IMF-structure molecular sieve, preparation method of hydrocarbon oil desulfurization catalyst and process for hydrocarbon oil desulfurization

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The present invention also provides the preparation method of the hydrocarbon oil desulfurization catalyst provided by the present invention, the preparation method comprising: a, the sulfur storage metal oxide and / or the precursor of the sulfur storage metal oxide, the precursor of the inorganic oxide binder , boron nitride, molecular sieve with IMF structure, water and an acidic liquid are mixed to obtain a carrier slurry; wherein, the pH value of the carrier slurry is 1-5; b, the obtained carrier slurry is sequentially spray-dried and formed, the first drying and the second 1. Roasting to obtain a catalyst carrier; c. Introducing the precursor of the metal promoter into the catalyst carrier and then performing the second drying and second calcination in sequence; optionally d. Reducing the product obtained in step c under a hydrogen-containing atmosphere; A hydrocarbon oil desulfurization catalyst is obtained.

[0037] According to the present invention, the precurso...

Embodiment approach

[0047] One embodiment, the present invention specifically includes the following solutions:

[0048] 1. A desulfurization catalyst comprising:

[0049] 1) Sulfur-storage metal oxides, wherein the sulfur-storage metal is selected from one or more of the metals of Group IIB of the Periodic Table of the Elements, the metals of Group VB of the Periodic Table of the Elements, and the metals of Group VIB of the Periodic Table of the Elements, preferably selected from One or more of zinc, cadmium, niobium, tantalum, chromium, molybdenum, tungsten and vanadium, more preferably one or more selected from zinc, molybdenum and vanadium, more preferably zinc;

[0050] 2) Inorganic binder, preferably one or more selected from heat-resistant inorganic oxides, more preferably selected from one or more of aluminum oxide, silicon oxide, titanium oxide and tin oxide, more preferably selected from One or more of aluminum oxide, titanium oxide and tin oxide;

[0051] 3) The carrier component is ...

Embodiment 1

[0099] Get 2.38kg of titanium tetrachloride (Beijing Chemical Plant, analytically pure, 99% by weight) slowly add 4.6kg of 5% by weight of dilute hydrochloric acid, stir slowly to avoid the precipitation of titanium oxide crystals, and obtain a light yellow transparent titanium sol pH=2.0 ;

[0100] With 4.43kg of zinc oxide powder (Headhorse company, purity 99.7% by weight), 0.75kg of HIM-5 molecular sieve (Sinopec Catalyst Changling Branch Company, containing dry basis 0.70kg, SiO 2 :Al 2 o 3 The molar ratio is 25), 2.06kg of hexagonal boron nitride (purity>99.0%, Qinhuangdao Yinuo High-tech Material Development Co., Ltd.) and 6.57kg of deionized water are mixed, and after stirring for 30 minutes, zinc oxide, HIM-5 molecular sieve and a mixed slurry of hexagonal boron nitride; then add the above-mentioned titanium sol, mix and stir for 1 hour to obtain a carrier slurry with a pH value of 3.5;

[0101] The resulting carrier slurry was used in Niro Bowen Nozzle Tower TM Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hydrocarbon oil desulfurization catalyst containing an IMF-structure molecular sieve, a preparation method of the hydrocarbon oil desulfurization catalyst and a process forhydrocarbon oil desulfurization. Through adoption of the weight of the hydrocarbon oil desulfurization catalyst or the total weight of sulfur-storing metal oxide, an inorganic oxide binder, boron nitride, the IMF-structure molecular sieve and a metal promoter as a standard, the hydrocarbon oil desulfurization catalyst contains, by weight, 10-80% of the sulfur-storing metal oxide on the basis of oxide, 3-35% of the inorganic oxide binder on the basis of oxide, 5-40% of boron nitride, 1-20% of the IMF-structure molecular sieve based on a dry basis and 5-30% of the metal promoter on the basis ofmetal elements. The hydrocarbon oil desulfurization catalyst has the advantages of high stability, good desulfurization activity and good wear resistance when applied to the process for hydrocarbon oil desulfurization.

Description

technical field [0001] The invention relates to a hydrocarbon oil desulfurization catalyst containing an IMF structure molecular sieve, a preparation method thereof and a hydrocarbon oil desulfurization process. Background technique [0002] With the increasing scarcity of crude oil resources, how to effectively utilize limited resources to produce light products in a large amount has become the goal pursued by refinery technology developers. On the other hand, with the continuous improvement of environmental protection requirements, environmental protection regulations are becoming increasingly strict. The current gasoline quality standard GB17930-2013 requires that the sulfur content in gasoline must be less than 10ppm from January 1, 2017. Therefore, the clean product production technology that can simultaneously increase the yield of the target product has become the choice of many refiners. [0003] In my country, catalytic cracking has been widely used due to its good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/70B01J29/76C10G45/12
Inventor 宋烨林伟王磊刘俊田辉平
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com