Preparation method of phase change heat storage capsule for power lithium battery thermal regulation

A phase change heat storage and lithium battery technology, which is applied in microcapsule preparations, microsphere preparation, heat exchange materials, etc., can solve the problems of liquid molten salt being easily lost, leaking, corrosive, unsuitable for phase change energy storage materials, etc.

Active Publication Date: 2021-12-10
HUBEI UNIV OF SCI & TECH
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the melting points of these materials are all over 65°C, so they are not suitable as phase change energy storage materials for thermal regulation of lithium batteries.
In addition, when the above two mixed molten salt phase change energy storage materials undergo a solid-liquid phase transition during the heat absorption process, the liquid molten salt is easy to leak and has a certain degree of corrosion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of phase change heat storage capsule for power lithium battery thermal regulation
  • Preparation method of phase change heat storage capsule for power lithium battery thermal regulation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 20~35wt% lithium nitrate, 1.5~5wt% sodium nitrate, 2.5~10wt% potassium nitrate, 2~10wt% calcium nitrate, 5~15wt% sodium nitrite, 15~35wt% sodium chloride, 1~6wt% carbonic acid Potassium and 1-8wt% potassium sulfate are mixed and ground into fine powder, dried at 150°C for 10 hours, mixed according to a certain mass fraction ratio to obtain a mixed salt (melting point is 50-55°C), heated and melted at 200°C for 10 hours, Take it out and put it in a desiccator to cool, then grind it into a fine powder, and sieve it with a 120-mesh sieve;

[0017] Put 4 grams of sieved mixed molten salt fine powder and 15 milliliters of n-butyl ether in a round-bottomed flask, and after 30 minutes of ultrasonic dispersion, add 3 grams of n-butyl ether of perhydropolysilazane (PHPS) Solution (mass fraction is 30%), adopt magnetic stirring to mix evenly, then add 150 grams of n-dodecane and stir and extract for 15 minutes, let stand for 30 minutes, remove the mixed solution of n-butyl ether ...

Embodiment 2

[0019] 20~35wt% anhydrous lithium nitrate, 1.5~5wt% sodium nitrate, 2.5~10wt% potassium nitrate, 2~10wt% anhydrous calcium nitrate, 5~15wt% sodium nitrite, 15~35wt% sodium chloride, 1 ~6wt% potassium carbonate and 1~8wt% potassium sulfate are mixed and ground into fine powder, dried at 150°C for 10 hours, mixed according to a certain mass fraction ratio to obtain mixed salt (melting point is 50~55°C), heated at 200°C Melt for 10 hours, take it out and put it in a desiccator to cool, then grind it into a fine powder, and sieve it with a 120-mesh sieve;

[0020] Put 4 grams of sieved mixed molten salt fine powder and 15 milliliters of n-butyl ether in a round-bottomed flask, and after 30 minutes of ultrasonic dispersion, add 3 grams of n-butyl ether of perhydropolysilazane (PHPS) Solution (mass fraction is 30%), adopt magnetic stirring to mix evenly, then add 150 grams of n-dodecane and stir and extract for 15 minutes, let stand for 30 minutes, remove the mixed solution of n-but...

Embodiment 3

[0022] 35~63wt% lithium nitrate trihydrate, 1.5~5wt% sodium nitrate, 2.5~10wt% potassium nitrate, 2.5~15wt% calcium nitrate tetrahydrate, 5~15wt% sodium nitrite, 15~35wt% sodium chloride, 1 ~6wt% potassium carbonate and 1~8wt% potassium sulfate are mixed and ground into fine powder, dried at 150°C for 10 hours, mixed according to a certain mass fraction ratio to obtain mixed salt (melting point is 50~55°C), heated at 200°C Melt for 10 hours, take it out and put it in a desiccator to cool, then grind it into a fine powder, and sieve it with a 120-mesh sieve;

[0023] Put 4 grams of sieved mixed molten salt fine powder and 15 milliliters of n-butyl ether in a round-bottomed flask, and after 30 minutes of ultrasonic dispersion, add 3 grams of n-butyl ether of perhydropolysilazane (PHPS) Solution (mass fraction is 30%), adopt magnetic stirring to mix evenly, then add 150 grams of n-dodecane and stir and extract for 15 minutes, let stand for 30 minutes, remove the mixed solution of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
phase transition temperatureaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a phase-change heat storage capsule used for thermal regulation of a power lithium battery, and belongs to the technical field of power batteries. 20~35wt% lithium nitrate, 1.5~5wt% sodium nitrate, 2.5~10wt% potassium nitrate, 2~10wt% calcium nitrate, 5~15wt% sodium nitrite, 15~35wt% sodium chloride, 1~6wt% carbonic acid Potassium, the mixed salt that 1~8wt% potassium sulfate forms is ground into fine powder, forms the molten salt fine powder of uniform particle size after sieving with 120 mesh sieves; The molten salt fine powder after 4 grams of sieving is mixed with 3 grams of perhydrogen The n-butyl ether solution (mass fraction: 30%) of polysilazane (PHPS) was put into a round-bottomed flask and mixed evenly, and 150 g of n-dodecane was added and stirred for 10 minutes, then allowed to stand for 30 minutes. The invention has the advantages of phase transition temperature of 50-55 DEG C, low cost and the like.

Description

technical field [0001] The invention belongs to the technical field of power batteries, and relates to a preparation method of a phase-change heat storage capsule used for thermal regulation of a power lithium battery. Background technique [0002] In recent years, the new energy electric vehicle market at home and abroad has developed rapidly, and its power source is mainly lithium batteries. The comprehensive electrochemical performance of lithium-ion battery is excellent, and the specific energy density is as high as 250WhKg -1 , and in continuous improvement, while manufacturing costs continue to decline, has great prospects for development. However, lithium-ion batteries also have their shortcomings. During their frequent charging and discharging, they tend to generate heat and heat up. If the heat and temperature cannot be controlled in time, it will easily lead to thermal runaway and cause the battery to short-circuit, catch fire or even explode, such as: Tesla Ther...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): B01J13/02C09K5/06
Inventor王军涛
OwnerHUBEI UNIV OF SCI & TECH