Surface functionalized carbon fiber reinforced polyether-ether-ketone dental composite material and preparation method thereof

A technology of polyether ether ketone and composite materials, which is applied in medical science, pharmaceutical formulations, coatings, etc., can solve problems such as difficult to meet, low surface activity, poor biocombination performance, and poor osteogenesis performance. The effect of mild treatment conditions and simple operation methods

Pending Publication Date: 2019-09-06
FIRST HOSPITAL OF SHANXI MEDICAL UNIV
View PDF7 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, carbon fiber-reinforced polyetheretherketone composite is an inert material with low surface activity, poor biocom...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface functionalized carbon fiber reinforced polyether-ether-ketone dental composite material and preparation method thereof
  • Surface functionalized carbon fiber reinforced polyether-ether-ketone dental composite material and preparation method thereof
  • Surface functionalized carbon fiber reinforced polyether-ether-ketone dental composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The preparation method of the surface functionalized carbon fiber reinforced polyetheretherketone dental composite material specifically comprises the following steps:

[0034] (1) Injection molding carbon fiber reinforced polyether ether ketone molding composite material containing 20wt% carbon fiber at 360°C, then use 120 mesh, 600 mesh, 2000 mesh, 3000 mesh sandpaper to polish the surface, and then use acetone and absolute ethanol in sequence 1. Wash with deionized water, and wash for 15 minutes each, and then dry in a 60°C drying oven;

[0035] (2) Soak the carbon fiber reinforced polyether ether ketone molding composite material treated in step (1) in a sulfuric acid solution with a mass fraction of 80% for 10 minutes, take it out and rinse it with deionized water, and then immerse it in deionized water for 10 minutes;

[0036] (3) Take out the carbon fiber reinforced polyether ether ketone molding composite material treated in step (2) and dry it in an oven at 60°...

Embodiment 2

[0038] The preparation method of the surface functionalized polyether ether ketone dental composite material specifically comprises the following steps:

[0039] (1) Injection-molding polyether ether ketone molding composite materials at 350°C, and then using 120-mesh, 600-mesh, 2000-mesh, and 3000-mesh sandpaper to polish the surface, and then using acetone, absolute ethanol, and deionized water to clean the surface, and Wash for 20 minutes each, and then dry in a drying oven at 60°C;

[0040] (2) Soak the polyether ether ketone molding composite material treated in step (1) in a sulfuric acid solution with a mass fraction of 50% for 30 minutes, take it out, rinse it with deionized water, and then immerse it in deionized water for 10 minutes;

[0041] (3) Take out the polyether ether ketone molding composite material treated in step (2) and dry it in a 60°C oven for 12h, then soak it in a 5wt% graphene oxide solution for 10min, then take it out and put it in an 80°C oven Dry...

Embodiment 3

[0043] The preparation method of the surface functionalized carbon fiber reinforced polyetheretherketone dental composite material specifically comprises the following steps:

[0044] (1) Injection molding a carbon fiber reinforced polyetheretherketone molding composite material containing 60wt% carbon fiber at 390°C, then use 120 mesh, 600 mesh, 2000 mesh, 3000 mesh sandpaper to polish the surface, and then use acetone and absolute ethanol in sequence 1. Wash with deionized water, and wash for 20 minutes each, and then dry in a drying oven at 60°C;

[0045] (2) Soak the carbon fiber reinforced polyether ether ketone molding composite material treated in step (1) in a sulfuric acid solution with a mass fraction of 98% for 2 minutes, take it out, rinse it with deionized water, and then immerse it in deionized water for 10 minutes;

[0046] (3) Take out the carbon fiber reinforced polyetheretherketone molding composite material treated in step (2) and dry it in an oven at 60°C f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a surface functionalized carbon fiber reinforced polyether-ether-ketone dental composite material. The surface treatment of the carbon fiber reinforced polyether-ether-ketone composite material is carried out by sulfonation and functionalization of graphene oxide to obtain a surface functionalized carbon fiber reinforced polyether-ether-ketone composite material coated witha graphene oxide functional layer, the functional layer has strong binding force to a substrate, is not easy to fall off, and can effectively change the surface geometry and surface functional group composition of the carbon fiber reinforced polyether-ether-ketone composite material, the carbon fiber reinforced polyether-ether-ketone composite material is given with a new surface topography and surface properties, the biocompatibility and osteogenicity are increased, the application in medical materials is increased, the operation method of the invention is simple and easy, the surface treatment condition is mild, and the method is suitable for large-scale promotion and application, and has high medical value.

Description

technical field [0001] The invention relates to the technical field of medical materials, in particular to the technical field of dental materials, and more specifically relates to a surface functionalized carbon fiber reinforced polyether ether ketone dental composite material and a preparation method thereof. Background technique [0002] Due to the non-renewability of teeth, once damaged, implant materials can only be selected for repair or replacement. Most of the dental implant materials used clinically in the prior art are titanium implant materials, but the elastic modulus between titanium metal and bone tissue There is a huge difference, and it has metal allergies, which affects normal use. [0003] Polyether ether ketone is a kind of fully aromatic semi-crystalline thermoplastic special engineering plastics, which has excellent high temperature resistance, wear resistance, hydrolysis resistance, chemical corrosion resistance, etc., easy extrusion and injection moldi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L27/18A61L27/08A61L27/30
CPCA61L27/18A61L27/08A61L27/303A61L2400/18A61L2420/02A61L2430/12C08L71/00
Inventor 李英马婧
Owner FIRST HOSPITAL OF SHANXI MEDICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap