Preparation method of cyanate ester based wear-resistant self-lubricating swash plate
A cyanate ester, self-lubricating technology, used in mechanical equipment, devices for coating liquid on surfaces, special surfaces, etc., can solve problems such as increasing the difficulty of preparation, harmful to the social environment, and increasing social energy consumption, and achieves easy spray thickness. , the composition is reasonable, the effect of improving mechanical properties and heat resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] Example one
[0028] The preparation method of a cyanate ester-based wear-resistant self-lubricating swash plate involved in this embodiment includes the following steps: preparation of accelerator, preparation of graphene oxide / cyanate ester-epoxy resin composite material, and wear resistance Preparation, spraying and curing of self-lubricating coatings.
[0029] Step (1) Preparation of accelerator: add methyl tin mercaptan aqueous solution and fatty acid mercaptoethanol ester, slowly and uniformly add ammonia or sodium hydroxide aqueous solution with stirring until pH is 7.5, reaction temperature is 45°C, and reaction time is After 3 hours, separate the upper ammonium chloride aqueous solution or the sodium chloride aqueous solution, and the lower oil phase is washed with water to obtain the fatty acid mercaptoethanol ester methyl tin liquid product. The methyl tin mercaptan used is one of the three major organotin varieties. It is transparent, clear and viscous liquid, h...
Example Embodiment
[0041] Example two
[0042] The preparation method of a cyanate ester-based wear-resistant self-lubricating swash plate involved in this embodiment includes the following steps: preparation of accelerator, preparation of graphene oxide / cyanate ester-epoxy resin composite material, and wear resistance Preparation, spraying and curing of self-lubricating coatings.
[0043] Step (1) Preparation of accelerator: add methyl tin mercaptan aqueous solution and fatty acid mercaptoethanol ester, slowly and uniformly add ammonia or sodium hydroxide aqueous solution with stirring to pH 7.7, reaction temperature is 48°C, and reaction time is For 2.5 hours, separate the upper ammonium chloride aqueous solution or the sodium chloride aqueous solution, and the lower oil phase is washed with water to obtain the fatty acid mercaptoethanol ester methyl tin liquid product. The methyl tin mercaptan used is one of the three major organotin varieties. It is transparent, clear and viscous liquid, has goo...
Example Embodiment
[0055] Example three
[0056] The preparation method of a cyanate ester-based wear-resistant self-lubricating swash plate involved in this embodiment includes the following steps: preparation of accelerator, preparation of graphene oxide / cyanate ester-epoxy resin composite material, and wear resistance Preparation, spraying and curing of self-lubricating coatings.
[0057] Step (1) Preparation of accelerator: add methyl tin mercaptan aqueous solution and fatty acid mercaptoethanol ester, slowly and uniformly add ammonia or sodium hydroxide aqueous solution with stirring until the pH value is 8, the reaction temperature is 50°C, and the reaction time is After 3 hours, separate the upper ammonium chloride aqueous solution or the sodium chloride aqueous solution, and the lower oil phase is washed with water to obtain the fatty acid mercaptoethanol ester methyl tin liquid product. The methyl tin mercaptan used is one of the three major organotin varieties. It is transparent, clear and...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap