Preparation process of wear-resistant and anti-fading knitted fabric

A knitted fabric and preparation technology, which is applied in knitting, weft knitting, warp knitting, etc., can solve the problems that the wear resistance cannot meet the requirements, and achieve the effects of preventing clothing from wearing, improving wear resistance, and preventing discoloration

Active Publication Date: 2019-10-15
合肥乖米熊科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a preparation process for wear-resistant and anti-fading knitted fabrics. The composite yarn is prepared by blending wear-resistant fibers and cotton fibers, and then sizing is carried out through a weak acid sizing agent. Since the wear-resistant fiber preparation process is The monomer used is a monomer with a multi-conjugated structure. The polymer formed after polymerization has a high degree of conjugation, which can improve the wear resistance and toughness of the fabric, and solve the problem that is usually encountered in the preparation of the existing wear-resistant fabric. Can use cotton fiber, because the toughness and wear resistance of cotton fiber are strong, it can prevent clothes from wearing and tearing, but its wear resistance still cannot meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of wear-resistant and anti-fading knitted fabric
  • Preparation process of wear-resistant and anti-fading knitted fabric
  • Preparation process of wear-resistant and anti-fading knitted fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The specific preparation process of wear-resistant fiber is as follows:

[0024] ① Weigh 192g of β-ionone and 800mL of carbon tetrachloride solution into the reaction vessel at the same time, then add 187g of N-bromosuccinimide and 120g of benzoyl peroxide, heat up to 120-130°C and reflux for 20 -22h, then the product obtained is subjected to underpressure distillation to obtain light yellow bromoionone solution;

[0025] ② Add 24g of magnesium chips to 500mL of ether, and add 128g of 4-chlorophenol to it at the same time, at this time, the ether boils slightly until the ether boils off, and then distills under reduced pressure to obtain hydroxymagnesium chloride;

[0026] ③Add 152g of hydroxymagnesium chloride to 1000mL of ether, then add 272g of the bromoionone solution prepared in step ①, stir and react at room temperature for 2-3h, then evaporate to remove the solvent, and add the product to ethyl acetate Carrying out extraction, carrying out vacuum distillation to...

Embodiment 2

[0034] The specific preparation process of wear-resistant fiber is as follows:

[0035] 1. Add 24g of magnesium chips into 500mL of ether, and add 128g of 4-chlorophenol to it at the same time. At this time, the ether boils slightly until the ether boils and stops, and then distills under reduced pressure to obtain magnesium hydroxychloride;

[0036] ②Add 152g of hydroxymagnesium chloride to 1000mL of ether, then add 192g of β-ionone into it, stir and react at room temperature for 2-3h, then evaporate to remove the solvent, add the product into ethyl acetate for extraction, and extract the obtained The oil phase is subjected to vacuum distillation to obtain unsaturated phenol, and the reaction structure is as follows;

[0037]

[0038] ③ Add 1kg of the unsaturated phenol prepared in step ② into 10L of ethanol, stir and mix evenly, add 132g of potassium hydroxide to it, stir to dissolve, then heat up to 120-130°C and reflux for 15-16h, and then evaporate the product to remov...

Embodiment 3

[0045] A preparation process of wear-resistant and anti-fading knitted fabric, the specific preparation process is as follows:

[0046] In the first step, add 100g of cotton fiber to 500mL of 2% sodium hydroxide solution, heat up to 50-60°C and cook for 72 hours, then wash until neutral, dry and mix with the wear-resistant fiber filament prepared in Example 1 Blending according to the mass ratio of 1:4.6 to obtain composite yarn;

[0047] In the second step, add 105g detergent, 23g dispersant, 10g weak acid dye and 45g water into the dye vat at the same time, then adjust the temperature of the dye vat to 50-55°C, and then add 100g of the composite yarn prepared in the first step Dip dyeing in the dye vat for 30-40min, then raise the temperature to 90-100°C, add 12g of ammonium sulfate to it, then dip-dye for 20-30min, then wash in hot water at 50-60°C, and dry the washed composite yarn Then weave to form a knitted fabric;

[0048] The 3rd step, chitosan is added in acetic ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process of wear-resistant and anti-fading knitted fabric. The preparation process comprises specific preparation process as follows: adding cotton fiber to a sodium hydroxide solution with concentration of 2%, increasing the temperature to 50-60 DEG C, digesting the cotton fiber for 72 h, then, washing the cotton fiber to be neutral, and blending the cotton fiber with wear-resistant fiber after drying to obtain composite yarn; adding a detergent, a dispersant, dye and water to a dye vat simultaneously, then, adding the composite yarn to the dye vat for dipdyeing, next, washing the composite yarn in hot water, drying the washed composite yarn, and knitting the dried composite yarn to form knitted fabric; adding the knitted fabric to a sizing agent forsizing treatment to obtain the wear-resistant and anti-fading knitted fabric. The wear-resistant fiber and the cotton fiber are blended to prepare the composite yarn, then, sizing treatment is performed by the weakly acid sizing agent, as monomers used in the preparation process of the wear-resistant fiber are monomers adopting multi-conjugated structures, the conjugation degree of a polymer formed after polymerization is higher, and the wear resistance and toughness of the fabric can be further improved.

Description

technical field [0001] The invention belongs to the field of fabric preparation and relates to a preparation process of a wear-resistant and anti-fading knitted fabric. Background technique [0002] In workshop operations and construction site operations, since clothing often rubs against hard and rough objects, and high-intensity work processes are prone to sweating, the wear resistance of workers' uniforms determines the wearing life and comfort of clothing. The existing wear-resistant Cotton fiber is usually used in the fabric preparation process. Due to the strong toughness and wear resistance of cotton fiber, it can prevent clothing from wearing out. However, its wear resistance still cannot meet the requirements. At the same time, the existing fabrics are usually made of polyester. Acrylic acid is used as a sizing agent for sizing treatment, so that the surface of the fabric is covered with a layer of sizing agent. The protective effect of the sizing agent is used to e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/03D06M15/263D06P1/39D06P3/85D01F6/70D04B1/14D04B21/00D02G3/04D06M101/06D06M101/30
CPCD06M15/03D06M15/263D06M16/00D06P1/39D06P3/8204D01F6/70D04B1/14D04B21/00D02G3/04D06M2101/06D06M2101/30D06M2200/40D10B2201/02D10B2331/10
Inventor 崔永珍
Owner 合肥乖米熊科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com