A kind of bone repair material and preparation method thereof

A bone repair and hydrogel technology, applied in prosthetics, tissue regeneration, medical science, etc., can solve the problems that particles cannot be combined with hydrogel infinitely, magnesium ions are limited, and the release of magnesium ions is limited

Active Publication Date: 2021-11-30
SHENZHEN INST OF ADVANCED TECH CHINESE ACAD OF SCI
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, micro-nano core-shell particles are difficult to be directly applied to bone defects as bone repair materials, and they need to be compounded into other material systems, which will inevitably affect the release of magnesium ions
Nanocompositehydrogels stabilized by self-assembled multivalent bisphosphonate-magnesium nanoparticles mediate sustained release of magnesium ion and promote in-situ regeneration, Acta Biomaterialia.2017,64:389-400 Introducing phosphate groups into the gel and compounding magnesium salts into the hydrogel can also achieve the purpose of slow release of magnesium ions. Although this method can regulate the release of magnesium ions, the process of forming nanoparticles between magnesium ions and phosphoric acid is mainly through phosphoric acid. Combined with magnesium ions, but the magnesium ions combined by this method are limited, and the formed particles cannot be combined with the hydrogel indefinitely, so that the final release of magnesium ions is limited, and it is difficult to achieve continuous and stable release of magnesium ions in the whole process of bone defect repair. Purpose

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bone repair material and preparation method thereof
  • A kind of bone repair material and preparation method thereof
  • A kind of bone repair material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A bone repair material, the preparation method is as follows:

[0048] (1) Weigh 9g of chitosan with a molecular weight greater than 20kDa and add it to 300mL of 2% acetic acid aqueous solution. After it is completely dissolved, add 3.3mL of methacrylic anhydride (MA) dropwise to chitosan at a rate of 0.5mL / min. Sugar acetic acid solution, stirred overnight at room temperature, then added 100mL deionized water to the solution and continued to stir to dilute it; put the diluted solution in a 12-14kDa dialysis bag, and dialyze in deionized water at room temperature for 5 days, Change the deionized water every morning and evening, and keep stirring; after dialysis, freeze-dry to obtain white loose methacrylated chitosan.

[0049] (2) Take 1 g of methacrylated chitosan obtained in step (1), dissolve it in 100 mL of deionized water, add 0.05 M MES (monohydrate, about 10.6 g / L) after dissolving, and then add 0.7 g 3-phosphonohexanoic acid (3-phosphonohexanoic acid), after be...

Embodiment 2

[0052] A bone repair material, the preparation method is as follows:

[0053] (1) Weigh 9g of hyaluronic acid with a molecular weight greater than 20kDa and add it to 300mL of deionized aqueous solution. After it is completely dissolved, add 5mL of methacrylic anhydride (MA) dropwise to the aqueous solution of hyaluronic acid at a rate of 0.5mL / min , and add a small amount of sodium hydroxide to the solution, adjust the pH of the solution to weak alkaline, stir overnight under ice bath, then add 100mL deionized water to the solution and keep stirring to dilute it; place the diluted solution in In a 12-14kDa dialysis bag, dialyze in deionized water at room temperature for 5 days, change the deionized water every morning and evening, and keep stirring; after dialysis, freeze-dry to obtain white loose methacrylated hyaluronic acid.

[0054] (2) Take 1 g of the methacrylated hyaluronic acid obtained in step (1), dissolve it in 100 mL of deionized water, add 0.05 M MES (monohydrate...

Embodiment 3

[0057] A bone repair material, the preparation method is as follows:

[0058] (1) Weigh 9g of gelatin with a molecular weight greater than 20kDa and add it to 300mL of deionized aqueous solution. After it is completely dissolved, add 5mL of methacrylic anhydride (MA) dropwise to the gelatin aqueous solution at a rate of 0.5mL / min. Stir overnight, then add 100mL of deionized water to the solution and continue to stir to dilute it; place the diluted solution in a 12-14kDa dialysis bag, dialyze in deionized water at room temperature for 5 days, and change the deionized water every morning and evening water with continuous stirring; after dialysis, freeze-dry to obtain white loose methacrylated gelatin.

[0059] (2) Take 1 g of the methacrylated gelatin obtained in step (1), dissolve it in 100 mL of deionized water, then add 0.7 g of 3-phosphonohexanoic acid, and add 0.3 g of it after it is completely dissolved EDC (1-Ethyl-3-(3'-dimethylaminopropyl)carbodiimide), after stirring ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a bone repair material and a preparation method thereof, comprising hydrogel and magnesium-containing micro-nano particles; wherein, based on the total mass of the bone repair material as 100%, the mass percentage of magnesium is 0.1- 15%. The bone repair material provided by the present invention can realize the purpose of regulating the release rate of magnesium ions by regulating the cross-linking density of the hydrogel and the content of interacting groups with magnesium ions; at the same time, the bone repair material provided by the present invention has a large release amount of magnesium ions and Magnesium ions are released for a long time.

Description

technical field [0001] The invention belongs to the technical field of bone repair materials, and relates to a bone repair material and a preparation method thereof. Background technique [0002] Magnesium metal is a potential bone repair material for clinical use; Magnesium is an essential element in the human body and participates in various important metabolic processes in the human body. More than half of the magnesium in the human body is stored in the bone. Magnesium ions can promote bone formation by up-regulating the expression of calcitonin gene-related polypeptide CGRP in the periosteum. Appropriate concentration of magnesium ions can promote early angiogenesis in bone defects, up-regulate the expression of vascular endothelial growth factor, and promote the expression of middle and late osteogenic genes and bone marrow stem cells. Osteogenic differentiation can promote the proliferation of neural stem cells and the growth of neurite, showing comprehensive therapeu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/04A61L27/20A61L27/22A61L27/50A61L27/52
CPCA61L27/047A61L27/20A61L27/222A61L27/50A61L27/52A61L2300/102A61L2300/412A61L2300/602A61L2430/02C08L5/08C08L5/04
Inventor 赖毓霄陈英奇龙晶秦岭
Owner SHENZHEN INST OF ADVANCED TECH CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com