Self-growing deeply-combined exterior wall coating and manufacturing method thereof

A technology for exterior wall coatings and manufacturing methods, applied in wax coatings, fireproof coatings, antifouling/underwater coatings, etc., can solve problems such as harming human health, achieve strong permeability, strong self-permeability, and maintain stability Effect

Inactive Publication Date: 2019-12-06
青岛天地彩建筑科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, with the development of the times and the advancement of science and technology, the defects of oil-based paints have gradually emerged: First, it contains a strong pungent smell, and the gas contains a large amount of harmful substances, which are harmful to human health. , the strong pungent smell is volatilized to basically tasteless, but in fact its potential hazards still exist; second, banana water and thinner are often used as diluents, which contain a large amount of harmful carcinogens such as benzene and xylene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of self-growth penetrating deep high binding exterior wall paint, this self-growth penetrating deep high binding exterior wall coating is composed of triethanolamine borate 0.75kg by weight, some long-chain alkyl aryl silicone oil emulsions, some modified beeswax solutions Mixed; Among them, the long-chain alkylaryl silicone oil emulsion is obtained by mixing 14.3kg of long-chain alkylaryl silicone oil and 1.7kg of isomeric alkyl alcohol polyethers; the modified beeswax solution is obtained by Obtained by mixing reaction of 0.32kg of octacanoic acid, 0.74kg of nano zinc oxide and 10.7kg of beeswax.

[0025] The manufacturing method of above-mentioned exterior wall paint, comprises the following steps;

[0026] 1) Raw material preparation

[0027] ① Raw material preparation: Prepare stearic acid 0.32kg, nano-zinc oxide 0.74kg, beeswax 10.7kg, triethanolamine borate 0.75kg, long-chain alkyl aryl silicone oil 14.3kg, isomeric alkyl alcohol polyether by weight 1.7k...

Embodiment 2

[0042] The whole is consistent with Example 1, the difference is:

[0043] A kind of self-growth deep-penetrating high-bonding exterior wall coating, this self-growth deep-penetrating high-bonding exterior wall paint is composed of triethanolamine borate 0.7kg by weight, some long-chain alkyl aryl silicone oil emulsions, some modified beeswax solutions The long-chain alkylaryl silicone oil emulsion is obtained by mixing and reacting 13kg of long-chain alkylaryl silicone oil and 1.6kg of isomeric alkyl alcohol polyether; the modified beeswax solution is made of octadecyl It is obtained by mixing reaction of 0.4kg of alkanoic acid, 0.8kg of nanometer zinc oxide and 12kg of beeswax.

[0044] The manufacturing method of above-mentioned exterior wall paint, comprises the following steps;

[0045] 1) Raw material preparation

[0046] ① Raw material preparation: Prepare stearic acid 0.4kg, nano-zinc oxide 0.8kg, beeswax 12kg, triethanolamine borate 0.7kg, long-chain alkylaryl silic...

Embodiment 3

[0048] The whole is consistent with Example 1, the difference is:

[0049] A kind of self-growth deep-penetrating high-bonding exterior wall paint, this self-growth deep-penetrating high-bonding exterior wall paint is composed of triethanolamine borate 0.8kg by weight, some long-chain alkyl aryl silicone oil emulsions, some modified beeswax solutions The long-chain alkylaryl silicone oil emulsion is obtained by mixing and reacting 15kg of long-chain alkylaryl silicone oil and 1.8kg of isomeric alkyl alcohol polyether; the modified beeswax solution is made of eighteen It is obtained by mixing reaction of 0.3kg of alkanoic acid, 0.7kg of nanometer zinc oxide and 10kg of beeswax.

[0050] The manufacturing method of above-mentioned exterior wall paint, comprises the following steps;

[0051] 1) Raw material preparation

[0052] ① Raw material preparation: Prepare stearic acid 0.3kg, nano-zinc oxide 0.7kg, beeswax 10kg, triethanolamine borate 0.8kg, long-chain alkylaryl silicone...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a self-growing deeply-combined exterior wall coating and a manufacturing method thereof. The self-growing deeply-combined exterior wall coating is prepared from the following components of 0.7-0.8 parts of triethanolamine borate, certain long-chain alkyl aryl silicone oil emulsion and certain modified beewax solution in parts by weight through mixing, wherein the long-chainalkyl aryl silicone oil emulsion is prepared from 13-15 parts of long-chain alkyl aryl silicone oil and 1.6-1.8 parts of iso-alkyl alcohol polyether; and the modified beewax solution is prepared from0.3-0.4 parts of octadecanoic acid, 0.7-0.8 parts of nano zinc oxide and 10-12 parts of beewax. The coating disclosed by the invention is water-based, environment-friendly, high-temperature-resistant, ultraviolet-resistant, weather-resistant, strong in permeation force and high in film-forming strength.

Description

technical field [0001] The invention relates to the technical field of exterior wall coatings, in particular to a self-grown deep-depth high-combination exterior wall coating and a manufacturing method thereof. Background technique [0002] Exterior wall paint is used to paint the exterior walls of buildings, so the most important indicator is anti-ultraviolet radiation, which requires long-term exposure without discoloration. Currently, exterior wall coatings on the market are mainly oil-based paints, which have the following advantages: 1) Protective function, which is the common advantage of oil-based paints. Oil-based paints are relatively more anti-corrosion, waterproof, oil-proof, chemical-resistant, light-resistant, and durable. Wen et al. Objects are exposed to the atmosphere and are eroded by oxygen, moisture, etc., resulting in damages such as metal corrosion, wood decay, and cement weathering. Applying oil-based paint on the surface of the object forms a protect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D191/06C09D5/14C09D7/61C09D7/63C09D7/65
CPCC08K2003/2296C08K2201/011C08L2201/08C08L2205/03C09D5/14C09D5/18C09D183/04C09D7/61C09D7/63C09D7/65C08L71/00C08L91/06C08K13/02C08K5/09C08K3/22C08K5/55
Inventor 刘英武刘丰毓
Owner 青岛天地彩建筑科技有限公司