High anion permeability and high ion selectivity anion exchange membrane, preparation method and application thereof

An anion-exchange membrane and ion-selective technology, which is applied in the field of electrodialysis process, can solve the problems of difficulty in anion-exchange membranes, pouring membranes, etc., and achieve the effects of inhibiting water absorption and swelling, high anion permeability, and reducing surface resistance

Active Publication Date: 2020-01-17
SOUTH CHINA UNIV OF TECH
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention solves the problem that comb-like PPO anion exchange membranes are difficult to pour into membranes at a higher IEC by introducing hydrophobic alkyl-modified series dication side chains on the PPO skeleton

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High anion permeability and high ion selectivity anion exchange membrane, preparation method and application thereof
  • High anion permeability and high ion selectivity anion exchange membrane, preparation method and application thereof
  • High anion permeability and high ion selectivity anion exchange membrane, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) Preparation of BPPO with DBM of 0.1

[0035] Dissolve PPO (12.00g, methyl mole number 200mmol) in 100ml of chlorobenzene, add N-bromosuccinimide NBS (3.56g, 20mmol) and azoisobutyronitrile AIBN (0.22g, 1.33mmol) , react at 135°C for 2.5h, use 500 ml of methanol as the reaction solution to obtain a light yellow solid, filter and wash three times with methanol, dry in the air at 60°C and vacuum-dry to obtain brominated poly-2,6-dimethylphenyl ether with a DBM of 0.1 ( BPPO).

[0036] (2) single ion quaternization reagent a) preparation

[0037]Dissolve 1-bromohexane (10mmol, 1.65g) in 30mL ethyl acetate, add N,N,N',N'-tetramethylethylenediamine (11mmol, 1.28g), and stir the reaction at 30°C for 48h After filtration, a light yellow solid was obtained, and the light yellow solid was washed with 50 mL of ethyl acetate and then dried to obtain quaternization reagent a): N-(2-(dimethylaminoethyl)-N,N-dimethylhexyl- 1-ammonium bromide, the structural formula is as follow...

Embodiment 2

[0044] (1) Preparation of BPPO with DBM of 0.15

[0045] Dissolve PPO (12.00g, methyl mole number 200mmol) in 100ml of chlorobenzene, add N-bromosuccinimide NBS (5.34g, 30mmol) and azoisobutyronitrile AIBN (0.32g, 2.00mmol) , react at 135°C for 2.5h, use 500 ml of methanol as the reaction solution to obtain a light yellow solid, filter and wash three times with methanol, dry in the air at 60°C and vacuum-dry to obtain brominated poly-2,6-dimethylphenyl ether with a DBM of 0.15 ( BPPO).

[0046] (2) single ion quaternization reagent) a preparation

[0047] Single ion quaternization reagent a) is prepared with the same example 1 (2).

[0048] (3) Preparation of tandem dication side chain type polyphenylene ether anion exchange membrane QPTa-2 linked by hydrophobic alkyl groups:

[0049] Dissolve the quaternization reagent a) (1.5mmol, 0.42g) in (23mL) N-methylpyrrolidone, add BPPO (1.32g, bromomethyl mole number 1.5mmol) with a DBM of 0.15, and then stir the reaction at 30°C ...

Embodiment 3

[0053] (1) Preparation of BPPO with DBM of 0.2

[0054] Dissolve PPO (12.00g, methyl mole number 200mmol) in 100ml of chlorobenzene, add N-bromosuccinimide NBS (7.12g, 40mmol) and azoisobutyronitrile AIBN (0.434g, 2.67mmol) , react at 130°C for 3h, use 500ml of methanol for the reaction solution to obtain a light yellow solid, filter and wash three times with methanol, dry in the air at 60°C and vacuum-dry to obtain brominated poly-2,6-dimethylphenylene ether (BPPO) with a DBM of 0.2 ).

[0055] (2) single ion quaternization reagent a) preparation

[0056] Single ion quaternization reagent a) is prepared with the same example 1 (2).

[0057] (3) Preparation of tandem dication side chain type polyphenylene ether anion exchange membrane QPTa-3 linked by hydrophobic alkyl groups:

[0058] Dissolve the quaternization reagent a) (2.0mmol, 0.56g) in (25mL) N-methylpyrrolidone, add BPPO (1.36g, bromomethyl mole number 2.0mmol) with a DBM of 0.2, and then stir the reaction at 40°C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface resistanceaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high anion permeability and high ion selectivity anion exchange membrane, a preparation method and application thereof. The material of the ion exchange membrane is a hydrophobic alkyl modified free dication string structure type polyphenyl ether ionomer of C1 to C6, and the ion selective permeability is 90% to 96% and the sheet resistance is 1.60 to 5.57 omega / cm<2> whenIEC is 1.30 to 2.59 meq / g. Hydrophobic alkyl modified series dications of C1 to C6 are introduced into a poly (2,6-dimethylphenyl ether) skeleton, so that the charge density of the obtained membraneis effectively improved, the problem of low anion-cation selectivity of a commercialized mono-quaternary ammonium ion PPO anion exchange membrane when the commercialized mono-quaternary ammonium ion PPO anion exchange membrane has higher IEC is solved, and the ion conductivity of the membrane is enhanced while the anion-cation selective permeability of the membrane is improved. The membrane has good mechanical properties, and can meet the requirement of the electrodialysis process on the comprehensive performance of the anion exchange membrane.

Description

technical field [0001] The invention relates to a preparation method of a serial double cation anion exchange membrane connected by a hydrophobic alkyl side chain, and the anion exchange membrane is suitable for an electrodialysis process. Background technique [0002] Electrodialysis technology is an emerging membrane separation technology, which has the characteristics of simple equipment, convenient operation, high efficiency and no pollution. In recent years, electrodialysis technology with ion exchange membrane as the core has been widely used to control environmental pollution, solve problems such as water shortage and energy shortage, and has shown great application prospects. [0003] Anion exchange membrane is the core component of electrodialysis technology. As two important performance parameters of membranes, ionic conductivity and ion selective permeability always show a negative correlation. Generally, anion exchange membranes can only have efficient ion condu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J41/13B01J47/12C02F1/469
CPCB01J47/12B01J41/13C02F1/4693
Inventor 李秀华魏标文余以刚潘健聪
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap