A polyethylene/carboxymethylete shell polyanose, nano -nano -fiber medical dressing and preparation methods and applications

A technology of carboxymethyl chitosan and polyvinyl alcohol, applied in the field of medicine, can solve problems such as adhesion between wounds and dressings, secondary trauma of new tissues, poor hemostasis effect, etc., and achieve good application, good air permeability, easy to dissolve effect

Active Publication Date: 2021-06-01
东莞华工创为生物科技有限公司 +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, most medical institutions in my country still use traditional cotton gauze as a commonly used medical dressing, but traditional medical gauze needs to be replaced frequently, and the wound is easy to dry. The adhesion between the new tissue will cause secondary trauma to the new tissue, and there will also be clinical phenomena such as bacterial growth and poor hemostasis effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A polyethylene/carboxymethylete shell polyanose, nano -nano -fiber medical dressing and preparation methods and applications
  • A polyethylene/carboxymethylete shell polyanose, nano -nano -fiber medical dressing and preparation methods and applications
  • A polyethylene/carboxymethylete shell polyanose, nano -nano -fiber medical dressing and preparation methods and applications

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The experiment was carried out under the environment temperature of 30° C. and humidity of 40% RH. Take by weighing the PVA of 10g with electronic balance, it is packed in the clean Erlenmeyer flask, then 1.5g (known solid content is 30%) of Periplaneta americana concentrated solution is added in the Erlenmeyer flask, adds 2g in the volumetric flask CMCS, after calculating the mass ratio of solute and solvent, add 100g of pure water into the Erlenmeyer flask, stir in a water bath at a temperature of 60°C for 5 hours, and prepare the Periplaneta americana @PVA / CMCS spinning solution. The spinning conditions were set as follows: injection speed 4.0mm / h, receiving distance 20cm, spinning voltage 23kV, using electrospinning machine to prepare Periplaneta americana @PVA / CMCS nanofiber membrane medical dressing. Set the drying temperature at 85°C, dry in an oven for 30 minutes, and undergo a certain heat treatment to promote the crosslinking reaction and improve the water res...

Embodiment 2

[0035] The experiment was carried out under the condition that the ambient temperature was 25° C. and the humidity was 42% RH. Take by weighing the PVA of 5g with electronic balance, it is packed in the clean Erlenmeyer flask, then 0.8g (known solid content is 30%) of Periplaneta americana concentrated solution is added in the Erlenmeyer flask, adds 2g in the volumetric flask CMCS, after calculating the mass ratio of solute and solvent, add 45g of pure water into the Erlenmeyer flask, stir in a water bath at a temperature of 60°C for 5 hours, and prepare the Periplaneta americana @PVA / CMCS spinning solution. The spinning conditions were set as follows: injection speed 3.0mm / h, receiving distance 18cm, spinning voltage 20kV, using electrospinning machine to prepare Periplaneta americana @PVA / CMCS nanofiber membrane medical dressing. Set the drying temperature at 90°C, and dry in an oven for 60 minutes. After a certain heat treatment, the cross-linking reaction is promoted, and ...

Embodiment 3

[0038] The experiment was carried out under the environment temperature of 25° C. and humidity of 39% RH. Take by weighing the PVA of 5g with electronic balance, it is packed in the clean Erlenmeyer flask, then 0.7g (known solid content is 30%) of Periplaneta americana concentrated solution is added in the Erlenmeyer flask, adds 1.5 to the volumetric flask g CMCS. After calculating the mass ratio of solute to solvent, add 40g of pure water into the Erlenmeyer flask, stir in a water bath at a temperature of 60°C for 5 hours, and prepare the Periplaneta americana @PVA / CMCS spinning solution. The spinning conditions were set as follows: injection speed 5.0mm / h, receiving distance 20cm, spinning voltage 21kV, using electrospinning machine to prepare Periplaneta americana @PVA / CMCS nanofiber membrane medical dressing. Set the drying temperature at 80°C, and dry in an oven for 90 minutes. After a certain heat treatment, the cross-linking reaction is promoted, and the water resistance...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of medicine, and specifically discloses a polyvinyl alcohol / carboxymethyl chitosan nanofiber medical dressing as well as a preparation method and application thereof. The preparation method specifically includes the following steps: mixing polyvinyl alcohol (PVA), carboxymethyl chitosan (CMCS), Periplaneta americana concentrate and water evenly to prepare a spinning solution containing the active substance of Periplaneta americana ; Then the Periplaneta americana slow-release medical dressing was prepared by electrospinning. Compared with the traditional medical gauze plus dressing or the preparation of medical dressings by coating, the slow-release nanofiber medical dressing has good air permeability and high porosity, which can keep the wound moist and facilitate the respiration of cells . Nanofibers can effectively prevent bacteria and particles in the air from contacting wounds. Compared with the general medical dressing prepared by coating, the nanofiber medical dressing has good air permeability and better absorption of skin exudate.

Description

technical field [0001] The invention belongs to the technical field of medicine, and in particular relates to a polyvinyl alcohol / carboxymethyl chitosan nanofiber medical dressing and a preparation method and application thereof. Background technique [0002] Periplaneta americana belongs to the genus Periplaneta, commonly known as cockroach, is one of the insect groups with the strongest vitality, the oldest and the most successful reproduction so far in the world. Periplaneta americana is a traditional Chinese medicinal material that was first recorded in "Shen Nong's Materia Medica". Modern research has shown that it has pharmacological effects such as anti-cancer, anti-bacterial, anti-inflammatory, and promotion of tissue repair. The chemical components in Periplaneta americana mainly include pheromones, aggregation pheromones, amino acids, neuropeptides, sugars, proteins, oils, nucleic acids, isoflavones, etc. [0003] Carboxymethyl chitosan and its various derivatives...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/4326D04H1/728D01F6/50D01F1/10D01D5/00A61F13/00
CPCA61F13/00012A61F13/00063A61F13/00987A61F2013/00906D01D5/003D01D5/0092D01F1/103D01F6/50D04H1/4326D04H1/728
Inventor 程建华黄政张继勇
Owner 东莞华工创为生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com