Polypropylene composite material and preparation method thereof

A composite material, polypropylene technology, applied in the field of permanent antistatic, low-odor automotive interior polypropylene composite materials and its preparation, can solve the problem of not being able to meet the requirements of automotive interior material odor, and achieve the benefit of large-scale business The effect of modern production, excellent antistatic performance and low cost

Inactive Publication Date: 2020-05-19
联泓(江苏)新材料研究院有限公司
View PDF21 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the main source of polypropylene odor is small molecular substances such as alcohols, ketones, acids, and hydrocarbons produc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Add polypropylene, toughening agent and mineral filler to the high-speed mixer and mix thoroughly. During the stirring process, add antistatic agent, porous adsorbent, acid absorbing agent, and finally add antioxidant and light stabilizer. After mixing evenly, transfer it to A twin-screw extruder with a length-to-diameter ratio of 48 and a total of 12 barrels is used for melt extrusion and granulation. The temperature of the second barrel is 185°C, the temperature of the third barrel is 230°C, and the temperature of the fourth barrel is 220°C, the fifth barrel temperature is 220°C, the sixth barrel temperature is 210°C, the seventh barrel temperature is 210°C, the eighth barrel temperature is 205°C, and the ninth barrel temperature is 205°C, the temperature of the tenth barrel is 205°C, the temperature of the eleventh barrel is 205°C, the temperature of the twelfth barrel is 185°C, the temperature of the head is 190°C, the feeding frequency is 40 Hz, the host The rotati...

Embodiment 2

[0050] According to the processing method of embodiment 1, carry out the preparation of permanent antistatic, low-odor automobile interior decoration polypropylene composite material, the difference is that the parts by weight of each component are as follows:

[0051] Copolymerized polypropylene (China Taiwan Plastics 5250T) 67 parts

[0052] Ethylene-octene copolymer (Dow POE 8150) 10 parts

[0053] Talc powder 20.8 parts

[0054] 0.5 parts of polyether ester imide

[0055] Tin antimony oxide 0.5 parts

[0056] Hydrotalcite 0.5 parts

[0057] Calcium stearate 0.2 parts

[0058] Antioxidant 168 0.2 parts

[0059] Antioxidant 1010 0.1 parts

[0060] Light stabilizer T78 0.2 parts

Embodiment 3

[0062] According to the processing method of embodiment 1, carry out the preparation of permanent antistatic, low-odor automobile interior decoration polypropylene composite material, the difference is that the parts by weight of each component are as follows:

[0063] Homopolypropylene (Shanghai Petrochemical M1200HS) 10 parts

[0064] Copolymerized polypropylene (Korean SK BX3800) 46 parts

[0065] Ethylene-octene copolymer (Dow POE 8180) 20 parts

[0066] Calcium carbonate 20 parts

[0067] Polyether ester amide 1.5 parts

[0068] Tin antimony oxide 0.8 parts

[0069] Zeolite 1 part

[0070] Calcium stearate 0.2 parts

[0071] Antioxidant 168 0.2 parts

[0072] Antioxidant 1010 0.1 parts

[0073] Light stabilizer 3853 0.2 parts

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polypropylene composite material and a preparation method thereof. The composite material comprises the following raw materials in parts by weight: (1) 35-85 parts of polypropylene; (2) 5-35 parts of a toughening agent; (3) 5-40 parts of a mineral filler; (4) 0.3-15 parts of a composite antistatic agent, wherein the composite antistatic agent is composed of a polymer permanent antistatic agent and an inorganic permanent antistatic agent, and the composite material can also comprise a porous adsorbent, an acid acceptor, an antioxidant and a light stabilizer. Accordingto the invention, the polypropylene composite material disclosed by the invention adopts the composite antistatic agent, has low volume resistivity, and can meet the antistatic and dustproof requirements of automotive trim materials; by adding deodorants with different smell removal mechanisms, the smell of the product is low, so the product can meet the requirements of automotive trim materials for smell; and the polypropylene composite material has characteristics of excellent mechanical properties, simple preparation process, good processability, low cost, and facilitation of large-scale commercial production.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a polypropylene composite material for permanent antistatic and low-odor automobile interior decoration and a preparation method thereof. Background technique [0002] With the rapid development of the automobile industry, the requirements for lightweight, energy saving and emission reduction are becoming more and more stringent, and more and more plastic materials are applied to the interior and exterior parts of automobiles. Polypropylene (PP) has been widely used in instrument panels, door panels, floor mats, trunk covers, and pillars in recent years because of its low density, low price, good mechanical properties, and excellent processing properties. And other automotive interior parts. [0003] Although polypropylene resin has many advantages as a material for automotive interior parts, because its molecular chain is non-polar, its volume resistivity ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/14C08L23/12C08L23/08C08L79/08C08K13/04C08K7/26C08K7/24C08K3/22C08K5/098
CPCC08L23/14C08L2205/06C08L2201/04C08L2201/08C08L2205/03C08L2205/035C08K2201/017C08K2003/265C08K2201/011C08K2201/014C08L23/0815C08L79/08C08K13/04C08K7/26C08K3/22C08K5/098C08K7/24C08L23/12C08K3/26C08L23/0876
Inventor 李成浪吴集钱钱伟李方
Owner 联泓(江苏)新材料研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap