A silk fiber and fabric technology, which is applied in the field of preparation of colored silk fiber fabrics, can solve the problems of poor overall performance, low production efficiency and yield rate, and poor performance stability of colored silk fabrics, and achieves preparation efficiency and yield rate High, simple preparation method, excellent performance stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] This example provides a kind of colored silk fiber fabric, comprises face thread structure and bottom thread structure, wherein: the mass percentage that the face thread structure accounts for in the fabric is 60%, and the face thread structure is formed by face thread, the The bottom thread structure is formed by the bottom thread; the bottom thread is DTY colored thread, and the top thread is modified polyester thread.
[0021] The DTY colored yarn is 150D / 288F; the denier of the modified polyester yarn is 50D.
[0022] The preparation method of described modified polyester yarn, comprises the steps:
[0023] S1. Mix polyester chips with pumice stone, pearl powder and coupling agent, extrude and granulate to obtain masterbatch;
[0024] S2. The masterbatch is melt-spun to obtain the modified polyester fiber;
[0025] S3. The polyester fiber yarn is sequentially subjected to cleaning and carding, combing, drawing, coarse sanding, and spinning processes, and then wash...
Embodiment 2
[0035] Example 2 provides a colored silk fiber fabric, its formula and preparation method are basically the same as in Example 1, the difference is that the bottom yarn is modified polyester yarn, the top yarn is DTY colored yarn, and the warping process parameters : The number of warping strips is 120, the warping speed is 400m / min, the hairiness induction setting is 1; the pressing roller pressure is 3.5kg / C㎡, the coiling tension is 36kg, the creel tension is 13g / piece, and the monofilament is 31g / piece. Hardness 57.
Embodiment 3
[0037] Example 3 provides a colored silk fiber fabric, its formula and preparation method are basically the same as in Example 1, the difference is that the warping process parameters: the number of warping strips is 120, the warping speed is 420m / min, the hairiness The induction setting is 1; the pressing roller pressure is 4kg / C㎡, the coiling tension is 36kg, the creel tension is 14g / piece, the monofilament is 33g / piece, and the hardness is 60.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com