A kind of preparation method of hydrogenation carbon residue removal catalyst

A technology for removing carbon residues and catalysts, which is applied in the field of preparation of hydrogenation carbon residue removal catalysts. It can solve the problems of less macropore content, high pore channel content, and increased surface acid content, and achieve suitable acid strength distribution, high acid content, and The effect of moderate pore structure

Active Publication Date: 2022-03-08
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The catalyst prepared by this method has a relatively high 6-8nm pore content and a relatively small macropore content, which is not conducive to the diffusion of macromolecular reactants. In addition, the surface acid content of the carrier needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of hydrogenation carbon residue removal catalyst
  • A kind of preparation method of hydrogenation carbon residue removal catalyst
  • A kind of preparation method of hydrogenation carbon residue removal catalyst

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] Preparation of Material B:

[0029] (1) Preparation of material B1

[0030] 200 grams of kaolin was placed in a high-temperature muffle furnace and activated at 850° C. for 5 hours. Weigh 100 grams of the above-mentioned activated kaolin, 400 grams of ammonium bicarbonate, add 1500 grams of distilled water to the above materials and stir for 20 minutes, transfer the mixed materials into an autoclave and seal it and heat it up to 80 degrees Celsius at a speed of 10 degrees Celsius / min The temperature was kept constant for 3 hours, then the temperature was raised to 135°C at a rate of 5°C / min for 5 hours, and then the material was dried at 110°C for 6 hours and calcined at 750°C for 5 hours.

[0031] Weigh 50 grams of the above-mentioned materials, place them in a beaker, add 1500 grams of hydrochloric acid solution with a mass percentage concentration of 25% into the beaker, place the beaker in an ultrasonic container for ultrasonic treatment, the ultrasonic frequency i...

Embodiment 1

[0037] (1) Mix 5 grams of starch and 200 grams of pseudo-boehmite evenly to prepare mixed material A.

[0038] (2) Put 100g of mixed material A in the turntable molding machine and mix thoroughly, adjust the inclination angle of the turntable to 40º, and the rotation speed of the turntable to 10rpm; spray the acetic acid aqueous solution with a mass concentration of 2% on the mixed material A in the turntable through the sprayer After mixing and contacting, the molding time of the material in the turntable is 30 minutes, and the precursor I with a diameter of 1.0-1.5 mm is obtained;

[0039] (3) Put 100g of material B1 and the precursor I prepared in step (2) into the turntable molding machine and mix thoroughly, adjust the inclination angle of the turntable to 40º, and the rotation speed of the turntable to 10rpm, spray the acetic acid aqueous solution with a mass concentration of 2% After being sprayed on the materials in the turntable and mixed and contacted, the molding ti...

Embodiment 2

[0042] The same as in Example 1, except that the amount of starch added in the mixed material A is 8 grams, and the material B1 is replaced with material B3 to obtain the hydrogenation carbon removal catalyst Cat-2, and the properties of the catalyst are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a hydrogenation carbon removal catalyst, which comprises the following contents: (1) mixing a pore-enlarging agent with pseudo-boehmite to obtain a mixture A; (2) mixing metakaolin, ammonium bicarbonate and Mix with water, seal and crystallize. After crystallization, the material is dried, roasted, dealuminated, and dried to obtain material B; (3) Mixture A is ball-shaped to obtain precursor I; (4) Material B and precursor I Mixing, ball forming, drying, calcining, and loading of active components to obtain a hydrogenation carbon removal catalyst. The catalyst prepared by the method has relatively high macropore content and suitable surface acidity, and the hydrogenation carbon removal catalyst has high carbon removal activity and high hydrogenation desulfurization and denitrogenation activities.

Description

technical field [0001] The invention relates to the field of catalyst preparation, in particular to a method for preparing a hydrogenation carbon removal catalyst. Background technique [0002] Residual oil contains the heaviest components in crude oil, including a variety of complex hydrocarbons, as well as high concentrations of sulfur, nitrogen and metals (mainly nickel and vanadium), and has the characteristics of high viscosity and high carbon residue value . Because the carbon residue value of the generated oil is one of the key indicators affecting the feed ratio of the downstream FCC unit, and it is also an important reason for catalyst deactivation, so it is very important to carry out hydrogenation and decarbonization of residual oil in the hydrotreating process a link. The precursor of residue carbon is mainly composed of larger polycyclic aromatic hydrocarbons in asphaltenes or colloids. To remove these impurities as much as possible, it is necessary to improve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/882B01J35/10B01J37/10B01J37/08C10G45/08
CPCB01J23/882B01J35/1019B01J35/1042B01J37/08C10G45/08
Inventor 季洪海凌凤香王少军张会成沈智奇
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com