Preparation method of N-hydroxymethyl acrylamide composite water-based acrylic coating for wickerwork

The technology of methylol acrylamide and methylene bisacrylamide is applied in the field of preparation of N-methylol acrylamide composite water-based acrylic paint for willow weaving, which can solve the problem of aggravating the corrosion of willow weaving products, unable to continue to use, short growth cycle, etc. problem, to achieve the effect of excellent adhesion, improved life, and improved aging resistance

Active Publication Date: 2020-12-04
安徽三和工艺品有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The growth cycle of willow is short, usually it can be used as raw materials in one year, and the rate of finished products is extremely high, the supply of raw materials is sufficient, and it is convenient to obtain materials. Willow products are common containers and handicrafts in people's lives. Baskets, baskets, dustpans, buckets, wicker boxes, baskets, flower baskets, fences, food plates, etc., have been innovated and developed, and have formed flowerpots, vases, lampshades, and many other decorations, which are deeply loved by people. , but due to its wood properties, especially when the air is kept at high humidity for a long time, it will cause a large amount of mold to grow on the surface of the willow product, which will intensify the corrosion of the willow product, making it unusable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] A preparation method of N-methylolacrylamide composite water-based acrylic paint for wicker, comprising:

[0030] (1) Gel resin preparation:

[0031] Add itaconic acid to the reaction kettle, then feed nitrogen into the reaction kettle, discharge the air in the reaction kettle, then add sodium hydroxide solution, stir for 30 minutes, and then add N-methylolacrylamide and N, N-methylenebisacrylamide, initiator, heated to 30°C, stirred at 500r / min for 2 hours, then heated to 50-60°C, kept for 10-12 hours, filtered, washed until neutral, dried Afterwards, obtain gel resin;

[0032] Itaconic acid: The scientific name is methylene succinic acid, methylene succinic acid, which is an unsaturated dibasic organic acid. It contains unsaturated double bonds, has active chemical properties, can carry out polymerization between itself, and can also be polymerized with other monomers such as acrylonitrile, slightly soluble in benzene, chloroform, ether, petroleum ether, carbon disu...

Embodiment 1

[0079] A preparation method of N-methylolacrylamide composite water-based acrylic paint for wicker, comprising:

[0080] (1) Gel resin preparation:

[0081] Add itaconic acid to the reaction kettle, then feed nitrogen into the reaction kettle, discharge the air in the reaction kettle, then add sodium hydroxide solution, stir for 30 minutes, and then add N-methylolacrylamide and N, N-methylenebisacrylamide and initiator, heated to 30°C, stirred at 500r / min for 2 hours, then heated to 50°C, kept for 10 hours, filtered, washed until neutral, and dried to obtain a condensate Glue resin; The sodium hydroxide mol ratio in described itaconic acid and sodium hydroxide solution is 3:1. The weight ratio of N-methylolacrylamide, N,N-methylenebisacrylamide, initiator and itaconic acid is 3:1:0.8:50. The initiator is ammonium persulfate.

[0082] (2) Castor oil-based complex:

[0083] Dissolve ricinoleic acid in an organic solvent to obtain a ricinoleic acid solution, heat to 110°C, ke...

Embodiment 2

[0087] A preparation method of N-methylolacrylamide composite water-based acrylic paint for wicker, comprising:

[0088] (1) Gel resin preparation:

[0089] Add itaconic acid to the reaction kettle, then feed nitrogen into the reaction kettle, discharge the air in the reaction kettle, then add sodium hydroxide solution, stir for 30 minutes, and then add N-methylolacrylamide and N, N-methylenebisacrylamide and initiator, heated to 30°C, stirred at 500r / min for 2 hours, then heated to 60°C, kept warm for 12 hours, filtered, washed until neutral, and dried to obtain a condensate Glue resin; The sodium hydroxide mol ratio in described itaconic acid and sodium hydroxide solution is 3:1. The weight ratio of N-methylolacrylamide, N,N-methylenebisacrylamide, initiator and itaconic acid is 5:1.6:0.9:50. The initiator is ammonium persulfate.

[0090] (2) Castor oil-based complex:

[0091] Dissolve ricinoleic acid in an organic solvent to obtain a ricinoleic acid solution, heat to 11...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of an N-hydroxymethyl acrylamide composite water-based acrylic coating for wickerwork, and belongs to the field of artcraft. The preparation method comprises the following steps: (1) gel resin preparing; (2) a castor oil-based compound; (3) raw material mixing. The coating prepared through the method has excellent adhesive force and impact resistance, the coating is brushed on the surface of the wickerwork, the bonding performance of the formed coating and the surface of the wickerwork is better, the bonding force between the coating and the wickerwork can be greatly improved through the promotion effect of the gel resin, and the adhesive force is greatly increased.

Description

technical field [0001] The invention belongs to the technical field of handicrafts, in particular to a preparation method of N-methylolacrylamide composite water-based acrylic paint for wicker. Background technique [0002] Willow is highly adaptable to the environment. It grows all over the country. Different regions breed different weaving cultures. People get inspiration from wicker straw hats for shade and develop richer weaving skills. There are many types of willows, and the ones that can be used for weaving mainly include: Salix salix, Chinese bark willow, dry willow, small red willow, soap willow, weeping willow, Artemisia willow, etc. The growth cycle of willow is short, usually it can be used as raw materials in one year, and the rate of finished products is extremely high, the supply of raw materials is sufficient, and it is convenient to obtain materials. Willow products are common containers and handicrafts in people's lives. Baskets, baskets, dustpans, buckets...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/65C09D7/61C08F222/02C08F220/58C08F222/38
CPCC08F222/02C08K2003/2241C08K2201/011C08L2205/03C09D133/04C09D7/61C09D7/65C08F220/58C08F222/385C08L67/06C08L35/00C08K7/26C08K3/22
Inventor 徐治合徐蓝天徐艳云
Owner 安徽三和工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap