Carbon fiber bundle for winding forming and preparation method and application thereof

A technology of winding and forming carbon fiber bundles, which is applied in the field of carbon fibers to achieve high strength conversion rate, high degree of uniformity, and good thickness uniformity

Active Publication Date: 2020-12-08
HENGSHEN
View PDF13 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, for the research on the influence of other states of carbon fiber bundles except strength on their conversion rate, no literature has clearly pointed out that

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon fiber bundle for winding forming and preparation method and application thereof
  • Carbon fiber bundle for winding forming and preparation method and application thereof
  • Carbon fiber bundle for winding forming and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0087] In the second aspect, the embodiment of the present invention provides a preparation method corresponding to the above-mentioned carbon fiber bundle for winding molding, including: soaking the pretreated carbon fiber bundle in a sizing agent for sizing, followed by drying at 125-145°C for 20-30s, and sizing to The fiber bundle tension in the drying process is controlled at 8-60mN / tex. Specifically include the following steps:

[0088] S1. Pretreating the fibers.

[0089] The fibers in the present application are polyacrylonitrile-based carbon fibers, pitch-based carbon fibers or viscose-based carbon fibers; ) is most suitable. The PAN-based carbon fiber here refers to the copolymer obtained by copolymerizing acrylonitrile as the main monomer with vinyl monomers such as itaconic acid, acrylic acid, and methyl acrylate in a molar ratio of less than 10% as a raw material, and is first prepared into PAN Raw silk, and then through a series of processes to obtain carbon fi...

Embodiment 1-6

[0103] Embodiment 1-6 provides a kind of carbon fiber bundle for winding molding, and its preparation method is as follows:

[0104] Use the PAN raw silk produced by Jiangsu Hengshen Company, carry out pre-oxidation treatment at 200-300°C in an air atmosphere; carry out carbonization treatment at a maximum temperature of 1350°C in a nitrogen atmosphere; Under the condition of surface anodic oxidation treatment, unsized HF30s carbon fiber (12000 single filaments, circular cross section, surface roughness Ra=39) without sizing is obtained, and it is continuously passed through the sizing agent bath (emulsion concentration 3%), After impregnation, heat rollers were used for contact drying. The surface temperature and drying time of the heat rollers and the tension during sizing and drying were shown in Table 1. The moisture in the fiber bundles was removed to obtain carbon fiber bundle products.

[0105] The components of the sizing agent include 20wt% of resin, 8wt% of emulsifie...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carbon fiber bundle for winding forming and a preparation method and application thereof, and relates to the technical field of carbon fibers. The carbon fiber bundle for winding molding has a K value defined by the following formula of 6.5-8.5; K is equal to L / D, wherein L is the breadth of the fiber bundle, the unit is mm, and L is 5.5mm-6mm; and D is the linear densityof the fiber bundle, and the unit is g / m. The preparation method comprises the following steps that pretreated fibers are put into a sizing agent for dipping and sizing, then drying is carried out for 20-30 seconds at 125-145 DEG C, and the fiber bundle tension is controlled in the process from sizing to drying to be 8-60 mN / tex. By limiting the ratio of the breadth to the linear density of the fiber bundle, the relative breadth is limited, it can be guaranteed that the cellulose impregnation uniformity degree is high, and the thickness uniformity of a formed body is good, so that the carbonfiber bundle is closely arranged on a mandrel, no gap is generated, resin impregnation can be rapidly conducted, and the high strength conversion rate is achieved.

Description

technical field [0001] The invention relates to the technical field of carbon fibers, in particular to a carbon fiber bundle for winding and forming, a preparation method and application thereof. Background technique [0002] Compared with other reinforcing fibers, carbon fiber has the characteristics of high strength, high modulus, and light weight. With the increase in carbon fiber production and the decline in cost in recent years, its application range has ranged from the initial aerospace field and high-end sports and entertainment fields. Rapidly expanded to automotive applications, wind power energy, pressure vessels, and building reinforcement in many industrial fields. Especially in recent years, with the policy tendency of countries around the world on new energy vehicles, in the field of pressure vessels, as gas storage tanks for new energy vehicle fuels such as natural gas and hydrogen, due to the high strength and light weight requirements for products, carbon f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06B3/02D06B15/00D06B23/02D06M15/55D06M15/564D06M15/53D06M13/224D06M101/40
CPCD06B3/02D06B15/00D06B23/028D06M15/55D06M15/564D06M15/53D06M13/224D06M2101/40D06M2200/40D06M13/17B29C53/582B29C53/602B29C70/10B29B15/08B29C70/32