High-moisture mask based on cellulose fibers
A cellulose fiber, wet face technology, applied in skin care preparations, cosmetics, cosmetic preparations, etc., can solve the problems of the moisturizing effect of moisturizing mask can not meet our needs, the skin is easy to age, etc., to improve the moisturizing effect, The effect of promoting the excretion of supply and waste, and improving the antibacterial and moisturizing properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0046] S1: Prepare materials
[0047] S2: Preparation of mask base fabric:
[0048] Take sodium alginate, dissolve in distilled water, stir for 10 minutes, let stand for 3 hours, continue to stir for 4 hours, filter, defoam under vacuum, the vacuum defoaming time is 15 hours, and obtain spinning solution; take spinning solution, carry out wet spinning, and Enter the calcium chloride coagulation bath for 30 minutes, wash with water, draw and dry to obtain the first fiber; take chitosan fiber, viscose fiber, silk fiber and the first fiber, lay the net after carding, and spunlace reinforcement to obtain the mask base fabric ;
[0049] S3: Preparation of antimicrobial peptides:
[0050] Take the pepper seed protein, dissolve it in distilled water, put it in a water bath and heat it to 30°C, then add pepsin, react for 3 hours, heat up to 90°C in a water bath to inactivate the enzyme, cool, centrifuge at 8000r / min for 10min, take the supernatant, and adjust pH to neutral, vacuum ...
Embodiment 2
[0059] S1: Prepare materials
[0060] S2: Preparation of mask base fabric:
[0061] Take sodium alginate, dissolve in distilled water, stir for 15 minutes, let stand for 3.2 hours, continue to stir for 4.1 hours, filter, defoam under vacuum, the vacuum defoaming time is 17 hours, and obtain spinning solution; take spinning solution, and carry out wet spinning , and enter the calcium chloride coagulation bath for 35min, wash with water, draw and dry to obtain the first fiber; take chitosan fiber, viscose fiber, silk fiber and the first fiber, lay the net after carding, and spunlace reinforcement to obtain the mask fabric;
[0062] S3: Preparation of antimicrobial peptides:
[0063] Take Zanthoxylum bungeanum protein, dissolve it in distilled water, heat it in a water bath to 32°C, then add pepsin, react for 3.2 hours, heat up to 90°C in a water bath to inactivate the enzyme, cool, centrifuge at 8200r / min for 13min, take the supernatant, and then Adjust the pH to neutral, and...
Embodiment 3
[0072] S1: Prepare materials
[0073] S2: Preparation of mask base fabric:
[0074] Take sodium alginate, dissolve in distilled water, stir for 20min, let stand for 3.5h, continue to stir for 4.2h, filter, defoam under vacuum, the vacuum defoaming time is 18h, and obtain spinning solution; take spinning solution, and carry out wet spinning , and enter the calcium chloride coagulation bath for 40min, wash with water, draw and dry to obtain the first fiber; take chitosan fiber, viscose fiber, silk fiber and the first fiber, lay the net after carding, and spunlace reinforcement to obtain the mask fabric;
[0075] S3: Preparation of antimicrobial peptides:
[0076] Take Zanthoxylum bungeanum protein, dissolve it in distilled water, heat it in a water bath to 35°C, then add pepsin, react for 3.5 hours, heat up to 90°C in a water bath to inactivate the enzyme, cool, centrifuge at 8500r / min for 15min, take the supernatant, and then Adjust the pH to neutral, and vacuum freeze-dry t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com