Carboxyl-terminated liquid fluororubber/acrylate rubber blended elastomer and preparation method thereof

A technology of liquid fluororubber and acrylate, which is applied in the field of rubber materials and can solve problems such as mechanical properties that need to be improved

Active Publication Date: 2021-02-26
BEIJING UNIV OF CHEM TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its mechanical properties still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carboxyl-terminated liquid fluororubber/acrylate rubber blended elastomer and preparation method thereof
  • Carboxyl-terminated liquid fluororubber/acrylate rubber blended elastomer and preparation method thereof
  • Carboxyl-terminated liquid fluororubber/acrylate rubber blended elastomer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0085] Prepare the liquid fluororubber / acrylate rubber blended elastomer of the present invention according to the following raw material formula and steps, including the following raw material components by mass:

[0086] Acrylic rubber 95 parts

[0087] Carboxyl-terminated liquid fluororubber 5 parts

[0088] SA 1 copy

[0089] Carbon black N550 30 parts

[0090] Talc powder 10 parts

[0091] TCY 1

[0092] Accelerator BZ 2 parts

[0093] Zirconia 2 parts

[0094] 3 parts calcium carbonate

[0095] Anti-scorch agent CTP 0.5 parts

[0096] The preparation process is as follows:

[0097] (1) Preparation of 2.5% liquid fluororubber

[0098] Take 250g of vinylidene fluoride-hexafluoropropylene solid copolymer (number average molecular weight Mn=40w, weight average molecular weight Mw=45w) and dissolve it in 784g of acetone for 12h. Weigh 120g of hydrogen peroxide solution with a mass concentration of 30%, and 60g of potassium hydroxide, and dissolve them in 73mL of wat...

Embodiment 2

[0105] Prepare the liquid fluororubber / acrylate rubber blended elastomer of the present invention according to the following raw material formula and steps, including the following raw material components by mass:

[0106] Acrylic rubber 90 parts

[0107] Carboxyl-terminated liquid fluororubber 10 parts

[0108] Fumed white carbon black 40 parts

[0109] clay 10 parts

[0110] SA 1 copy

[0111] TCY 1

[0112] Accelerator BZ 2 parts

[0113] Titanium oxide 4 parts

[0114] 1 part magnesium carbonate

[0115] Anti-scorch agent CTP 0.5 part

[0116] The preparation process is as follows:

[0117] (1) Preparation of 3% liquid fluororubber

[0118] Take 250g of vinylidene fluoride-hexafluoropropylene solid copolymer (number average molecular weight Mn=40w, weight average molecular weight Mw=45w) and dissolve it in 784g of acetone for 12h. Weigh 150g of hydrogen peroxide solution with a mass concentration of 30%, and 80g of potassium hydroxide, and dissolve them in 98mL o...

Embodiment 3

[0124] Prepare the liquid fluororubber / acrylate rubber blended elastomer of the present invention according to the following raw material formula and steps, including the following raw material components by mass:

[0125] Acrylic rubber 85 parts

[0126] Carboxyl-terminated liquid fluororubber 15 parts

[0127] Carbon black N330 50 parts

[0128] SA 1 copy

[0129] TCY 1

[0130] Accelerator BZ 2 parts

[0131] Zinc oxide 2 parts

[0132] 3 parts sodium carbonate

[0133] Anti-scorch agent CTP 0.5 parts

[0134] The preparation process is as follows:

[0135] (1) Preparation of 3.5% liquid fluororubber

[0136] Take 250g of vinylidene fluoride-hexafluoropropylene solid copolymer (number average molecular weight Mn=40w, weight average molecular weight Mw=45w,) and dissolve it in 784g of acetone for 12h. Weigh 170g of hydrogen peroxide solution with a mass concentration of 30%, and 100g of potassium hydroxide, and dissolve them in 122mL of water. Add hydrogen peroxide ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a carboxyl-terminated liquid fluororubber / acrylate rubber blended elastomer, which is mainly prepared from the following raw materials in parts by weight: 5-100 parts of acrylate rubber, 5-100 parts of carboxyl-terminated liquid fluororubber and 1-10 parts of a curing agent. The raw materials also comprise a reinforcing filler, a vulcanizing agent and a vulcanizing aid; preferably, the use amount of the reinforcing filler is 10-70 parts, the use amount of the vulcanizing agent is 1-9 parts, the use amount of the vulcanizing aid is 1-9 parts, and preferably, the use amount is metered based on 100 parts of the total amount of the acrylate rubber and the carboxyl-terminated liquid fluororubber. According to the carboxyl-terminated liquid fluororubber / acrylate rubber blended elastomer material provided by the invention, carboxyl-terminated groups and a curing agent form ionic crosslinking, so that the material is endowed with a double-crosslinking structure and hasa reinforcing effect, and particularly, the hardness and strength of the carboxyl-terminated liquid fluororubber / acrylate rubber blended elastomer material are obviously improved at the same time; the compression set is reduced, and the comprehensive performance is good.

Description

technical field [0001] The invention belongs to the field of rubber materials, in particular to a liquid fluororubber / acrylate rubber blended elastic body, in particular to a carboxyl-terminated liquid fluororubber / acrylate rubber blended elastic body material and a preparation method thereof. Background technique [0002] Acrylate rubber (ACM) is a special synthetic rubber based on alkyl acrylate as the main monomer. The saturated main chain structure and the existence of polar ester groups make acrylate rubber have good characteristics such as high temperature resistance, oil resistance, and aging resistance. , widely used in hot oil environment, especially used as oil seal material in the automobile industry, known as automobile glue. At the same time, ACM also has problems such as insufficient temperature resistance, low strength, and large compression permanent deformation. With the development of the automobile industry, there are higher requirements for the temperatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/16C08L27/16C08K13/02C08K3/04C08K3/34C08K3/22C08K3/26C08K5/43C08K3/36C08K13/04C08K7/26
CPCC08L33/16C08K2003/265C08K2003/2244C08K2003/2241C08K2003/267C08K2003/2206C08L2201/08C08L27/16C08K13/02C08K3/04C08K3/34C08K3/22C08K3/26C08K5/43C08K3/36C08K13/04C08K7/26
Inventor 刘力傅家森
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com