Waterproof mortar as well as preparation method and application thereof

A technology of waterproof mortar and water reducing agent, which is applied in the field of waterproof mortar and its preparation, can solve the problems of reduced compressive/flexural strength and viscosity, high bleeding volume, long setting time, etc., and achieves strong scratch resistance and bleeding volume Low, high compressive and flexural strength effects

Active Publication Date: 2021-04-09
FUJIAN KZJ NEW MATERIALS CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Based on this, it is necessary to provide a waterproof mortar, which aims to solve the technical problems of the waterproof mortar using recycled materials in the prior art with reduced compressive / flexural strength and viscosity, high bleeding and long setting time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof mortar as well as preparation method and application thereof
  • Waterproof mortar as well as preparation method and application thereof
  • Waterproof mortar as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0092] The present invention also provides the preparation method of the above-mentioned waterproof mortar, mixing and stirring the liquid material component and the powder material component evenly; wherein,

[0093] Liquid feed components include:

[0094] Styrene-acrylate copolymer emulsion: 20-50 parts;

[0095] Vinyl acetate-ethylene copolymer emulsion: 10-40 parts;

[0096] Workability improver: 10-20 parts;

[0097] Film-forming aids: 1 to 5 parts;

[0098] Defoamer: 0.3~0.9 parts;

[0099] Water: 15-60 parts;

[0100] Powder components include:

[0101] Portland cement: 10-40 parts;

[0102] Aluminate cement: 5-40 parts;

[0103] Gypsum: 5 to 17 parts;

[0104] Glass sand: 25-50 parts;

[0105] Glass powder: 5 to 15 parts;

[0106] Water reducing agent: 0.1~0.5 parts;

[0107] Stabilizer: 0.05 to 0.3 parts;

[0108] Coagulant regulator: 0.05 to 0.5 parts;

[0109] Fiber: 0.1 to 1 part.

[0110] The preparation method of the waterproof mortar in the presen...

Embodiment 1

[0117] Prepare the liquid component and the powder component of the waterproof mortar in the following proportions, wherein,

[0118] Liquid material components: 500g styrene-acrylate copolymer emulsion, 100g vinyl acetate-ethylene copolymer emulsion, 100g polyacrylic acid sodium salt derivative, 5g triterpenoid compound, 50g propylene glycol butyl ether, 9g polysiloxane organic matter, water 236g;

[0119] Powder components: ordinary portland cement 150g, aluminate cement 300g, gypsum 80g, granulated blast furnace slag powder 30g, (70-140) mesh glass sand 280g, 200 mesh glass powder 120g, calcite powder 40g, naphthalene series Water reducing agent 4g, higher fatty acid 5g, hydroxypropyl methylcellulose (8000 viscosity) 0.7g, Brunei gum 0.3g, potassium silicate 0.3g, crystal nucleus nano-reinforcer 0.3g, sodium gluconate 0.1g, basalt Mineral fiber 1g, polypropylene fiber 1.5g;

[0120] Take 500g of the liquid component and 1000g of the powder component and mix them evenly to...

Embodiment 2

[0122] Prepare the liquid component and the powder component of the waterproof mortar in the following proportions, wherein,

[0123] Liquid material components: 450g styrene-acrylate copolymer emulsion, 120g vinyl acetate-ethylene copolymer emulsion, 130g polyacrylic acid sodium salt derivative, 6g triterpenoid compound, 40g propylene glycol butyl ether, 8g polysiloxane organic matter, water 246g;

[0124] Powder components: ordinary Portland cement 200g, aluminate cement 250g, gypsum 70g, granulated blast furnace slag powder 40g, (70~140) mesh glass sand 300g, 200 mesh glass powder 100g, calcite powder 40g, naphthalene series Water reducer 4g, zinc stearate 5g, hydroxypropyl methylcellulose (8000 viscosity) 0.7g, Brunei gum 0.3g, potassium silicate 0.2g, crystal nucleus nano-strengthener 0.3g, sodium hexametaphosphate 0.2 g, basalt mineral fiber 1g, polypropylene fiber 1.5g;

[0125] Take 400g of the liquid component and 1000g of the powder component and mix them evenly to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to waterproof mortar which comprises a liquid component and a powder component. The liquid component comprises the following components in parts by weight: 20 to 50 parts of styrene-acrylate copolymer emulsion; 10 to 40 parts of vinyl acetate-vinyl copolymer emulsion; 10 to 20 parts of a workability improver; 1 to 5 parts of coalescing agent; 0.3 to 0.9 part of a defoaming agent; and 15 to 60 parts of water. The powder component comprises 10 to 40 parts of ordinary Portland cement; 5 to 40 parts of aluminate cement; 5 to 17 parts of gypsum; 25 to 50 parts of glass sand; 5 to 15 parts of glass powder; 0.1 to 0.5 part of a water reducing agent; 0.05 to 0.3 part of a stabilizing agent; 0.05 to 0.5 part of a thickening time control agent; and 0.1 to 1 part of fibers. The waterproof mortar disclosed by the invention simultaneously has the properties of higher mortar cohesiveness, proper setting time, higher compression strength and breaking strength, low bleeding amount, uniform appearance, no precipitate and strong scratch resistance, and in addition, the waterproof mortar disclosed by the invention has better construction performance at different external environment temperatures.

Description

technical field [0001] The invention relates to the technical field of polymer cement-based materials, in particular to a waterproof mortar and a preparation method thereof. Background technique [0002] At present, with the development of polymer cement-based materials, polymer cement waterproof mortar has been widely used in many projects. Polymer cement waterproof mortar has strong adhesion, excellent waterproof, impermeability and crack resistance, convenient and fast construction, and flatness. Good and many other advantages, with the gradual application of various recycled materials, the research on the product formula of related polymer cement waterproof mortar is gradually deepening, but currently on the market, all kinds of polymer cement waterproof mortar using recycled materials still have compression resistance. / The problems of reduced flexural strength and viscosity, high bleeding and long setting time limit the further application of polymer cement waterproof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B111/27
CPCC04B28/14C04B2111/27C04B2201/50C04B24/2641C04B24/2623C04B24/00C04B24/023C04B24/42C04B7/02C04B7/32C04B18/141C04B14/22C04B14/28C04B2103/302C04B24/085C04B24/383C04B24/38C04B12/04C04B24/10C04B14/4656C04B16/0633C04B2103/0068C04B22/16C04B22/126C04B24/06
Inventor 陈周鹏邱岳涛胡俊华王永定苏伟东温宾煌
Owner FUJIAN KZJ NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com