Polyester cotton sizing aid and preparation method thereof

A technology of sizing auxiliaries and polyester-cotton, applied in the field of polyester-cotton sizing auxiliaries and preparation, to achieve the effects of protecting the environment, stabilizing the performance of the auxiliaries, and improving brittleness and hardness

Pending Publication Date: 2021-04-13
上海新齐力助剂科技有限公司 +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above-mentioned deficiencies in the current technology, the present invention provides a polyester-cotton sizing aid and a preparation method with lower cost, stronger adhesion of the size, stable viscosity of the size, and flexibility of the size film, and a preparation method, which can overcome the sizing of existing polyester-cotton varieties. slurry defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027]6.0 kg of ethylene glycol, 1.5kg PEG400, 1kg sorbitol fatty acid ester polyoxyethylene ether T80, 1 kg fatty alcohol polyoxyethylene ether (HLB value at 13), 0.75 kg of fatty alcohol ether phosphate salt, 3.5kg isomeric alcohol polyoxyethylene ether, in turn, in a stirred water, gradually heating and thoroughly stirred, reacted at 65 ° C for 55min, then add 5 wt% sodium carbonate solution (in the present invention, sodium carbonate solution, However, in practical applications, the sodium carbonate solution is not limited to the pH of 7.0, and 0.05 kg of silicone defoaming agent and 0.05 kg of sorbate preservatives were added, and finally 50 kg of polyester coaperidaid.

[0028]7kg of the polyester cotton upper slurry additive to 112.5 kg of corn starch was cooked in a polyester cotton variety 75 "T / C 65 / 35 21S * 16S + 70D 85 * 58 2 / 1 trial, trial Information is shown in Table 1.

[0029]Table 1 75 "T / C 65 / 35 21S * 16S + 70D 85 * 58 2 / 1

[0030] Original formula Weight (kg) new f...

Embodiment 2

[0033]5.0kg of ethylene glycol and 3.5kg PEG6000, 1.25kg sorbitan fatty acid ester polyoxyethylene ether T40, 1.25 kg fat alcohol polyoxyethylene ether (HLB value at 16), 1.25 kg fatty alcohol ether phosphate Salt, 1.5 kg of secondary alkyl sulfonate, sequentially put it in the stirred water, gradually heating and stirring, at 61 ° C for 60 min, then 5 wt% sodium carbonate solution (sodium carbonate in this practice) However, in practice, the actual application is not limited to the sodium carbonate solution. The pH is 7.1, and the 0.12 kg of polyether antifoaming agent, 0.1 kg nitrite preservative and 0.1 kg of isothiazolin antifurer is stirred, and finally obtained 50 kg of polyester coat berry aid.

[0034]8 kg of the polyester coat, 25 kg denaturation starch, 100 kg corn starch, 50 kg of polyacrylic chemical slurry, 25 kg of polyacrylic chemical slurry, is carried out in the polyester cotton seed 64 "T / C 65 / 35 45s 128 * 68 Trial 2 / 1 + 1 / 2, trial data is shown in Table 2.

[0035]Tab...

Embodiment 3

[0039]6.5kg ethylene glycol, 0.75 kg PEG300 and 1.75KG PEG12000, 0.75 kg sorbitan fatty acid ester polyoxyethylene ether T60, 0.75 kg fatty alcohol polyoxyethylene ether (HLB value at 15), 0.75 kg The phosphate ester salt, 1.0 kg of sodium secondary alkyl sulfonate and 1.5 kg isomeric alcohol polyoxyethylene ether, sequentially put into the stirred water, gradually heating and stirring, reacted at 70 ° C for 45min, then added 5% by weight The sodium carbonate solution (in the present invention is a sodium carbonate solution, but the actual application is not limited to the sodium carbonate solution) to the pH of 6.8, then add 0.14 kg of polyether defoamer and 0.25 kg isothiazolinone anti-corrosion The agent was stirred and finally obtained 50 kg of polyester coaramophotoid.

[0040]The polyester cotton upper slurry aid, 25 kg denaturation starch, 100 kg corn starch obtained by 6kg this embodiment, 37.5 kg of polyacrylic chemical slurry, was carried out after cooking slurry 74 "T / C 80...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyester cotton sizing aid and a preparation method thereof. The polyester cotton sizing aid comprises the following raw materials in percentage by weight: 10.00-15.00 wt% of ethylene glycol, 3.00-8.00 wt% of polyethylene glycol (PEG), 1.50-3.00 wt% of sorbitan fatty acid ester polyoxyethylene ether, 1.50-3.00 wt% of fatty alcohol-polyoxyethylene ether, 0.80-2.50 wt% of antistatic agent, 3.0-7.0 wt% of degreasing agent, 0.05-0.3 wt% of defoamer, 0.1-0.5 wt% of preservative and the balance of water. The preparation method comprises the following steps: sequentially adding the ethylene glycol, polyethylene glycol (PEG), sorbitan fatty acid ester polyoxyethylene ether, fatty alcohol-polyoxyethylene ether, the antistatic agent and the degreasing agent into water which is being stirred; heating and fully stirring; adjusting the pH value to be neutral; and adding the defoamer and the preservative. The cost is lower, the adhesive force of the sizing agent is stronger, the viscosity of the sizing agent is stable, and a sizing film is flexible and excellent in performance.

Description

Technical field[0001]The present invention relates to the field of textile depassing, and more particularly to a polyester coil aid and a method of preparation.Background technique[0002]At present, PVA, starch, polyacrylic acid is three large slurrys on the slurry. During the surface of natural fibers such as cotton, since the fiber structure is rich in a large amount of hydroxyl group, similarity to the slurry structure such as starch, acrylic, auxiliary agent, is easy to form hydrogen bonds and better compatibility. It greatly enhances the affinity and adhesion between fibers and slurry, which has completely realized no PVA overlooking, or even low cost without PVA depassry.[0003]However, in the polyester, PVA is still the best choice of the upper paste material, which brings severe challenges and pressure to the downstream printing and dyeing enterprises. At the same time, my country's polyester and polyester blend products have ranked first in the world. Exports to foreign count...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/53D06M13/148D06M13/292D06M13/256D06M15/11D06M15/263D06M101/06
CPCD06M15/53D06M13/148D06M13/292D06M13/256D06M15/11D06M15/263D06M2101/06D06M2200/40
Inventor 路彦景江生元王雪芳
Owner 上海新齐力助剂科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products