Precursor for lithium-ion battery with double-layer structure, positive electrode material and preparation method

A lithium-ion battery and double-layer structure technology, which is applied to battery electrodes, structural parts, secondary batteries, etc., can solve the problems of reducing material tap density and unfavorable material compaction density, so as to improve stability and improve cycle stability performance, such as the effect of capacity and rate performance

Active Publication Date: 2022-01-11
JINGMEN GEM NEW MATERIAL
View PDF21 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the internal packing is loose, certain pores will appear inside, which will reduce the tap density of the material, which is not conducive to improving the compacted density of the material. Therefore, in order to increase the compacted density of the material, when preparing the material, it should be within a certain Improve the packing density inside the material particles to a certain extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Precursor for lithium-ion battery with double-layer structure, positive electrode material and preparation method
  • Precursor for lithium-ion battery with double-layer structure, positive electrode material and preparation method
  • Precursor for lithium-ion battery with double-layer structure, positive electrode material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method of the precursor for the lithium-ion battery of double-layer structure comprises the following steps:

[0027] (1) Mix soluble nickel salt, soluble cobalt salt, soluble manganese salt, and soluble M salt corresponding to doping element M according to the ratio of molar ratio Ni: Co: Mn: M to x: y: (1-x-y-a): a , to obtain the first mixed salt solution, wherein, 0.3

[0028] (2) Mix ...

Embodiment 1

[0034] Mix the mixed solution of nickel sulfate and nickel nitrate, the mixed solution of cobalt sulfate and cobalt nitrate, the mixed solution of manganese nitrate and manganese sulfate, magnesium sulfate, Fully mixed with the mixed solution of magnesium nitrate to prepare the first mixed salt solution with a total concentration of metal ions of 3 mol / L.

[0035] Fully mix nickel sulfate, cobalt sulfate, manganese sulfate and zirconium sulfate solutions according to the ratio of molar ratio Ni:Co:Mn:Zr of 0.8:0.1:0.05:0.05 to make the second mixture with a total concentration of metal ions of 3mol / L saline solution.

[0036] Under the protection of an inert gas, the first mixed salt solution, the sodium hydroxide solution with a concentration of 5mol / L, and the ammonia water with a concentration of 8mol / L were respectively added to the reaction kettle containing the bottom liquid through a metering pump. The flow rate that the solution is added into the reaction kettle conta...

Embodiment 2

[0041] Fully mix nickel sulfate, cobalt sulfate, manganese sulfate, and titanium sulfate solutions according to the molar ratio Ni: Co: Mn: Ti of 0.9: 0.03: 0.02: 0.05 to make the first solution with a total concentration of metal ions of 1mol / L. Mix the salt solution.

[0042] Mix the mixed solution of nickel sulfate and nickel nitrate, the mixed solution of cobalt sulfate and cobalt nitrate, manganese nitrate and manganese sulfate according to the ratio of molar ratio Ni: Co: Mn: W: Al 0.9: 0.03: 0.02: 0.025: 0.025 solution, a mixed solution of tungsten sulfate and tungsten nitrate, and a mixed solution of aluminum sulfate and aluminum nitrate are thoroughly mixed to prepare a second mixed salt solution with a total concentration of metal ions of 1 mol / L.

[0043] Under the protection of an inert gas, the first mixed salt solution, the sodium hydroxide solution with a concentration of 3mol / L, and the ammonia water with a concentration of 6mol / L were respectively added to the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a double-layer structure lithium ion battery precursor, positive electrode material and preparation method. By using different reaction conditions, the invention prepares a product in which primary particles are tightly packed inside and loosely packed outside. The inner close packing ensures the tap density of the particles, while the loose outer part can exert better specific capacity and rate performance, which is beneficial to improve the specific capacity, rate performance and energy density of the material at the same time; Doping with different elements can improve the internal rate performance and external cycle stability of the material at the same time; choose to directly add doping elements during the co-precipitation reaction, so that the doping elements can be uniformly distributed in the surface layer of the precursor particles at the atomic level , give full play to the role of doping modification. Using different structures inside and outside the particles and using different doping elements can effectively improve the comprehensive properties of the layered ternary material.

Description

technical field [0001] The invention belongs to the field of lithium battery materials, and in particular relates to a double-layer structure lithium ion battery precursor, positive electrode material and preparation method. Background technique [0002] Lithium-ion batteries (LIBs) have been widely used in portable electronics, electric vehicles, and energy storage systems due to their many advantages such as high energy density, low self-discharge, no memory effect, long cycle life, and low environmental pollution. In the current lithium-ion battery technology, the cathode material is the key component of the lithium-ion battery. It not only participates in the electrochemical reaction as an electrode material, but also acts as a lithium ion source, which largely determines the safety and performance of the battery. , cost and lifetime. [0003] Among the commonly used cathode materials for lithium-ion batteries, ternary materials have become a research hotspot in recent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/485H01M4/505H01M4/525H01M10/0525C01G53/00C01B35/12
CPCH01M4/366H01M4/485H01M4/505H01M4/525H01M10/0525C01G53/006C01G53/50C01B35/128C01P2004/80C01P2006/40C01P2004/61Y02E60/10
Inventor 许开华张坤陈康李聪杨幸薛晓斐黎俊孙海波范亮姣
Owner JINGMEN GEM NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap