A method for hot-pressing preparation and performance testing of heterogeneous metal composite block materials

A technology of heterogeneous metals and testing methods, which is applied in the preparation of test samples, testing the strength of materials by applying stable tension/compression, and testing the strength of materials by applying stable shear force. Process parameters cannot be accurately controlled, etc., to achieve the effect of short test period, rapid preparation and accurate control

Active Publication Date: 2022-05-17
YANSHAN UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem to be solved in the present invention is to provide a method for hot-pressing preparation and performance testing of heterogeneous metal composite blocks, that is, to realize hot-pressing process parameters such as heating rate, reduction amount, hot-pressing temperature, holding time, and cooling rate. Accurate control, so as to study the influence of various parameters on the formability of the composite plate and the interface reaction layer, and explore the production process that meets the production requirements; it can solve the problem that the process parameters of the existing metal composite plate preparation process cannot be accurately controlled and affect the performance of the composite interface question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for hot-pressing preparation and performance testing of heterogeneous metal composite block materials
  • A method for hot-pressing preparation and performance testing of heterogeneous metal composite block materials
  • A method for hot-pressing preparation and performance testing of heterogeneous metal composite block materials

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] Such as figure 1 , 2 As shown, a method for preparing a heterogeneous metal composite bulk material by hot pressing for testing, comprising the following steps:

[0048] Step 1, surface treatment: sand and polish the surfaces of the metal A bar 6, the metal B sleeve 3 with a circular step in the middle, the metal B bar 1 and the metal B bar 2 of the same size and size with sandpaper, and then Wipe clean with alcohol after cleaning with acetone;

[0049] The metal B sleeve 3 is the same metal as the bars of the metal B bar one 1 and the metal B bar two 2 .

[0050] The size of the metal A bar 6 matches the size of the circular step in the middle of the metal B sleeve 3; the diameters of the metal B bar one 1 and metal B bar two 2 match the metal B sleeve The inner diameter of the barrel 3 is matched.

[0051] Step 2, assemble the sample: place the metal A bar 6 on the circular step in the middle of the metal B sleeve 3, and then place the metal B bar 1 and the metal B ...

Embodiment

[0070] In this embodiment, two materials, TA2 and low-carbon steel with a C content of 0.18%, are selected for hot pressing.

[0071] The specific operation steps are as follows:

[0072] Step 1, surface treatment: use two low-carbon steel bars with a size of φ15×45mm, a low-carbon steel sleeve with a size of φ20×25 mm and a wall thickness of 2.5mm, and a TA2 bar with a size of φ12×5mm. Sand paper to polish, then clean with acetone and wipe clean with alcohol.

[0073] Step 2, assemble the sample: Assemble the TA2 bar stock at the circular step in the middle of the low-carbon steel sleeve, then assemble two low-carbon steel bars on both sides of the sleeve respectively, and the end faces are close to the two ends of the TA2 bar stock ; And the thermocouple wire is welded on the side of the TA2 bar stock through the sleeve through hole whose diameter φ is 2mm on the sleeve.

[0074] Step 3, isolation and anti-sticking: apply high-temperature lubricant to the other two ends of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hot-pressing preparation and performance testing method for a heterogeneous metal composite block test, which belongs to the technical field of heterogeneous metal composite material preparation. The hot-pressing preparation method includes surface treatment, assembling samples, isolation and anti-sticking, and hot pressing and cooling, to complete the preparation; the performance test method is an interface mechanical property test method, including a Z-direction tensile test method and a compressive shear test method. The present invention realizes the accurate control, fast preparation and performance detection of the hot pressing process of the composite material through the structural design of the metal material to be compounded, and the control of the hot pressing process parameters by the thermocouple wire, so as to study the effect of the process parameters on the heterogeneous The influence of the interface performance of the metal composite block can reduce the process window while ensuring the interface performance, and provide technical support for the industrial production of metal composite materials; and the device of the present invention has simple structure, convenient operation method, short test period and low test cost .

Description

technical field [0001] The invention relates to the technical field of preparation of heterogeneous metal composite materials, in particular to a method for hot-pressing preparation and performance testing of heterogeneous metal composite block materials for testing. Background technique [0002] With the development of the economy and the advancement of science and technology, metal materials are more and more widely used in more harsh and complex working environments, but a single metal material is difficult to meet the comprehensive performance requirements of people at this stage. Therefore, metal composite materials emerged as the times require and become an important direction of material research at the present stage. Metal composite materials have been widely used in bridges, railways, natural gas storage tanks, ships and many other industries. The use of composite materials not only reduces the cost of materials, but also meets the high comprehensive performance req...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N1/28G01N1/32G01N1/44G01N3/08G01N3/24
CPCG01N1/286G01N1/32G01N1/44G01N3/08G01N3/24G01N2001/2873G01N2203/0019G01N2203/0025G01N2203/0298
Inventor 王青峰杨啸雨郭凯高云哲吴炳南张栩源王秋鸣
Owner YANSHAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com