Silicon-containing polyimide anti-static antifouling coating as well as preparation method and application thereof

A technology of silicon polyimide and silicon polyimide resin, which is applied in the field of silicon-containing polyimide antistatic and antifouling coatings and its preparation, can solve pollution flashover, but cannot solve insulation equipment, antifouling To avoid problems such as poor flashing effect, achieve the effects of reducing maintenance costs, good water-repellent and oil-repellent effects, and improving weather resistance

Pending Publication Date: 2021-06-11
成都普利美特科技有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the above-mentioned deficiencies or defects, the purpose of the present invention is to provide a silicon-containing polyimide antistatic antifouling coating and its preparation method and application, which can effectively solve the poor antifouling flashover effect and inability of existing antifouling flashover coatings. Solve the problem of pollution flashover in insulation equipment from the root

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silicon-containing polyimide anti-static antifouling coating as well as preparation method and application thereof
  • Silicon-containing polyimide anti-static antifouling coating as well as preparation method and application thereof
  • Silicon-containing polyimide anti-static antifouling coating as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] This embodiment 1 provides a silicon-containing polyimide antistatic antifouling coating, including the following components by weight: 50 parts of silicon-containing polyimide resin, 5 parts of mica powder, 5 parts of talcum powder, and 3 parts of kaolin , 4 parts of magnesium hydroxide, 3 parts of antimony trioxide, 5 parts of pigment (a mixture of ethylene oxide and carbon black, the mass ratio of ethylene oxide and carbon black is 2:1), 1 part of silane coupling agent, 2 parts of aluminate coupling agent, 1.2 parts of organic tin laurate TMG216 catalyst, 0.8 parts of tin acetate TMG233 catalyst, 4 parts of silicone thinner X-13, 2 parts of nitro thinner X-102, diisopropyl peroxide 5 parts of benzene (DCP) crosslinking agent, 5 parts of benzoyl peroxide (BPO), 2.5 parts of acrylate thickener KM-60 and 1.5 parts of thickener KM-20.

[0041] The reaction equation and synthetic approach of silicon-containing polyimide resin in the present embodiment 1 are as follows:

...

Embodiment 2

[0056] This embodiment 2 provides a silicon-containing polyimide antistatic antifouling coating, including the following components by weight: 60 parts of silicon-containing polyimide resin, 5 parts of mica powder, 2 parts of talcum powder, and 3 parts of kaolin , 3 parts of magnesium hydroxide, 2 parts of antimony trioxide, 3 parts of pigment (a mixture of ethylene oxide and carbon black, the mass ratio of ethylene oxide and carbon black is 5:1), 1 part of silane coupling agent, 1 part of aluminate coupling agent, 1.5 parts of organic tin laurate TMG216 catalyst, 1.5 parts of tin acetate TMG233 catalyst, 4 parts of silicone thinner X-13, 4 parts of nitro thinner X-102, diisopropyl peroxide 1 part of benzene (DCP) crosslinking agent, 4 parts of benzoyl peroxide (BPO), 2 parts of acrylate thickener KM-60 and 2 parts of thickener KM-20.

[0057] The preparation method of the silicon-containing polyimide resin and the preparation method of the silicon-containing polyimide antista...

Embodiment 3

[0059] This embodiment 3 provides a silicon-containing polyimide antistatic antifouling coating, including the following components by weight: 55 parts of silicon-containing polyimide resin, 5 parts of mica powder, 5 parts of talcum powder, magnesium hydroxide 4 parts, 4 parts of antimony trioxide, pigment (a mixture of ethylene oxide and carbon black, the mass ratio of ethylene oxide and carbon black is 2:1) 5 parts, 1.4 parts of silane coupling agent, aluminate coupling agent 1.6 parts of joint agent, 1 part of organotin laurate TMG 216 catalyst, 1 part of tin acetate TMG233 catalyst, 4 parts of silicone thinner X-13, 3 parts of nitro thinner X-102, dicumyl peroxide (DCP ) 3.5 parts of crosslinking agent, 4 parts of benzoyl peroxide (BPO), 0.5 parts of acrylate thickener KM-6 and 2 parts of thickener KM-20.

[0060] The preparation method of the silicon-containing polyimide resin in Example 3 is the same as that in Example 1.

[0061] The difference between the preparation ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a silicon-containing polyimide antistatic antifouling coating and a preparation method and application thereof, and belongs to the technical field of coatings. The silicon-containing polyimide antistatic antifouling coating comprises the following components by weight: 45-60 parts of silicon-containing polyimide resin, 10-15 parts of a filler, 3-8 parts of a flame retardant, 2-6 parts of a pigment, 2-4 parts of a coupling agent, 1-5 parts of a catalyst, 5-10 parts of a diluent, 5-13 parts of a cross-linking agent and 1-5 parts of a thickener. The coating integrates the antifouling and antistatic characteristics, can be used on the surface of electric porcelain of electric insulation equipment such as an insulator, forms a compact coating layer after being cured, has excellent antifouling and antistatic effects, radically solves the pollution flashover phenomenon, effectively ensures smooth operation of a power grid, reduces the maintenance cost, and ensures normal power supply.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a silicon-containing polyimide antistatic and antifouling coating and its preparation method and application. Background technique [0002] The electric porcelain surface of the insulation equipment of the power system will inevitably occur in the natural environment, the adhesion of ice, snow and rain, and the long-term adhesion will destroy the insulation performance of the insulation equipment, and pollution flashover will occur. Under severe weather conditions, flashover will occur along the wet insulator surface, resulting in pollution flashover accidents in the power system. The occurrence of pollution flashover will not only affect the normal operation of the power system, but also increase the workload of power personnel. Increased maintenance costs, and even safety accidents in serious cases. However, the existing permanent form-in-place anti-fouling flashover composit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D179/08C09D5/24C09D5/08C09D7/61C09D7/63C08G73/10
CPCC08G73/1007C08G73/106C08G73/1067C08K2003/2224C09D5/08C09D5/24C09D179/08C09D7/61C09D7/63C08K13/02C08K3/34C08K3/346C08K3/22C08K3/2279C08K5/1515C08K3/04
Inventor 毛金成章慧程琰杨飞龙
Owner 成都普利美特科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com