Composition for high-strength and high-toughness rock plate blank and application of composition

A high-toughness, high-strength technology, applied in the field of rock slabs, can solve the problems of low-cost rock slab body composition, and it is not easy to increase the strength of rock slabs, so as to increase toughness, reduce the situation of cutting cracks, The effect of improving tear resistance

Active Publication Date: 2021-06-18
FOSHAN SANSHUI NEW PEARL CONSTR CERAMICS IND +1
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The application realizes the high strength of the ceramic rock slab by setting the composition of the rock slab, bottom glaze and top glaze. The above effect can be achieved only if the three are highly matched. If the blank and glaze fluctuate during production , when t...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for high-strength and high-toughness rock plate blank and application of composition
  • Composition for high-strength and high-toughness rock plate blank and application of composition
  • Composition for high-strength and high-toughness rock plate blank and application of composition

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 1

[0130] (1) Green body ingredients: Weigh each raw material of the composition for the high-strength and high-toughness rock slab green body of the present invention as shown in Table 1 below:

[0131] (2) Billet processing: Mix the raw materials weighed in step (1) to make them evenly mixed, then add water, sodium tripolyphosphate and sodium methyl cellulose in the amounts shown in Table 1 and place them in a ball mill Ball milling is carried out until the processing fineness of the slurry is 250 mesh and more than 0.8%, and the specific gravity is 1.67g / ml;

[0132] (3) Slurry screening and iron removal: Pass the slurry obtained in step (2) through a 100-mesh vibrating screen twice to remove coarse particles, and then put the slurry into a high-frequency Gauss automatic magnetic separator for iron removal. , to obtain a slurry with coarse particles and iron-containing fine impurities removed;

[0133] (4) Spray pulverization: the slurry obtained in step (3) is atomized by a ...

preparation Embodiment 2

[0137] (1) Green body ingredients: Weigh each raw material of the composition for the high-strength and high-toughness rock slab green body of the present invention as shown in Table 1 below:

[0138] (2) Billet processing: Mix the raw materials weighed in step (1) to make them evenly mixed, then add water, sodium tripolyphosphate and sodium methyl cellulose in the amounts shown in Table 1, and then place them in the Carry out ball milling in a ball mill until the processing fineness of the slurry is 250 mesh and more than 0.9%, and the specific gravity is 1.68g / ml;

[0139] (3) Slurry screening and iron removal: Pass the slurry obtained in step (2) through a 90-mesh vibrating screen twice to remove coarse particles, and then put the slurry into a high-frequency Gauss automatic magnetic separator for iron removal. , to obtain a slurry with coarse particles and iron-containing fine impurities removed;

[0140] (4) Spray pulverization: the slurry obtained in step (3) is atomize...

preparation Embodiment 3

[0144] (1) Green body ingredients: Weigh each raw material of the composition for the high-strength and high-toughness rock slab green body of the present invention as shown in Table 1 below:

[0145] (2) Billet processing: Mix the raw materials weighed in step (1) to make them evenly mixed, then add water, sodium tripolyphosphate and sodium methyl cellulose in the amounts shown in Table 1, and then place them in the Carry out ball milling in a ball mill until the processing fineness of the slurry is 1.0% of the 250-mesh sieve, and the specific gravity is 1.69 g / ml;

[0146] (3) Slurry screening and iron removal: Pass the slurry obtained in step (2) through an 80-mesh vibrating screen twice to remove coarse particles, and then put the slurry into a high-frequency Gauss automatic magnetic separator for iron removal. , to obtain a slurry with coarse particles and iron-containing fine impurities removed;

[0147] (4) Spray pulverization: the slurry obtained in step (3) is atomiz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composition for a high-strength and high-toughness rock plate blank and application of the composition. The composition comprises feldspar powder, high-alumina clay, calcined talc, pyrophyllite, potassium-sodium feldspar, high-sodium feldspar, ball clay, kaolin, diopside, high-alumina clay, ceramic waste and white carbon black. The white carbon black with the characteristics of serious surface coordination insufficiency, large specific surface area, surface oxygen deficiency and the like is used in the composition for the high-strength and high-toughness rock plate blank, so that the binding force between materials is improved, and the strength, toughness, ductility and tear resistance of the blank material are greatly improved. The rock plate blank body prepared by the method has relatively high breaking strength, relatively high toughness and relatively high stress resistance, and the situation of cutting cracks of the prepared rock plate is greatly reduced.

Description

technical field [0001] The present invention relates to the technical field of ceramic slate production, in particular to a composition for a high-strength and high-toughness slate green body, and also relates to a method for preparing a slate from the green body composition and a slate prepared therefrom. Background technique [0002] With the improvement of people's living standards and the continuous development of science and technology, building decoration and decoration materials are increasingly developing towards new decorative materials that are environmentally friendly, multi-functional, high-strength and light-weight, finished products, and intelligently controlled. The aesthetics are becoming more and more personalized, and the styles are more and more diverse. [0003] As a new type of ceramic product, slate is a new concept evolved on the basis of ceramic thin plate and ceramic large plate. The paving efficiency is high, so it has quickly become popular in the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/04C04B33/13C04B33/132C04B33/16C04B33/34
CPCC04B33/04C04B33/13C04B33/1324C04B33/16C04B33/34C04B2235/3463C04B2235/3472C04B2235/6567C04B2235/96Y02P40/60
Inventor 黄春林仝松贞徐雪英朱光耀陈育昆谢怡伟宁毓胜傅建涛韦前
Owner FOSHAN SANSHUI NEW PEARL CONSTR CERAMICS IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap