High-temperature-resistant and wear-resistant gear and preparation method thereof

A high-temperature-resistant, gear-based technology, applied in the field of high-temperature-resistant and wear-resistant gears and its preparation, can solve the problems of reduced wear resistance, low production efficiency, and short service life of gears

Inactive Publication Date: 2021-06-29
WUXI WEIFU CHINA ITAL GEAR
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the existing technology, the main problems of gears in our country are low precision and low production efficiency. Due to the heat generated by the friction of the gear material w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant and wear-resistant gear and preparation method thereof
  • High-temperature-resistant and wear-resistant gear and preparation method thereof
  • High-temperature-resistant and wear-resistant gear and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A high-temperature-resistant and wear-resistant gear provided in this embodiment, the material for preparing the high-temperature-resistant and wear-resistant gear includes the following components in parts by weight:

[0033]

[0034] This embodiment also provides a method for preparing the above-mentioned high-temperature-resistant and wear-resistant gear, including the following steps:

[0035] 1) 30 parts of 6061 aluminum alloy powder, 15 parts of NiCrBSi powder, 10 parts of ZrB 2 , 5 copies of B 4 C is placed in a planetary ball mill and ground at room temperature for 1.5h at a speed of 200rpm to form a nanometer particle size metal mixed powder with a particle size of 5nm;

[0036] 2) Dissolve 8 parts of nano-calcium carbonate with a particle size of 20nm and 4 parts of tetraethyl orthosilicate in a mixed solution of ethanol and distilled water, and stir at a temperature of 55° C. at a speed of 150 rpm for 30 minutes to obtain a modified compound with a hydrox...

Embodiment 2

[0041] A high-temperature-resistant and wear-resistant gear provided in this embodiment, the material for preparing the high-temperature-resistant and wear-resistant gear includes the following components in parts by weight:

[0042]

[0043] This embodiment also provides a method for preparing the above-mentioned high-temperature-resistant and wear-resistant gear, including the following steps:

[0044] 1) 35 parts of 6205 aluminum alloy powder, 17.5 parts of NiCrBSi powder, 12.5 parts of ZrB 2 , 3.5 parts of TiC and 4 parts of ZrC are placed in a planetary ball mill, and ground at room temperature for 1.75 hours at a speed of 250 rpm to form a nano-sized metal mixed powder with a particle size of 10 nm;

[0045] 2) 9 parts of nano-calcium carbonate with a particle size of 35nm and 6.5 parts of tetraethyl orthosilicate were dissolved in a mixed solution of ethanol and distilled water, and stirred at 170 rpm for 40 min at a temperature of 58 ° C to obtain a compound with a ...

Embodiment 3

[0050] A high-temperature-resistant and wear-resistant gear provided in this embodiment, the material for preparing the high-temperature-resistant and wear-resistant gear includes the following components in parts by weight:

[0051]

[0052]

[0053] This embodiment also provides a method for preparing the above-mentioned high-temperature-resistant and wear-resistant gear, including the following steps:

[0054] 1) 40 parts of 6463 aluminum alloy powder, 20 parts of NiCrBSi powder, 15 parts of ZrB 2 10 parts of SiC are placed in a planetary ball mill and ground at room temperature for 2 hours at a speed of 300rpm to form a nano-sized metal mixed powder with a particle size of 15nm;

[0055] 2) Dissolve 10 parts of nano-calcium carbonate with a particle size of 50 nm and 9 parts of tetraethyl orthosilicate in a mixed solution of ethanol and distilled water, and stir at 190 rpm for 45 minutes at a temperature of 60° C. to obtain a modified compound with hydroxyl functiona...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-temperature-resistant and wear-resistant gear and a preparation method thereof. The high-temperature-resistant and wear-resistant gear is prepared from the following materials in parts by mass: 30-40 parts of aluminum alloy powder, 15-20 parts of NiCrBSi powder, 20-30 parts of polybutylene terephthalate, 10-15 parts of ZrB, 5-10 parts of a carbonized cubic crystal material, 3-5 parts of glass fibers, 8-10 parts of nano calcium carbonate, 5 -15 parts of bis (hydrogenated tallow alkyl) dimethyl quaternary ammonium bentonite salt, 10-18 parts of zinc stearate and 4-9 parts of tetraethoxysilane. Nano calcium carbonate with hydroxyl functional groups is obtained after nano calcium carbonate is modified through tetraethoxysilane, then the nano calcium carbonate is combined with polybutylene terephthalate to form a core-shell structure, and then the core-shell structure is doped with glass fibers in the presence of a bis (hydrogenated tallow alkyl) dimethyl quaternary ammonium bentonite salt solution, so that the high temperature resistance and wear resistance of the finally formed gear material are improved.

Description

technical field [0001] The invention belongs to the technical field of gear preparation, and in particular relates to a high-temperature-resistant and wear-resistant gear and a preparation method thereof. Background technique [0002] Humans have a long history of inventing and applying gears. Dating back to the distant times before BC, the important role and significance of gears as important mechanical transmission components is self-evident. According to historical records, 2200 years ago, in ancient China, gears were widely used. The bronze gear unearthed in Shanxi, my country is the oldest gear discovered so far. As a guide car reflecting the achievements of ancient science and technology, it is a mechanical device with a gear mechanism as its core. In addition, Archimedes, the ancient Greek philosopher, also explained the problem of using bronze gears to transmit rotary motion in "Mechanical Problems". Various gear machines have also appeared successively afterwards...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08K13/06C08K9/06C08K9/04C08K3/26C08K7/14C08K3/34C08K3/38C08K3/08
CPCC08K13/06C08K9/06C08K9/04C08K3/26C08K7/14C08K3/346C08K3/38C08K3/08C08L2201/08C08K2201/011C08K2003/265C08K2201/005C08K2201/014C08L67/02
Inventor 林天琪贡庆许智慧魏莹莹
Owner WUXI WEIFU CHINA ITAL GEAR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap